Abstract: For integrally bonding a first member and a second member made of copper or a copper alloy by brazing, a paste brazing material composed essentially of copper (Cu), tin (Sn), nickel (Ni) and phosphorus (P) is beforehand applied to at least one of the first and second members. A base material is exposed at the whole or a part of a contact portion between the first and second members. Thereafter, the first and second members are assembled at a predetermined position, and heated at a temperature in a range of 600° C.-800° C. within a reducing atmosphere furnace. By the brazing method, an oxide film on the surface of the base material can be sufficiently removed, so that the paste brazing material can smoothly flow on the surface at the contact portion.

Abstract: For integrally bonding a first member and a second member made of copper or a copper alloy by brazing, a paste brazing material composed essentially of copper (Cu), tin (Sn), nickel (Ni) and phosphorus (P) is beforehand applied to at least one of the first and second members. A base material is exposed at the whole or a part of a contact portion between the first and second members. Thereafter, the first and second members are assembled at a predetermined position, and heated at a temperature in a range of 600° C.-800° C. within a reducing atmosphere furnace. By the brazing method, an oxide film on the surface of the base material can be sufficiently removed, so that the paste brazing material can smoothly flow on the surface at the contact portion.

Abstract: There is disclosed an Al alloy composite tube for refrigerant passages, made by extruding, or extruding and drawing a two-layer composite pipe obtained by shrink-fit of a tubular Al alloy inner material to the inside of a tubular Al alloy core, or a three-layer composite pipe obtained by shrink-fit of the two-layer composite pipe to the inside of a tubular Al alloy outer material; and a method for producing the same. This Al alloy composite tube for refrigerant passages causes less blisters at the interface between an inner pipe and an outer pipe, and can prevent debonding of the inner pipe.