Abstract: A method for consolidating a fibrous material of plant-based fibers, such as cellulose fibers and/or poly-lactic acid fibers, the method including: applying to the fibrous material an aqueous solution including a cellulose derivative, and/or a salt thereof, and an acid, the aqueous solution having a pH within the range of from 3 to 7, optionally within the range of from 3 to 6, optionally within the range of from 3 to 4.5; and drying the bonded fibrous material, optionally at 100° C. or higher. Also, a fibrous material formed by the method, an aqueous binder solution including a cellulose derivative, and/or a salt thereof, and an acid, and a nonwoven material including airlaid plant-based fibers being consolidated by a bio-based binder in the presence of a carboxylic acid, the bio-based binder being a cellulose derivative, and/or a salt thereof.

Abstract: A fibrous sheet having a basis weight of between 20 and 1000 g/m2 that disintegrates in water, has 10% to 70% starch on the basis of the total weight of the dry fibrous sheet. The disintegration time in water, measured in accordance with standard NF Q34-020 applied to a specimen of the sheet of 9×8 cm2, is less than 50 seconds. A loss of strength of the sheet measured in accordance with a defined table test corresponds to a loss of strength of a specimen of said sheet forming an angle of at least 85° after having being wetted with water for a duration of 6 seconds, and/or a residual wet strength of the sheet relative to its dry strength, as measured according to a defined ring crush test, is less than 1%. The fibrous sheet may be used for the manufacture of a water disintegrable core in a roll of tissue paper.

Abstract: A fibrous sheet having a basis weight of between 20 and 1000 g/m2 that disintegrates in water, has 10% to 70% starch on the basis of the total weight of the dry fibrous sheet. The disintegration time in water, measured in accordance with standard NF Q34-020 applied to a specimen of the sheet of 9×8 cm2, is less than 50 seconds. A loss of strength of the sheet measured in accordance with a defined table test corresponds to a loss of strength of a specimen of said sheet forming an angle of at least 85° after having being wetted with water for a duration of 6 seconds, and/or a residual wet strength of the sheet relative to its dry strength, as measured according to a defined ring crush test, is less than 1%. The fibrous sheet may be used for the manufacture of a water disintegrable core in a roll of tissue paper.

Abstract: A fibrous sheet having a basis weight of between 20 and 1000 g/m2 being manufactured according to a wet papermaking process, and disintegrating in water in less than 120 seconds, has 10 to 70% starch and at least 30% of papermaking fibers on the basis of the total weight of the dry fibrous sheet. The sheet may be used for the manufacture of a water disintegrable core in a roll of tissue paper.

Abstract: A water degradable paper sheet has a basis weight of 80 to 400 g/m2 and is dry-formed from paper fibers bound together by a water-soluble binder including starch, the amount of binder in the sheet being 30 to 70%. Additionally, a tube is formed by a cylinder having a wall that includes at least one dry-formed paper sheet including paper fibers bound together by a water-soluble binder.

Abstract: A fibrous sheet having a basis weight of between 20 and 1000 g/m2 being manufactured according to a wet papermaking process, and disintegrating in water in less than 120 seconds, has 10 to 70% starch and at least 30% of papermaking fibres on the basis of the total weight of the dry fibrous sheet. The sheet may be used for the manufacture of a water disintegrable core in a roll of tissue paper.

Abstract: A fibrous sheet having a basis weight of between 20 and 1000 g/m2 being manufactured according to a wet papermaking process, and disintegrating in water in less than 120 seconds, has 10 to 70% starch and at least 30% of papermaking fibres on the basis of the total weight of the dry fibrous sheet. The sheet may be used for the manufacture of a water disintegrable core in a roll of tissue paper.

