Abstract: The invention relates to an ink for producing catalyst layers for electrochemical devices. The ink comprises catalyst materials, ionomer material, water and at least one organic solvent. The organic solvent belongs to the class of tertiary alcohols and/or the class of aliphatic diketones and bears functional groups which are stable to oxidative degradation in the ink. This prevents formation of decomposition products in the ink. The ink of the invention displays a high storage stability and is used for producing catalyst-coated substrates for electrochemical devices, in particular fuel cells (PEMFCs, DMFCs).

Abstract: The invention relates to an ink for producing catalyst layers for electrochemical devices. The ink comprises catalyst materials, ionomer material, water and at least one organic solvent. The organic solvent belongs to the class of tertiary alcohols and/or the class of aliphatic diketones and bears functional groups which are stable to oxidative degradation in the ink. This prevents formation of decomposition products in the ink. The ink of the invention displays a high storage stability and is used for producing catalyst-coated substrates for electrochemical devices, in particular fuel cells (PEMFCs, DMFCs).

Abstract: The invention relates to an ink for producing catalyst layers for electrochemical devices. The ink comprises catalyst material, ionomer material, water and at least one organic solvent. The organic solvent belongs to the class of tertiary alcohol's and/or the class of aliphatic diketones and bears functional groups which are stable to oxidative degradation in the ink. This prevents formation of decomposition products in the ink. The ink of the invention displays a high storage stability and is used for producing catalyst-coated substrates for electrochemical devices, in particular fuel cells (PEMFCs, DMFCs).

Abstract: The invention relates to an ink for producing catalyst layers for electrochemical devices. The ink comprises catalyst material, ionomer material, water and at least one organic solvent. The organic solvent belongs to the class of tertiary alcohol's and/or the class of aliphatic diketones and bears functional groups which are stable to oxidative degradation in the ink. This prevents formation of decomposition products in the ink. The ink of the invention displays a high storage stability and is used for producing catalyst-coated substrates for electrochemical devices, in particular fuel cells (PEMFCs, DMFCs).

Abstract: A process for preparing a shell-type catalyst which comprises applying to a substantially nonporous inorganic support material having a BET surface area of <80 m2/g, a catalytically active outer shell of a suspension containing at least one water soluble noble metal compound and a substantially water insoluble coating compound, drying the suspension onto the support material, and activating the coated support material in a reducing gas stream.

Abstract: A process for preparing a shell-type catalyst which comprises applying to a substantially nonporous inorganic support material having a BET surface area of <80 m2/g, a catalytically active outer shell of a suspension containing at least one water soluble noble metal compound and a substantially water insoluble coating compound, drying the suspension onto the support material, and activating the coated support material in a reducing gas stream.

Abstract: A process for preparing a shell-type catalyst which comprises applying to a substantially nonporous inorganic support material having a BET surface area of <80 m2/g, a catalytically active outer shell of a suspension containing at least one water soluble noble metal compound and a substantially water insoluble coating compound, drying the suspension onto the support material, and activating the coated support material in a reducing gas stream.

Abstract: A platinum/ruthenium alloy catalyst that includes finely dispersed alloy particles on a powdery, electrically conductive carrier material. The catalyst is particularly resistant to carbon monoxide poisoning when the alloy particles display mean crystallite sizes of 0.5 to less than 2 nm.