Abstract: The present invention relates to a process for manufacturing a projectile made of steel or based on iron, for a hunting or sports cartridge, for the purpose of giving it a Vickers hardness at room temperature of between 40 HV 10 and 110 HV 10, preferably between 40 HV 10 and 85 HV 10, characterized at least by the following successive steps:—liquid pig iron or steel is used, hereafter called liquid metal, the carbon content of which is between 0.8 and 4.0% C by weight, preferably between 0.8 and 2.0% C by weight;—the liquid metal is cast using a steam or water-vapor granulation process to obtain spheroidal steel particles; —said particles are subjected to a heat treatment for softening the solidified metal by graphitization, while remaining in the ferritic range; and—optionally, said particles are subjected to a surface coating treatment.

Abstract: The present invention relates to a process for manufacturing a projectile made of steel or based on iron, for a hunting or sports cartridge, for the purpose of giving it a Vickers hardness at room temperature of between 40 HV 10 and 110 HV 10, preferably between 40 HV 10 and 85 HV 10, characterized at least by the following successive steps:—liquid pig iron or steel is used, hereafter called liquid metal, the carbon content of which is between 0.8 and 4.0% C by weight, preferably between 0.8 and 2.0% C by weight;—the liquid metal is cast using a steam or water-vapour granulation process to obtain spheroidal steel particles;—said particles are subjected to a heat treatment for softening the solidified metal by graphitization, while remaining in the ferritic range; and—optionally, said particles are subjected to a surface coating treatment.

Abstract: A method and device are provided for analysis of a molten material using optical emission spectrometry. The molten material may be, for example, a molten metal, such as casting iron or steel, or slag, glass, or lava. A sensitive element is used having at least one emission spectrometer and at least one excitation device to effect the excitation of the molten material and to enable the partial or complete generation of a radiation to be analyzed by a spectrometer present in the sensitive element. The sensitive element is brought into contact with the molten material and transmits information, which contains analysis elements supplied by the spectrometer. An immersion sensor is also provided for carrying at least part of the device for performing the analysis method.

Abstract: A method and device are provided for analysis of a molten material using optical emission spectrometry. The molten material may be, for example, a molten metal, such as casting iron or steel, or slag, glass, or lava. A sensitive element is used having at least one emission spectrometer and at least one excitation device to effect the excitation of the molten material and to enable the partial or complete generation of a radiation to be analyzed by a spectrometer present in the sensitive element. The sensitive element is brought into contact with the molten material and transmits information, which contains analysis elements supplied by the spectrometer. An immersion sensor is also provided for carrying at least part of the device for performing the analysis method.

Abstract: Steel sheet is subjected to a thermal treatment as a result of which an oxide layer is formed. The sheet is pickled by contact with an organic acid solution (formic acid), containing at least 50 mg/l of iron, at a pH of 1.5 to 4 and at a temperature above a minimum value T.sub.m given by T.sub.m =20+(pH-1.5)32.