Abstract: The present disclosure relates to a process for the preparation of a zeolitic material having a CHA-type framework structure comprising YO2 and X2O3, wherein the process comprises: (1) providing a mixture comprising one or more sources for YO2, one or more sources for X2O3, one or more tetraalkylammonium cation R1R2R3R4N+-containing compounds, and one or more tetraalkylammonium cation R5R6R7R8N+-containing compounds as structure directing agent; (2) crystallizing the mixture to obtain a zeolitic material having a CHA-type framework structure; wherein Y is a tetravalent element and X is a trivalent element, wherein R1, R2, R3, R5, R6, and R7 independently from one another stand for alkyl, wherein R4 stands for CnH2nOH with n=1 to 6, and wherein R8 stands for cycloalkyl.

Abstract: A batch process for preparing a zeolitic material having framework type CHA and a framework structure comprising Si, Al, O, and H, comprising (i) providing a seeding material comprising a zeolitic material having framework type CHA and a framework structure comprising Si, Al, O, and H; (ii) preparing a mixture comprising a source of Si, a source of Al, a seeding material provided in (i), a CHA framework structure directing agent comprising a cycloalkylammonium compound, and water, wherein the cycloalkylammonium compound is a compound comprising a cation R1R2R3R4N+ wherein R1, R2, R3 are, independently from one another, an alkyl residue having from 1 to 6 carbon atoms, and R4 is a 5- to 8-membered cycloalkyl residue, wherein in mixture, the molar ratio of water relative to Si comprised in the source of Si and in the seeding material, calculated as SiO2, is in the range of from 5:1 to 15:1, wherein the mixture, the molar ratio of sodium, calculated as Na2O, relative to Si comprised in the source of Si and in th

Abstract: Methods of making supported polyamines, supported polyamines, and the like, are disclosed.

Abstract: Methods of making supported polyamines, supported polyamines, and the like, are disclosed.

Abstract: Methods of making supported polyamines, supported polyamines, and the like, are disclosed.

Abstract: A zeolite beta according to the present invention has a SiO2/Al2O3 ratio of 10 to 16 and is aluminum-rich. The zeolite beta has a BET specific surface area measured in the state of a sodium type of 500 to 700 m2/g, a micropore specific surface area of 350 to 500 m2/g, and a micropore volume of 0.15 to 0.25 cm3/g.

Abstract: A zeolite beta according to the present invention has a SiO2/Al2O3 ratio of 10 to 16 and is aluminum-rich. The zeolite beta has a BET specific surface area measured in the state of a sodium type of 500 to 700 m2/g, a micropore specific surface area of 350 to 500 m2/g, and a micropore volume of 0.15 to 0.25 cm3/g.