Abstract: A process produces a free flowing, silicic-acid-filled, powdered elastomer wherein the silicic acid employed has the properties set out below:(a) SiO.sub.2 content: about 82-91.5% by weight;(b) metallic oxides: about 0.5-3% by weight;(c) loss on ignition (DIN 55 921/2--measured at 100.degree. C.): about 8-15% by weight;(d) moisture (DIN 53 198--measured at 105.degree. C.): about 2-10% by weight;(e) surface area of the primary particles according to BET: about 40-250 m.sup.2 /g;(f) dibutyl phthalate absorption (ASTM D 2414-79) based on measured weight: about 170-290%.(g) linear average of numerical distribution of secondary particles: about 10-2,000 nm;(h) linear average of volume distribution of secondary particles: about 3-30 um;(i) proportion of secondary particles with a diameter of less than 1 um: about 0.01-5% by weightwherein the percentages of parameters (a) to (c), added up together, must yield 100% by weight.