Abstract: A lightweight ready-mix concrete composition that contains 8-20 volume percent cement, 11-50 volume percent sand, 10-31 volume percent prepuff particles, 9-40 volume percent coarse aggregate, and 10-22 volume percent water, where the sum of components used does not exceed 100 volume percent;. The prepuff particles have an average particle diameter of from 0.2 mm to 8 mm, a bulk density of from 0.02 g/cc to 0.64 g/cc, an aspect ratio of from 1 to 3. The slump value of the composition measured according to ASTM C 143 is from 2 to 8 inches. After the lightweight ready-mix concrete composition is set for 28 days, it has a compressive strength of at least 1400 psi as tested according to ASTM C39.

Abstract: A lightweight ready-mix concrete composition that contains 8-20 volume percent cement, 11-50 volume percent sand, 10-31 volume percent prepuff particles, 9-40 volume percent coarse aggregate, and 10-22 volume percent water, where the sum of components used does not exceed 100 volume percent;. The prepuff particles have an average particle diameter of from 0.2 mm to 8 mm, a bulk density of from 0.02 g/cc to 0.64 g/cc, an aspect ratio of from 1 to 3. The slump value of the composition measured according to ASTM C 143 is from 2 to 8 inches. After the lightweight ready-mix concrete composition is set for 28 days, it has a compressive strength of at least 1400 psi as tested according to ASTM C39.

Abstract: A lightweight cementitious composition containing from 22 to 90 volume percent of a cement composition and from 10 to 78 volume percent of particles having an average particle diameter of from 0.2 mm to 8 mm, a bulk density of from 0.03 g/cc to 0.64 g/cc, an aspect ratio of from 1 to 3, where after the lightweight cementitious composition is set it has a compressive strength of at least 1700 psi as tested according to ASTM C39. The cementitious composition can be used to make concrete masonry units, construction panels, road beds and other articles and can be included as a layer on wall panels and floor panels and can be used in insulated concrete forms. Aspects of the lightweight cementitious composition can be used to make lightweight structural units.

Abstract: A device and method for producing labeled expanded resin containers; the method including applying a label sheet, formed from a label material capable of maintaining an electrostatic charge, to an inner wall of female portions of two-part molds, positioning one or more male portions of the two-part molds in contact with the corresponding female portions to form one or more mold cavities; adding expandable resin beads or pre-expanded resin beads to the mold cavities; applying a sufficient amount of heat for a sufficient length of time to the mold cavities to effect expansion of the expandable resin beads or pre-expanded resin beads to form labeled containers; cooling the labeled containers; and removing the labeled containers from the mold cavities. The labels on the external wall of the labeled containers present a smooth circumferential surface.