Abstract: A cathode material for Li ion secondary batteries has high output and high energy density with excellent electron conductivity and Li ion conductivity. The cathode material contains an electrode active material base containing Li, which is capable of electrode oxidation/reduction accompanied by desorption and absorption of Li ions in a potential range of 4 V or more and 5 V or less based on a metal Li negative electrode and has a reversible charge/discharge capacity accompanying the electrode oxidation/reduction in the potential range described above of 30 mAh or more per 1 g. Surfaces of primary particles of an electrode active material base are coated with a layer containing a conductive polymer and a negative ion that enables the conductive polymer to produce electron conductivity equal to or higher than the electron conductivity of the electrode active material itself.

Abstract: A method is for molding a gas hydrate pellet for improving convenience of handling of a natural gas hydrate during transportation and storage, and thereby improving the practical use of the natural gas hydrate. Gas hydrate slurry is fed in a compression chamber, and pressure and compression are applied to the gas hydrate slurry by advancing a compression plunger. At that time, a stroking speed of the compression plunger is set minimum, preferably less than a value expressed by a stroke length of the compression plunger at compression×10?2 (m/min. By advancing the compression plunger at low speed, binding between particles of the gas hydrate is tightened, thereby the gas hydrate pellet with increased shearing strength can be molded.

Abstract: A method is for molding a gas hydrate pellet for improving convenience of handling of a natural gas hydrate during transportation and storage, and thereby improving the practical use of the natural gas hydrate. Gas hydrate slurry is fed in a compression chamber, and pressure and compression are applied to the gas hydrate slurry by advancing a compression plunger. At that time, a stroking speed of the compression plunger is set minimum, preferably less than a value expressed by a stroke length of the compression plunger at compression×10?2 (m/min). By advancing the compression plunger at low speed, binding between particles of the gas hydrate is tightened, thereby the gas hydrate pellet with increased shearing strength can be molded.