Abstract: A toner formulation is disclosed comprising a binder and an IR absorbing black pigment at a concentration of 0.25-2.0% by weight, including one or more infrared transmissive pigments, wherein the infrared transmissive pigments are configured to provide a black color. Such toner formulation may provide a response to a toner patch sensor to indicate a mass per unit area of 0.1-1.5 mg/cm2 or a reflectance relative to a substrate to define a reflectance ratio that varies relative to L* values for the toner over the range L*=0-50 or a bulk reflectivity of greater than 6.0% for a portion of the wavelength range of 850-2000 nanometers.

Abstract: A toner formulation is disclosed comprising a binder and an IR absorbing black pigment at a concentration of 0.25-2.0% by weight, including one or more infrared transmissive pigments, wherein the infrared transmissive pigments are configured to provide a black color. Such toner formulation may provide a response to a toner patch sensor to indicate a mass per unit area of 0.1-1.5 mg/cm2 or a reflectance relative to a substrate to define a reflectance ratio that varies relative to L* values for the toner over the range L*=0-50 or a bulk reflectivity of greater than 6.0% for a portion of the wavelength range of 850-2000 nanometers.

Abstract: The present invention relates to a method for combining extra particulate additive with toner. The method includes mixing toner and extra particulate additive in a conical mixer having temperature control. The toner may contain polymeric material having a glass transition temperature (Tg) and the mixing may be carried out wherein the temperature of the mixture is maintained at a temperature less than Tg. The above method may also be applied to a toner formulation that has first undergone a rounding operation.

Abstract: Toner is rounded by vigorously mixing less than about 5 percent by weight of particulate silica to the total weight of a starting toner in a closed, recirculating air system. The starting toner contains at least about 4.5 percent by weight of the starting toner of a wax and additionally contains at least 5 percent by weight of the starting toner of a softening agent. The temperature during the mixing is no more than 13 degrees C. above the onset of the glass transition temperature of the starting toner. The final toner comprises rounded starting toner having particulate silica embedded during the mixing process.