Abstract: Disclosed herein is a process that includes: (a) providing a powder blend comprising (1) one or more hydrogenated titanium powders containing around 0.2 to around 3.4 weight % of hydrogen, and (2) one or more master alloys, comprising Al, V, or a combination thereof, (b) consolidating the powder blend by compacting the powder blend to provide a green compact, (c) heating the green compact to a temperature ranging from around 400° C. to around 900° C.

Abstract: Disclosed herein is a process that includes: (a) forming a powder blend by mixing Commercially Pure (C.P.) titanium powder, one or more hydrogenated titanium powders containing around 3.4 to around 3.9 weight % of hydrogen (e.g., hydrogenated titanium powders available or referred to nominally as “titanium hydride” or TiH2), and one or more hydrogenated titanium powders containing around 0.2 to around 3.4 weight % of hydrogen, or a mixture of the hydrogenated titanium powders without the C.P. titanium powder, (b) consolidating the powder blend by either compacting the powder blend using die pressing, direct powder rolling, cold isostatic pressing, impulse pressing, metal injection molding, other room temperature consolidation method, or combination thereof, at a pressure in the range of around 400 to around 960 MPa, or loose sintering, to provide a green compact having a density lower than that of a green compact formed from only C.P.

Abstract: Disclosed herein is a process that includes: (a) providing a powder blend comprising (1) one or more hydrogenated titanium powders containing around 0.2 to around 3.4 weight % of hydrogen, and (2) one or more master alloys, comprising Al, V, or a combination thereof, (b) consolidating the powder blend by compacting the powder blend to provide a green compact, (c) heating the green compact to a temperature ranging from around 400° C. to around 900° C.

Abstract: A process including: (a) forming a powder blend by mixing titanium powders, (b) consolidating the powder blend by compacting to provide a green compact, (c) heating the green compact thereby releasing absorbed water from the titanium powder, (d) forming ?-phase titanium and releasing atomic hydrogen from the hydrogenated titanium by heating the green compact in an atmosphere of hydrogen emitted by the hydrogenated titanium, (e) reducing surface oxides on particles of the titanium powder with atomic hydrogen released by heating of the green compact, (f) diffusion-controlled chemical homogenizing of the green compact and densification of the green compact by heating followed by holding resulting in complete or partial dehydrogenation to form a cleaned and refined compact, (g) heating the cleaned and refined green compact in vacuum thereby sintering titanium to form a sintered dense compact, and (h) cooling the sintered dense compact to form a sintered near-net shaped article.

Abstract: A process including: (a) forming a powder blend by mixing titanium powders, (b) consolidating the powder blend by compacting to provide a green compact, (c) heating the green compact thereby releasing absorbed water from the titanium powder, (d) forming ?-phase titanium and releasing atomic hydrogen from the hydrogenated titanium by heating the green compact in an atmosphere of hydrogen emitted by the hydrogenated titanium, (e) reducing surface oxides on particles of the titanium powder with atomic hydrogen released by heating of the green compact, (f) diffusion-controlled chemical homogenizing of the green compact and densification of the green compact by heating followed by holding resulting in complete or partial dehydrogenation to form a cleaned and refined compact, (g) heating the cleaned and refined green compact in vacuum thereby sintering titanium to form a sintered dense compact, and (h) cooling the sintered dense compact to form a sintered near-net shaped article.