Abstract: A process for preparing an ethylene polymer in a suspension polymerization including the steps of separating the formed suspension of ethylene polymer particles in a solid-liquid separator into ethylene polymer particles and mother liquor, transferring a first part of the mother liquor into a work-up section including an evaporation unit for producing a wax-depleted portion of the mother liquor, wherein a protic agent is added to the part of the mother liquor which is transferred into the work-up section, and recycling a first part of the wax-depleted portion of the mother liquor to the polymerization reactor or the series of polymerization reactors.

Abstract: The present disclosure relates to a polyethylene composition with improved swell ratio and mechanical properties for use in preparing blow-molded articles and having the following features: 1) a density from 0.945 to less than 0.952 g/cm3; 2) an MIF/MIP ratio from 15 to 30; 3) a Shear-Induced Crystallization Index (SIC) from 2.5 to 5.5.

Abstract: The present disclosure relates to a polyethylene composition with improved swell ratio and mechanical properties for use in preparing blow-moulded articles and having the following features: 1) a density from 0.945 to less than 0.952 g/cm3; 2) an MIF/MIP ratio from 15 to 30; 3) a Shear-Induced Crystallization Index (SIC) from 2.5 to 5.5.

Abstract: The present disclosure relates to a polyethylene composition with improved swell ratio and mechanical properties for use in preparing blow-moulded articles and having the following features: 1) a density from 0.945 to less than 0.952 g/cm3; 2) an MIF/MIP ratio from 15 to 30; 3) a Shear-Induced Crystallization Index (SIC) from 2.5 to 5.5.

Abstract: The present disclosure relates to a polyethylene composition with improved swell ratio and mechanical properties, particularly suited for preparing blow-moulded articles, said composition having the following features: 1) a density from 0.952 to 0.960 g/cm3; 2) an MIF/MIP ratio from 17 to 30; and 3) a Shear-Induced Crystallization Index SIC from 2.5 to 5.0.

Abstract: The present disclosure relates to a polyethylene composition with improved swell ratio and mechanical properties for use in preparing blow-moulded articles and having the following features: 1) a density from 0.945 to less than 0.952 g/cm3; 2) an MIF/MIP ratio from 15 to 30; 3) a Shear-Induced Crystallization Index (SIC) from 2.5 to 5.5.

Abstract: Polyethylene composition with improved balance of environmental stress cracking resistance (FNCT) and impact resistance (Charpy), particularly suited for preparing pipes, said composition having the following features: 1) density from 0.945 to 0.955 g/cm3; 2) ratio MIF/MIP from more than 30 to 45; 3) Shear-Induced Crystallization Index SIC from 1.0 to 2.5; 4) Long Chain Branching index equal to or greater than 0.85.

Abstract: Polyethylene composition with improved swell ratio and mechanical properties, particularly suited for preparing blow-molded articles, said composition having the following features: 1) density from 0.945 to less than 0.952 g/cm3; 2) ratio MIF/MIP from 15 to 30; 3) Shear-Induced Crystallization Index SIC from 2.5 to 5.5.

Abstract: The present disclosure relates to a polyethylene composition with improved swell ratio and mechanical properties, particularly suited for preparing blow-moulded articles, said composition having the following features: 1) a density from 0.952 to 0.960 g/cm3; 2) an MIF/MIP ratio from 17 to 30; and 3) a Shear-Induced Crystallization Index SIC from 2.5 to 5.0.

Abstract: Polyethylene composition with improved swell ratio and mechanical properties, particularly suited for preparing blow-moulded articles, said composition having the following features: 1) density from 0.952 to 0.960 g/cm3; 2) ratio MIF/MIP from 17 to 30; 3) Shear-Induced Crystallization Index SIC from 2.5 to 5.0.

Abstract: Polyethylene composition with improved balance of environmental stress cracking resistance (FNCT) and impact resistance (Charpy), particularly suited for preparing pipes, said composition having the following features: 1) density from 0.945 to 0.955 g/cm3; 2) ratio MIF/MIP from more than 30 to 45; 3) Shear-Induced Crystallization Index SIC from 1.0 to 2.5; 4) Long Chain Branching index equal to or greater than 0.85.

Abstract: Polyethylene composition with improved swell ratio and mechanical properties, particularly suited for preparing blow-moulded articles, said composition having the following features: 1) density from 0.952 to 0.960 g/cm3; 2) ratio MIF/MIP from 17 to 30; 3) Shear-Induced Crystallization Index SIC from 2.5 to 5.0.

Abstract: Polyethylene composition with improved swell ratio and mechanical properties, particularly suited for preparing blow-moulded articles, said composition having the following features: 1) density from 0.945 to less than 0.952 g/cm3; 2) ratio MIF/MIP from 15 to 30; 3) Shear-Induced Crystallization Index SIC from 2.5 to 5.5.

