Abstract: The present disclosure provides a high-efficient rolling process for magnesium alloy sheet. Parameters of the rolling process are: the rolling speed of each rolling pass is 10-50 m/min, the rolling reduction of each rolling pass is controlled to be 40-90%, and both the preheating temperature before rolling and the rolling temperature of each rolling pass are 250-450° C. The present disclosure also provides a preparation method for magnesium alloy sheet, comprising: 1) preparing rolling billets; 2) high-efficient hot rolling; and 3) performing annealing. The rolling process can improve the mechanical performance especially, the strength and ductility of the sheet.

Abstract: A film forming treatment agent for a composite chemical conversion film for magnesium alloy, and a film forming process method, and a composite chemical conversion film are provided. Components of the film forming treatment agent for a composite chemical conversion film for magnesium alloy comprise a water solution and a suspension of reduced graphene oxide flakes to the water solution. The water solution comprises strontium ions at 0.1 mol/L to 2.5 mol/L and phosphate ions at 0.06 mol/L to 1.5 mol/L, and pH of the water solution is 1.5 to 4.5. Concentration of the reduced graphene oxide varies between 0.1 mg/L and 5 mg/L. The film forming process method for a composite chemical conversion film for magnesium alloy comprises the following steps of: 1) pretreatment on surface of magnesium alloy matrix; 2) immersion of magnesium alloy matrix in the film forming treatment agent; and 3) removal of magnesium alloy pieces for drying in air.

Abstract: A high strength and corrosion-resistant magnesium alloy material, comprising 0.01-1.2 wt % of Ge and 0.01-1.2 wt % of Zn. A high strength and corrosion-resistant magnesium alloy material, comprising the following chemical elements in percentage by weight: Ge: 0.01-1.2%; Zn: 0.01-1.2%; at least one of Mn, Ca, Zr, Sr, and Gd, with a total weight percentage of ?3%, wherein the percentage by weight of a single element is ?0.8%; and the balance of Mg and other inevitable impurities. A method for fabricating the above mentioned high strength and corrosion-resistant magnesium alloy material, comprising the steps of: smelting, solid solution heat treatment, and extrusion, wherein in the extrusion step, the extrusion temperature is 180-350° C., the extrusion rate is 0.1-10 mm/s, and the extrusion ratio is 10:1-30:1.

Abstract: A die-casting magnesium alloy. The die-casting magnesium alloy comprises, by mass percent, 1% to 5% of La, 0.5% to 3% of Zn, 0.1% to 2% of Ca, 0.1% to 1% of Mn and the balance Mg and other inevitable impurities. The die-casting magnesium alloy manufacturing method comprises smelting, refinement and die-casting. The die-casting magnesium alloy has good mechanical performance, die-casting performance and heat conduction performance.

Abstract: The present invention provides magnesium or magnesium alloys having high formability at room temperature, the magnesium or magnesium alloys having a grain size ?2 microns. The present invention also provides a method for manufacturing the magnesium or magnesium alloys having high formability at room temperature. The magnesium or magnesium alloys having high formability at room temperature are prepared by simple processing means. The present invention overcomes a problem of poor formability at room temperature.

Abstract: A high-efficient rolling process for magnesium alloy sheet. The process is a rolling process for rolling billets. Parameters of the rolling process are: the rolling speed of each rolling pass is 10˜50 m/min, the rolling reduction of each rolling pass is controlled to be 40˜90%, and both the preheating temperature before rolling and the rolling temperature of each rolling pass are 250˜450° C. A preparation method for magnesium alloy sheet. The method comprises the steps of: 1) preparing rolling billets; 2) high-efficient hot rolling: controlling the rolling speed of each rolling pass to be 10˜50 m/min, controlling the rolling reduction of each rolling pass to be 40˜90%, and controlling both the preheating temperature before rolling and the rolling temperature of the each rolling pass to be 250˜450° C.; and 3) performing annealing.

Abstract: A film forming treatment agent for a composite chemical conversion film for magnesium alloy, and a film forming process method, and a composite chemical conversion film are provided. Components of the film forming treatment agent for a composite chemical conversion film for magnesium alloy comprise a water solution and a suspension of reduced graphene oxide flakes to the water solution. The water solution comprises strontium ions at 0.1 mol/L to 2.5 mol/L and phosphate ions at 0.06 mol/L to 1.5 mol/L, and pH of the water solution is 1.5 to 4.5. Concentration of the reduced graphene oxide varies between 0.1 mg/L and 5 mg/L. The film forming process method for a composite chemical conversion film for magnesium alloy comprises the following steps of: 1) pretreatment on surface of magnesium alloy matrix; 2) immersion of magnesium alloy matrix in the film forming treatment agent; and 3) removal of magnesium alloy pieces for drying in air.

Abstract: A die-casting magnesium alloy. The die-casting magnesium alloy comprises, by mass percent, 1% to 5% of La, 0.5% to 3% of Zn, 0.1% to 2% of Ca, 0.1% to 1% of Mn and the balance Mg and other inevitable impurities. The die-casting magnesium alloy manufacturing method comprises smelting, refinement and die-casting. The die-casting magnesium alloy has good mechanical performance, die-casting performance and heat conduction performance.