Abstract: An about ? inch to ¾ inch thick low weight, low density gypsum panel with fire resistance capabilities sufficient to provide a Thermal Insulation Index of at least 17.0 minutes which when subjected to U419 test procedures will not fail for at least 30 minutes and, in selected embodiments, also has outstanding water resistance properties.

Abstract: The invention generally provides gypsum-containing slurries including stucco, naphthalenesulfonate dispersant, and pregelatinized starch. The naphthalenesulfonate dispersant is present in an amount of about 0.1%-3.0% by weight based on the weight of dry stucco. The pregelatinized starch is present in an amount of at least about 0.5% by weight up to about 10% by weight of pregelatinized starch by weight based on the weight of dry stucco in the formulation. Other slurry additives can include trimetaphosphate salts, accelerators, binders, paper fiber, glass fiber, and other known ingredients. The invention also comprises the gypsum-containing products made with such slurries, for example, gypsum wallboard, and a method of making gypsum wallboard.

Abstract: The invention provides gypsum wallboard, made from gypsum-containing slurries having outstanding hydration rate characteristics comprising alpha-hemihydrate ground to a particular particle size distribution range and having a Blaine surface area in the range from about 3100 cm2/g to about 9000 cm2/g, alone or in combination with beta-hemihydrate.

Abstract: The invention provides a light weight composite gypsum board including a foamed low density set gypsum core, a top non-foamed (or reduced-foamed) bonding high density layer and a bottom non-foamed (or reduced-foamed) bonding high density layer, a top cover sheet bonded to the foamed low density set gypsum core by the top non-foamed (or reduced-foamed) bonding high density layer, and a bottom cover sheet bonded to the foamed low density set gypsum core by the bottom non-foamed (or reduced-foamed) bonding high density layer. The foamed low density set gypsum core is prepared having a density of less than about 30 pcf using soap foam in the gypsum-containing slurry. The combination of components provide a composite gypsum board having light weight and high strength.

Abstract: The invention generally provides gypsum-containing slurries including stucco, naphthalenesulfonate dispersant, and pregelatinized starch. The naphthalenesulfonate dispersant is present in an amount of about 0.1%-3.0% by weight based on the weight of dry stucco. The pregelatinized starch is present in an amount of at least about 0.5% by weight up to about 10% by weight of pregelatinized starch by weight based on the weight of dry stucco in the formulation. Other slurry additives can include trimetaphosphate salts, accelerators, binders, paper fiber, glass fiber, and other known ingredients.

Abstract: A process is disclosed for making a blend of alpha- and beta-stucco including a slurry calcination step to produce alpha calcium sulfate hemihydrate followed by a fluidized bed calcination step to produce beta calcium sulfate hemihydrate. The process starts with 50-75% gypsum-containing solids slurry, and then steam calcines the slurry in a first reactor to form partially calcined gypsum slurry which contains calcium sulfate dihydrate and alpha calcium sulfate hemihydrate. The partially calcined slurry is then dewatered. Then the filter cake is fed into a kettle to complete the calcination process by converting the calcium sulfate dihydrate of the filter cake material into beta calcium sulfate hemihydrate.