Abstract: Aluminium-containing iron oxide pigments of the formula Fe2-xAlxO3 with x values from 0.01 to 0.25, characterized in that they possess an a* value of 30.5 to 32.5 CIELAB units and a b* value of 25.5 to 30.5 CIELAB units, measured in each case as full shade in the alkyd resin according to DIN EN ISO 787-25:2007.

Abstract: Aluminium-containing iron oxide pigments of the formula Fe2-xAlxO3 with x values from 0.01 to 0.25, characterized in that they possess an a* value of 30.5 to 32.5 CIELAB units and a b* value of 25.5 to 30.5 CIELAB units, measured in each case as full shade in the alkyd resin according to DIN EN ISO 787-25:2007.

Abstract: Aluminium-containing iron oxide pigments of the formula Fe2-xAlxO3 with x values from 0.01 to 0.25, characterized in that they possess an a* value of 30.5 to 32.5 CIELAB units and a b* value of 25.5 to 30.5 CIELAB units, measured in each case as full shade in the alkyd resin according to DIN EN ISO 787-25: 2007.

Abstract: Coated pigments for plastics, as well as processes for production of the pigments, the use thereof for colouring polyvinyl chloride (PVC), processes for colouring PVC, PVC coloured with such coated pigments, and also plastics products including such coated pigments, may include inorganic pigments coated with of at least one of hydroxides of magnesium, hydroxides of calcium, oxides of magnesium, and oxides of calcium.

Abstract: Coated pigments for plastics, as well as processes for production of the pigments, the use thereof for colouring polyvinyl chloride (PVC), processes for colouring PVC, PVC coloured with such coated pigments, and also plastics products including such coated pigments, may include inorganic pigments coated with of at least one of hydroxides of magnesium, hydroxides of calcium, oxides of magnesium, and oxides of calcium.

Abstract: The invention relates to iron oxide pigments comprising an average solid body diameter of 0.1 to 500 ?m, and to the production and use thereof.

Abstract: Iron Oxide pigment containing greater than 99% iron oxide, having a chloride content of less than 0.1% and a mean solid diameter of 10 to 500 ?m and methods of making the same are disclosed.

Abstract: The invention relates to iron oxide pigments comprising an average solid body diameter of 0.1 to 500 ?m, and to the production and use thereof.

Abstract: The present invention relates to a process for preparing yellow iron oxide pigments by the precipitation method from iron(II) chloride or iron(II) sulphate raw material and calcium carbonate precipitant.

Abstract: The invention relates to iron oxide pigments comprising an average solid body diameter of 10 to 500 ?m, and to the production and use thereof.

Abstract: The present invention relates to a process for preparing yellow iron oxide pigments by the precipitation method from iron(II) chloride or iron(II) sulphate raw material and calcium carbonate precipitant.

Abstract: The invention relates to a process for the preparation of magnetite particles and to their use.

Abstract: This invention relates to a process for producing magnetite particles having a coercivity of 6.366 kA/m to 10.345 kA/m (=80 to 130 Oe) and an octahedral particle shape, comprising heating an alkaline component and an iron(II) component in the form of an aqueous solution to a temperature of 50° C. to 100° C., whereby the molar ratio of iron(II) component to one equivalent of alkaline component is 0.38 to 0.45, and treating the suspension with an oxidizing agent at a rate of oxidation of 20 to 50 mol. % Fe(II)/h until the iron compound has an Fe(III) content of more than 65 mol. %, and then again adding an Fe(II) component in the form of an aqueous solution at a molar ratio of Fe(II) to one equivalent of total alkaline component used is 0.47 to 0.49, and treating the suspension with an oxidizing agent, at a rate of oxidation is 20 to 50 mol. % Fe(II)/h until the iron compound has an Fe(III) content of more than 65 mol.

Abstract: The invention relates to a toner containing low-silicon magnetite particles.

Abstract: This invention relates to a process for producing magnetite particles having a coercivity of 6.366 kA/m to 10.345 kA/m (=80 to 130 Oe) and an octahedral particle shape, comprising heating an alkaline component and an iron(II) component in the form of an aqueous solution to a temperature of 50° C. to 100° C., whereby the molar ratio of iron(II) component to one equivalent of alkaline component is 0.38 to 0.45, and treating the suspension with an oxidizing agent at a rate of oxidation of 20 to 50 mol. % Fe(II)/h until the iron compound has an Fe(III) content of more than 65 mol. %, and then again adding an Fe(II) component in the form of an aqueous solution at a molar ratio of Fe(II) to one equivalent of total alkaline component used is 0.47 to 0.49, and treating the suspension with an oxidizing agent, at a rate of oxidation is 20 to 50 mol. % Fe(II)/h until the iron compound has an Fe(III) content of more than 65 mol.

Abstract: The present invention relates to a process for producing a yellow iron oxide pigments comprising the steps of I) mixing preprecipitated FeCl2 and an &agr;-FeOOH nucleus produced by the “alkali” process, II) oxidizing the suspension in a first oxidation step at 20 to 45° C. III) oxidizing the suspension in a first oxidation step at 55 to 85° C.

Abstract: The invention relates to a process for the preparation of magnetite particles and to their use.

Abstract: This invention relates to magnetite particles with a mean particle size of 0.1 to 0.3 &mgr;m, a specific surface area of 6 to 9 m2/g, a coercive force of 80 to 110 Oe, a residual magnetization of 13 to 20 nTm3/g, a pH of 7 to 10 and a bulk density of 0.6 to 0.9 g/cm3, by heating an aqueous solution of an alkaline component under inert gas, to a precipitation temperature of 65-85° C., adding iron (II) and iron (III) components and oxidizing the suspension with an oxidizing agent at a speed of 7-25 mol % Fe (II)/h.

Abstract: The present invention relates to a process for the production of an iron oxide yellow by a) adding FeSO4 or FeCl2 with an Fe(III) content of 0.0 to 4.0 mol % Fe(III) and a Mn content of up to 0.7 wt. %, based on the Fe content, to a solution or suspension of an alkaline component that has been heated to a temperature of between 42 and 75° C., and b) oxidizing the suspension formed with an oxidizing agent until all iron(II) has been converted into iron(III) as &agr;-FeOOH, whereby the oxidizing agent is added at a rate such that the oxidation time is between 120 and 600 minutes and the reaction temperature during the entire oxidation time is at least at the temperature at which precipitation occurred.

Abstract: Process for the preparation of iron oxide pigments from the waste acid resulting from the preparation of titanium dioxide by the sulfate process, characterized in that in a first stage a partial neutralization of the sulfuric acid contained in the waste acid is performed with compounds from the group comprising metallic iron and/or iron compounds, the sulfuric acid is optionally further neutralized with a further alkaline compound, the precipitate containing Ti, Al, Cr and V compounds is separated from the resultant reaction product and an iron oxide yellow pigment or iron oxide black pigment is precipitated from the resultant iron sulfate-containing solution by addition of alkaline compounds as well as an oxidizing agent, each pigment being able to be baked to form an iron oxide red pigment.