Abstract: A multimodal ethylene copolymer having the following properties: i) density comprised in the range from 0.880 to 0.955 g/cm3; ii) total comonomer content ranging from 6% to 25% by weight; iii) content of 1-butene derived units ranging from 0 to 2% by weight; iv) Mw/Mn comprised from 4 to 20; v) intrinsic viscosity (decalin at 135° C. as determined according to EN ISO 1628-312003) comprised between 1.0 and 4.0 dL/g; said multimodal ethylene copolymer comprises from 10% to 80% by weight of a first polyethylene component and being detected at the Crystaf® apparatus at a temperature higher than 75° C. and from 90% to 20% by weight of a second polyethylene component being a copolymer being detected at a Crystaf® apparatus at a temperature lower than 75° C.; wherein said multimodal ethylene copolymer being fractionated into 12 fractions by means of the Holtrup analysis, the fractions containing more than 2% by weight of the total amount of material meet the following relationship: Cf/HDPE>?0.0075HDPE+0.

Abstract: An ethylene copolymer, a catalyst system suitable to prepare the ethylene copolymer, and a process to prepare such ethylene copolymer are described. The use of the ethylene copolymer as impact modifier in polyethylene and as compatibilizer in a polymer blend are also described. The ethylene copolymer has a density from 0.855 g/cm3 to 0.910 g/cm3, a polydispersity Mw/Mn lower than 3.5, comprises at least one first ethylene polymer component and at least one second ethylene polymer component having different comonomer contents so as to show at least two predetermined CRYSTAF peak temperatures.

Abstract: An ethylene copolymer, a catalyst system suitable to prepare the ethylene copolymer, and a process to prepare such ethylene copolymer are described. The use of the ethylene copolymer as impact modifier in polyethylene and as compatibilizer in a polymer blend are also described. The ethylene copolymer has a density from 0.855 g/cm3 to 0.910 g/cm3, a polydispersity Mw/Mn lower than 3.5, comprises at least one first ethylene polymer component and at least one second ethylene polymer component having different comonomer contents so as to show at least two predetermined CRYSTAF peak temperatures.

Abstract: A multimodal ethylene copolymer having the following properties: i) density comprised in the range from 0.880 to 0.955 g/cm3; ii) total comonomer content ranging from 6% to 25% by weight; iii) content of 1-butene derived units ranging from 0 to 2% by weight; iv) Mw/Mn comprised from 4 to 20; v) intrinsic viscosity (decalin at 135° C. as determined according to EN ISO 1628-312003) comprised between 1.0 and 4.0 dL/g; said multimodal ethylene copolymer comprises from 10% to 80% by weight of a first polyethylene component and being detected at the Crystaf® apparatus at a temperature higher than 75° C. and from 90% to 20% by weight of a second polyethylene component being a copolymer being detected at a Crystaf® apparatus at a temperature lower than 75° C.; wherein said multimodal ethylene copolymer being fractionated into 12 fractions by means of the Holtrup analysis, the fractions containing more than 2% by weight of the total amount of material meet the following relationship: Cf/HDPE>?0.0075HDPE+0.

Abstract: To meter catalysts into a reactor, the catalyst is firstly suspended in a hydrocarbon in a reservoir and the suspension obtained is kept in motion by stirring and then fed via a three-way metering valve and an ejector into the actual reactor, wherein the suspension containing the catalyst is firstly discharged from the reservoir by means of a pump and continuously circulated by returning the suspension via the three-way metering valve within a closed piping system to the reservoir, subsequently setting a pressure in the reservoir which is from 0.1 to 30 bar higher than the pressure in the reactor and then continuously introducing the suspension into the reactor via a flow meter which controls the three-way metering valve and via a downstream ejector by pulse operation of the now open three-way metering valve.

Abstract: Molding compositions made from a high-molecular-weight propylene polymer with a melt mass-flow rate MFR of from 0.3 to 1 g/10 min, to ISO 1133 at 230° C. and 5 kg, and with a proportion of ? modification crystallites in the range from 2 to 20% by weight. The molding compositions of the invention preferably comprise a quinarcidone pigment as nucleating agent. The high-molecular-weight propylene polymer used preferably comprises a high-molecular-weight propylene copolymer with up to 30% by weight of other copolymerized olefins having up to 10 carbon atoms. One of the uses of the molding compositions of the invention is as materials for pipes.

Abstract: The novel metallocenes of the formula I in which, preferably, M1 is Zr or Hf, R1 and R2 are alkyl or halogen, R3 and R4 are hydrogen, R5 and R6 are alkyl or haloalkyl, —(CR8R9)m—R7—(CR8R9)n— is a single- or multi-membered chain in which R7 may also be a (substituted) hetero atom, m+n is zero or 1, and R10 is hydrogen, form, together with aluminoxanes as cocatalysts, a very effective catalyst system for the preparation of polyolefins of high stereospecificity and high melting point.