Abstract: Methods are provided for selectively depositing a material on a first surface of a substrate relative to a second, different surface of the substrate. The selectively deposited material can be, for example, a metal, metal oxide, or dielectric material.

Abstract: Compositions, related methods, and related systems are disclosed. The compositions can comprise a precursor and a liquid solvent. The precursor can be unstable in substantially pure form in an inert atmosphere at a temperature of at least 10° C. to at most 100° C. The solvent can have a vapor pressure of at most 1.0 mPa at a temperature of 20° C.

Abstract: Methods for selective deposition are provided. Material is selectively deposited on a first surface of a substrate relative to a second surface of a different material composition. An inhibitor, such as a polyimide layer, is selectively formed from vapor phase reactants on the first surface relative to the second surface. A layer of interest is selectively deposited from vapor phase reactants on the second surface relative to the first surface. The first surface can be metallic while the second surface is dielectric. Accordingly, material, such as a dielectric transition metal oxides and nitrides, can be selectively deposited on metallic surfaces relative dielectric surfaces using techniques described herein.

Abstract: Methods and systems for selectively depositing dielectric films on a first surface of a substrate relative to a passivation layer previously deposited on a second surface are provided. The methods can include at least one cyclical deposition process used to deposit material on the first surface while the passivation layer is removed, thereby preventing deposition over the passivation layer.

Abstract: Processes are provided herein for deposition of organic films. Organic films can be deposited, including selective deposition on one surface of a substrate relative to a second surface of the substrate. For example, polymer films may be selectively deposited on a first metallic surface relative to a second dielectric surface. Selectivity, as measured by relative thicknesses on the different layers, of above about 50% or even about 90% is achieved. The selectively deposited organic film may be subjected to an etch process to render the process completely selective. Processes are also provided for particular organic film materials, independent of selectivity. Masking applications employing selective organic films are provided. Post-deposition modification of the organic films, such as metallic infiltration and/or carbon removal, is also disclosed.

Abstract: Methods of forming silicon nitride thin films on a substrate in a reaction space under high pressure are provided. The methods can include a plurality of plasma enhanced atomic layer deposition (PEALD) cycles, where at least one PEALD deposition cycle comprises contacting the substrate with a nitrogen plasma at a process pressure of 20 Torr to 500 Torr within the reaction space. In some embodiments the silicon precursor is a silyl halide, such as H2SiI2. In some embodiments the processes allow for the deposition of silicon nitride films having improved properties on three dimensional structures. For example, such silicon nitride films can have a ratio of wet etch rates on the top surfaces to the sidewall of about 1:1 in dilute HF.

Abstract: Methods for controlling the formation of oxygen containing thin films, such as silicon oxycarbide (SiOC) and silicon oxycarbonitride (SiOCN) thin films, on a substrate in a reaction space are provided. The methods can include at least one plasma enhanced atomic layer deposition (PEALD) cycle including alternately and sequentially contacting the substrate with a silicon precursor that comprises oxygen and a second reactant that does not include oxygen. In some embodiments the plasma power can be selected from a range to achieve a desired step coverage or wet etch rate ratio (WERR) for films deposited on three dimensional features.

Abstract: Processes are provided herein for deposition of organic films. Organic films can be deposited, including selective deposition on one surface of a substrate relative to a second surface of the substrate. For example, polymer films may be selectively deposited on a first metallic surface relative to a second dielectric surface. Selectivity, as measured by relative thicknesses on the different layers, of above about 50% or even about 90% is achieved. The selectively deposited organic film may be subjected to an etch process to render the process completely selective. Processes are also provided for particular organic film materials, independent of selectivity. Masking applications employing selective organic films are provided. Post-deposition modification of the organic films, such as metallic infiltration and/or carbon removal, is also disclosed.

Abstract: Methods and apparatus for vapor deposition of an organic film are configured to vaporize an organic reactant at a first temperature, transport the vapor to a reaction chamber housing a substrate, and maintain the substrate at a lower temperature than the vaporization temperature. Alternating contact of the substrate with the organic reactant and a second reactant in a sequential deposition sequence can result in bottom-up filling of voids and trenches with organic film in a manner otherwise difficult to achieve.

Abstract: Methods and apparatus for vapor deposition of an organic film are configured to vaporize an organic reactant at a first temperature, transport the vapor to a reaction chamber housing a substrate, and maintain the substrate at a lower temperature than the vaporization temperature. Alternating contact of the substrate with the organic reactant and a second reactant in a sequential deposition sequence can result in bottom-up filling of voids and trenches with organic film in a manner otherwise difficult to achieve.