Abstract: A fibrous sheet having a basis weight of between 20 and 1000 g/m2 that disintegrates in water, has 10% to 70% starch on the basis of the total weight of the dry fibrous sheet. The disintegration time in water, measured in accordance with standard NF Q34-020 applied to a specimen of the sheet of 9×8 cm2, is less than 50 seconds. A loss of strength of the sheet measured in accordance with a defined table test corresponds to a loss of strength of a specimen of said sheet forming an angle of at least 85° after having being wetted with water for a duration of 6 seconds, and/or a residual wet strength of the sheet relative to its dry strength, as measured according to a defined ring crush test, is less than 1%. The fibrous sheet may be used for the manufacture of a water disintegrable core in a roll of tissue paper.

Abstract: A fibrous sheet having a basis weight of between 20 and 1000 g/m2 that disintegrates in water, has 10% to 70% starch on the basis of the total weight of the dry fibrous sheet. The disintegration time in water, measured in accordance with standard NF Q34-020 applied to a specimen of the sheet of 9×8 cm2, is less than 50 seconds. A loss of strength of the sheet measured in accordance with a defined table test corresponds to a loss of strength of a specimen of said sheet forming an angle of at least 85° after having being wetted with water for a duration of 6 seconds, and/or a residual wet strength of the sheet relative to its dry strength, as measured according to a defined ring crush test, is less than 1%. The fibrous sheet may be used for the manufacture of a water disintegrable core in a roll of tissue paper.

Abstract: A fibrous sheet having a basis weight of between 20 and 1000 g/m2 that disintegrates in water, has 10% to 70% starch on the basis of the total weight of the dry fibrous sheet. The disintegration time in water, measured in accordance with standard NF Q34-020 applied to a specimen of the sheet of 9×8 cm2, is less than 50 seconds. A loss of strength of the sheet measured in accordance with a defined table test corresponds to a loss of strength of a specimen of said sheet forming an angle of at least 85° after having being wetted with water for a duration of 6 seconds, and/or a residual wet strength of the sheet relative to its dry strength, as measured according to a defined ring crush test, is less than 1%. The fibrous sheet may be used for the manufacture of a water disintegrable core in a roll of tissue paper.

Abstract: A water degradable paper sheet has a basis weight of 80 to 400 g/m2 and is dry-formed from paper fibres bound together by a water-soluble binder including starch, the amount of binder in the sheet being 30 to 70%. Additionally, a tube is formed by a cylinder having a wall that includes at least one dry-formed paper sheet including paper fibres bound together by a water-soluble binder.

Abstract: A water-degradable paper sheet has a basis weight of 80 to 400 g/m2 and is dry-formed from paper fibers bound together by a water-soluble binder including starch, the amount of binder in the sheet being 30 to 70%. Additionally, a tube is formed by a cylinder having a wall that includes at least one dry-formed paper sheet including paper fibers bound together by a water-soluble binder.

Abstract: A fibrous sheet having a basis weight of between 20 and 1000 g/m2 that disintegrates in water, has 10% to 70% starch on the basis of the total weight of the dry fibrous sheet. The disintegration time in water, measured in accordance with standard NF Q34-020 applied to a specimen of the sheet of 9×8 cm2, is less than 50 seconds. A loss of strength of the sheet measured in accordance with a defined table test corresponds to a loss of strength of a specimen of said sheet forming an angle of at least 85°, after having being wetted with water for a duration of 6 seconds, and/or a residual wet strength of the sheet relative to its dry strength, as measured according to a defined ring crush test, is less than 1%. The fibrous sheet may be used for the manufacture of a water disintegrable core in a roll of tissue paper.

Abstract: A fibrous sheet having a basis weight of between 20 and 1000 g/m2 being manufactured according to a wet papermaking process, and disintegrating in water in less than 120 seconds, has 10 to 70% starch and at least 30% of papermaking fibres on the basis of the total weight of the dry fibrous sheet. The sheet may be used for the manufacture of a water disintegrable core in a roll of tissue paper.

Abstract: A water-degradable paper sheet has a basis weight of 80 to 400 g/m2 and is dry-formed from paper fibres bound together by a water-soluble binder including starch, the amount of binder in the sheet being 30 to 70%. Additionally, a tube is formed by a cylinder having a wall that includes at least one dry-formed paper sheet including paper fibres bound together by a water-soluble binder.