Abstract: A method for welding iron-based or nickel-based superalloy assemblies into a unitary article. First, the assemblies are heated in an air atmosphere, at a rate suitable to minimize geometric distortion, to a temperature in the range of about 1400F (760C) to about 2000° F. (1090° C.) to form an oxide layer on the surface of the assemblies and optionally as a pre-weld solution heat treat. The temperature of the assemblies are then held in a range of about 1400F (760C) to about 2000° F. (1090° C.) for a time sufficient to form an oxide layer of sufficient thickness on the surface of the assemblies and optionally to solution the assemblies. The assemblies are then cooled to ambient temperature at a rate sufficient to avoid precipitation of unwanted metal phases at a rate sufficient to maintain dimensional stability. The oxide layer is then removed from at least the faying surfaces of the assemblies, but not from the face side of the assemblies. The faying surfaces of the assemblies are then cleaned.