Abstract: Disclosed is a process for forming a silicon oxycarbide (SiOC) thin film on a substrate in a reaction space by a plurality of deposition cycles. At least one deposition cycle includes contacting a surface of the substrate with a silicon precursor that does not comprise nitrogen and a second reactant that includes reactive species. The reactive species are generated from a gas that flows continuously to the reaction space throughout the at least one deposition cycle. A ratio of a wet etch rate of the SiOC thin film to a wet etch rate of thermal silicon oxide is less than 5.

Abstract: Methods for depositing silicon oxycarbide (SiOC) thin films on a substrate in a reaction space are provided. The methods can include at least one plasma enhanced atomic layer deposition (PEALD) cycle including alternately and sequentially contacting the substrate with a silicon precursor that does not comprise nitrogen and a second reactant that does not include oxygen. In some embodiments the methods allow for the deposition of SiOC films having improved acid-based wet etch resistance.

Abstract: Methods and systems for selectively depositing dielectric films on a first surface of a substrate relative to a passivation layer previously deposited on a second surface are provided. The methods can include at least one cyclical deposition process used to deposit material on the first surface while the passivation layer is removed, thereby preventing deposition over the passivation layer.

Abstract: Processes are provided herein for deposition of organic films. Organic films can be deposited, including selective deposition on one surface of a substrate relative to a second surface of the substrate. For example, polymer films may be selectively deposited on a first metallic surface relative to a second dielectric surface. Selectivity, as measured by relative thicknesses on the different layers, of above about 50% or even about 90% is achieved. The selectively deposited organic film may be subjected to an etch process to render the process completely selective. Processes are also provided for particular organic film materials, independent of selectivity.

Abstract: Methods are provided for dual selective deposition of a first material on a first surface of a substrate and a second material on a second, different surface of the same substrate. The selectively deposited materials may be, for example, metal, metal oxide, or dielectric materials.

Abstract: Methods and apparatus for vapor deposition of an organic film are configured to vaporize an organic reactant at a first temperature, transport the vapor to a reaction chamber housing a substrate, and maintain the substrate at a lower temperature than the vaporization temperature. Alternating contact of the substrate with the organic reactant and a second reactant in a sequential deposition sequence can result in bottom-up filling of voids and trenches with organic film in a manner otherwise difficult to achieve.

Abstract: Methods and systems for selectively depositing dielectric films on a first surface of a substrate relative to a passivation layer previously deposited on a second surface are provided. The methods can include at least one cyclical deposition process used to deposit material on the first surface while the passivation layer is removed, thereby preventing deposition over the passivation layer.

Abstract: Methods for depositing oxide thin films, such as metal oxide, metal silicates, silicon oxycarbide (SiOC) and silicon oxycarbonitride (SiOCN) thin films, on a substrate in a reaction space are provided. The methods can include at least one plasma enhanced atomic layer deposition (PEALD) cycle including alternately and sequentially contacting the substrate with a first reactant that comprises oxygen and a component of the oxide, and a second reactant comprising reactive species that does not include oxygen species. In some embodiments the plasma power used to generate the reactive species can be selected from a range to achieve a desired step coverage or wet etch rate ratio (WERR) for films deposited on three dimensional features. In some embodiments oxide thin films are selectively deposited on a first surface of a substrate relative to a second surface, such as on a dielectric surface relative to a metal or metallic surface.

Abstract: Methods and apparatus for vapor deposition of an organic film are configured to vaporize an organic reactant at a first temperature, transport the vapor to a reaction chamber housing a substrate, and maintain the substrate at a lower temperature than the vaporization temperature. Alternating contact of the substrate with the organic reactant and a second reactant in a sequential deposition sequence can result in bottom-up filling of voids and trenches with organic film in a manner otherwise difficult to achieve. Deposition reactors conducive to depositing organic films are provided.

Abstract: Methods and apparatus for vapor deposition of an organic film are configured to vaporize an organic reactant at a first temperature, transport the vapor to a reaction chamber housing a substrate, and maintain the substrate at a lower temperature than the vaporization temperature. Alternating contact of the substrate with the organic reactant and a second reactant in a sequential deposition sequence can result in bottom-up filling of voids and trenches with organic film in a manner otherwise difficult to achieve.