Abstract: A basal portion for locking and fixing of hanging yarn (7) to bag main body (3) is determined in accordance with the amount of extraction subject mass (T) placed in the bag main body so that within the plane of top face triangle (12) as a constituent of the bag main body (3) of inverted triangular pyramid form with its vertex downward, the vertex comes on a line connecting the basal portion and gravity center (d) or in the vicinity thereof when the bag main body (3) is hung. When the bag main body (3) is pulled up by pinching tag (5), the hot water as extractant within the bag main body (3) rapidly falls by virtue of the weights of the extraction subject mass (T) and hot water therearound to thereby attain complete pouring within a relatively short period of time.

Abstract: A method of producing permalloy cores comprising the steps of coating at least one surface of permalloy strip with a slurry consisting of water containing 1 to 5 percent by weight of magnesium hydroxide (Mg(OH).sub.2) powder and the addition of one or more selected from a binder, a thickening agent and a defoaming agent and drying said coating, slitting the permalloy strip thus covered with a coating that when dry is 0.1 to 50 .mu.m thick, more preferably 0.5 to 10 .mu.m thick, and contains not less than 50 percent by weight Mg(OH).sub.2, and more preferably not less than 80 percent by weight Mg(OH).sub.2, as the main constituent, to a final width, or first to an intermediate width if necessary, winding or punching the final width strip to obtain wound or laminated punched cores, and subjecting the core materials to magnetization annealing.

Abstract: The present invention is characterized by a superconducting magnetic shield comprising a seamless, bottomless hollow body or a seamless hollow body having a bottom, the hollow body having a wall comprised of, in the thickness direction thereof, at least one laminate structure comprising a unit of two layers of an Nb--Ti-base alloy layer and a metal layer having a high conductivity or three layers of the above two layers and a barrier layer sandwiched therebetween; a process for preparing a magnetic shield which comprises subjecting the magnetic shielding material to a heat treatment after deep drawing; and a process for preparing the magnetic shielding material.

Abstract: A method of producing Fe-Ni system high permeability alloy comprising the steps of obtaining cast steel sheet 0.3 to 7 mm thick by direct casting of a steel melt containing 35 to 85% by weight of nickel with the balance of iron and unavoidable impurities, forcibly cooling the sheet from solidification to 1200.degree. C. at a cooling rate of at least 75.degree. C./s, and cold-rolling the sheet at a reduction ratio of at least 20%.