Abstract: The technical field of the invention belongs to concrete and cement. The invention relates to a sialite binary wet cement and its package, transportation, storage and application. The sialite binary wet cement is composed of a “female body” as a primary component and a “male body” as a secondary component both of which are produced, stored, and transported separately, and are mixed together when they are used, wherein the “female body” and the “male body” each have a specific surface area of 2800-7500 cm2/g, the “female body” is mainly composed of inorganic cementitious materials and water, and it is in slurry, paste or wet powder form during the whole period of its production, storage, transportation and usage; the “male body” is mainly composed of inorganic cementitious materials, and it can be a wet form or a dry powder form. When they are used, the “female body” and the “male body” are mixed together with a small amount of regulating agents.

Abstract: The technical field of the invention belongs to concrete and cement. The invention relates to a sialite binary wet cement and its package, transportation, storage and application. The sialite binary wet cement is composed of a “female body” as a primary component and a “male body” as a secondary component both of which are produced, stored, and transported separately, and are mixed together when they are used, wherein the “female body” and the “male body” each have a specific surface area of 2800-7500 cm2/g, the “female body” is mainly composed of inorganic cementitious materials and water, and it is in slurry, paste or wet powder form during the whole period of its production, storage, transportation and usage; the “male body” is mainly composed of inorganic cementitious materials, and it can be a wet form or a dry powder form. When they are used, the “female body” and the “male body” are mixed together with a small amount of regulating agents.

Abstract: The invention provides cementitious mixtures, particularly for use as shotcrete binding materials. The resultant shotcrete has characteristics of rapid setting as low as 5 to 10 minutes, high early compressive strength (5 to 25 MPa in two hours curing, 20 to 60 MPa in one day curing), high permanent compressive strength and negligible shrinkage. High aluminous content roasted cement clinkers with gypsum, anhydrite, lime, limestone, bentonite and other additives are used in the mixtures. There are especially suitable for use in shotcrete engineering. The methods of using the improved shotcrete are similar to those of using Portland cement, with significantly decreased rebound at site.