Abstract: A method for synthesizing catalyst beads of bulk transmission metal carbides, nitrides and phosphides is provided. The method includes providing an aqueous suspension of transition metal oxide particles in a gel forming base, dropping the suspension into an aqueous solution to form a gel bead matrix, heating the bead to remove the binder, and carburizing, nitriding or phosphiding the bead to form a transition metal carbide, nitride, or phosphide catalyst bead. The method can be tuned for control of porosity, mechanical strength, and dopant content of the beads. The produced catalyst beads are catalytically active, mechanically robust, and suitable for packed-bed reactor applications. The produced catalyst beads are suitable for biomass conversion, petrochemistry, petroleum refining, electrocatalysis, and other applications.

Abstract: A method for synthesizing catalyst beads of bulk transmission metal carbides, nitrides and phosphides is provided. The method includes providing an aqueous suspension of transition metal oxide particles in a gel forming base, dropping the suspension into an aqueous solution to form a gel bead matrix, heating the bead to remove the binder, and carburizing, nitriding or phosphiding the bead to form a transition metal carbide, nitride, or phosphide catalyst bead. The method can be tuned for control of porosity, mechanical strength, and dopant content of the beads. The produced catalyst beads are catalytically active, mechanically robust, and suitable for packed-bed reactor applications. The produced catalyst beads are suitable for biomass conversion, petrochemistry, petroleum refining, electrocatalysis, and other applications.

Abstract: A method for bandgap shift and phase transformation for titania structures. The method can include providing a flexible substrate, depositing a titania film onto the substrate, and exposing the titania film to one or more pulses of infrared energy of sufficient energy density and for a sufficient time to crystallize the titania film to predominantly anatase crystalline phase. The flexible substrate can be formed from a polymeric material, and the method can achieve a bandgap shift from greater than 3.0 eV to approximately 2.4 eV. The method can also include forming a crystalline titania layer over a substrate and annealing the crystalline titania layer by applying pulsed thermal energy sufficient to modify the phase constitution of the crystalline titania layer. The source of pulsed thermal energy can include an infrared flashlamp or laser, and the resulting titania structure can be used with photovoltaic and photoelectrolysis systems.