Abstract: The invention discloses high-strength glass-ceramic-based lightweight aggregates and the preparation method thereof. The mass ratio of raw material components is 50-70 parts of engineering muck, 20-40 parts of glass, 3-7 parts of calcium carbonate, 3-7 parts of magnesium oxide, and 2-10 parts of a nucleating agent; the nucleating agent is at least one of calcium fluoride, titanium dioxide, and chromium oxide. After crushing, mixing, and granulating, spherical particles with a particle size of 10-12 mm are formed; and then the product can be obtained after drying, sintering, and cooling. The obtained lightweight aggregate from the invention has a diopside matrix which provides high strength and a low water absorption rate at low densities. Moreover, waste glass and engineering muck could be utilized with high value.

Abstract: The invention discloses high-strength glass-ceramic-based lightweight aggregates and the preparation method thereof. The mass ratio of raw material components is 50-70 parts of engineering muck, 20-40 parts of glass, 3-7 parts of calcium carbonate, 3-7 parts of magnesium oxide, and 2-10 parts of a nucleating agent; the nucleating agent is at least one of calcium fluoride, titanium dioxide, and chromium oxide. After crushing, mixing, and granulating, spherical particles with a particle size of 10-12 mm are formed; and then the product can be obtained after drying, sintering, and cooling. The obtained lightweight aggregate from the invention has a diopside matrix which provides high strength and a low water absorption rate at low densities. Moreover, waste glass and engineering muck could be utilized with high value.