Abstract: An improved aqueous coating agent for providing a decorative and protective coating for wood or wood products contains as a binder polyacrylate resins having chemically incorporated therein air-drying, unsaturated fatty acid moieties and quaternary ammonium moieties, and said agent is prepared by reactingA) excess polyacrylates containing epoxide groups and having an epoxide group equivalent weight of 200 to 1,300 withB) drying fatty acids, in an addition reaction with ester formation,C) reacting at least some of the remaining epoxide groups in the A)-B) reaction product with monoamine ammonium salts which contain an N-H bond in an addition reaction, anddissolving the reaction product obtained from step C) and containing quaternary ammonium groups in water.

Abstract: A process is disclosed for preparing aqueous, oxidatively-drying alkyd resins. The resins are useful as binders in aqueous lacquers and coating compositions.

Abstract: Oxidatively cross-linkable, water dilutable binders suitable for lacquers, coating compositions and sealing compounds are modified co-polymers of olefinically unsaturated compounds, having a molecular weight of 6000 to 160,000 and having for each 100 grams of solids content, a total of from60 to 250 milliequivalents of chemically incorporated carboxyl groups, of which from 10 to 100% are neutralized thereby rendering the product dilutable in water andfrom 15 to 50% by weight of chemically incorporated moieties corresponding to the formula--O--RwhereinR represents an olefinically monounsaturated or polyunsaturated aliphatic hydrocarbon having a molecular weight above 166 and containing from 12 to 22 carbon atoms, are prepared by:(a) preparing a co-polymer having a molecular weight from 5000 to 80,000, determined by gel permeation chromatography, and having intramolecular carboxylic acid anhydride units corresponding to the formula ##STR1## and an anhydride equivalent weight of from 240 to 1960 by a radically i

Abstract: The present invention is directed to a process for the production of urethane- or isocyanurate-modified polyisocyanates based on a starting diisocyanate selected from (i) 2,4-diisocyanatotoluene or mixtures thereof with up to about 35%, based on the mixture, of 2,6-diisocyanatotoluene, (ii) mixtures of the diisocyanates mentioned under (i) with up to 80 NCO equivalent %, based on the mixture, of 1,6-diisocyanatohexane and (iii) 1-isocyanato-3,3,5-trimethyl-5-isocyanatomethyl cyclohexane by reacting the starting diisocyanate with substoichiometric quantities of polyhydric alcohols or trimerizing a portion of the isocyanate groups of the starting diisocyanate, removing sufficient excess, unreacted starting diisocyanate to obtain modified polyisocyanates containing at most 3% by weight, based on solids, of monomeric starting diisocyanate, characterized in that, the content of starting diisocyanate is further reduced by adding at least 10 mol-% water, based on the content of unreacted 2,4-diisocyanatotoluene or 1

Abstract: The present invention is directed to a process for the preparation of polyisocyanates containing urethane groups in which the content in monomeric starting diisocyanate is at most 0.4% by weight by reacting in a urethane-forming reaction(a) an excess quantity, based on component (b), of a diisocyanate component containing at least one aromatic diisocyanate which is free from urethane groups with(b) a polyol component containing at least one polyhydric alcohol in the molecular weight range of 62 to about 250followed by distillative removal of the unreacted excess starting diisocyanate (a), characterized in that before the distillative removal of the excess starting diisocyanate (a) is carried out,(c) an aliphatic polyisocyanate containing isocyanurate groups is incorporated in the urethane-containing reaction product of components (a) and (b) in a quantity of about 0.

Abstract: The invention relates to a sulphonic acid amidamine corresponding to the following general formula I: ##STR1## wherein R.sup.1 represents a C.sub.8 -C.sub.30 linear, saturated aliphatic hydrocarbon group or said group which is substituted by one or more chlorine atoms;R.sup.2 and R.sup.5 independently represent hydrogen or C.sub.1 -C.sub.6 alkyl or C.sub.1 -C.sub.6 alkyl which is substituted with one of the groups: hydroxyl, amino, mercapto, cyano, carboxyl or carbamoyl, and/or is interrupted by at least one oxy (--O--) or thio (--S--) group;R.sup.3 and R.sup.4 independently represent C.sub.2 -C.sub.13 alkylene or C.sub.5 -C.sub.7 cycloalkylene or said alkylene or cycloalkylene groups which are substituted with one of the groups: hydroxyl, amino, mercapto, cyano, carboxyl or carbamoyl;p represents zero or an integer of from 1 to 3;q represents zero or an integer of from 1 to 12; andn represents an integer of from 1 to 8.

Abstract: The present invention is directed to a process for the production of oligourethanes having terminal mercapto groups by reacting organic polyisocyanates with sub-equivalent quantities of organic polyhydroxyl compounds and a mercapto-alkanol in the presence of at least one ester of phosphoric acid containing at least one hydroxyl group bound to phosphorus. The present invention is also directed to the mercapto group-containing oligourethanes obtainable by this process and their use as binders for oxidatively-hardenable coating and sealing compositions, additives for epoxide resins and cross-linking agents for plastics materials and plastics crude products containing olefinic double bonds.

Abstract: The present invention is directed to a process for the preparation of air drying binders containing free isocyanate groups, having thixotropic properties and prepared by reacting aromatic diamines which have at least one alkyl substituent in the ortho position to each amino group with either prepolymers or semi-prepolymers containing free isocyanate groups and based on polyisocyanate mixture of the diphenylmethane series containing at least 20% by weight of 2,4'-diisocyanatodiphenylmethane and organic polyhydroxyl compounds or mixtures of these prepolymers or semi-prepolymers with prepolymers or semi-prepolymers based on other organic polyisocyanates, provided that the mixture contains at least 3% of the prepolymers or semi-prepolymers based on polyisocyanate mixtures of the diphenylmethane series. The invention further relates to the binders produced by this process and their use for the preparation of coating and sealing compounds which harden under the influence of atmospheric moisture.

Abstract: The invention relates to a process for the production of oligourethanes containing terminal mercapto groups by reacting 1-isocyanatomethyl-1,3,3-trimethyl-5-isocyanatocyclohexane with substoichiometric quantities of relatively high molecular weight polyether polyols and mercapto ethanol and to the use of the oligourethanes obtainable in this way as binders for coating and sealing compositions hardenable by oxidation and as additives for epoxide resins.

Abstract: This invention relates to the use of catalyst systems containing (a) dibenzothiazyl disulphide, (b) carboxylates and/or organic complex compounds of manganese, iron, nickel or cobalt and (c) organic bases selected from the group consisting of guanidines and tertiary amines optionally containing inert substituents, as reaction accelerators for the oxidative hardening of plastics precursors containing mercapto groups.

Abstract: The present invention relates to a process for the preparation of coatings using a coating compound based on a system comprising (i) an isocyanate prepolymer based on isophorone diisocyanate and polyalkylene ether polyols having a hydroxyl functionality of 2 to 3 and (ii) at least one diprimary aromatic diamine having at least one alkyl substituent with 2 to 3 carbon atoms in an ortho-position to each amino group.

Abstract: The present invention relates to an insulated one-piece roof for use over heatable rooms comprising at least three layers, the first layer being a solid or other load-bearing construction, the second layer being an insulating board and the third layer being a prepared roofing, said one-piece roof further characterized in that the characteristics value .mu..multidot.s where .mu. is the diffusion resistance index and s is the layer thickness of the constituent material of the vertically adjacent layers, decreases outwardly, said prepared roofing being firmly joined to the underlying insulating board and having a characteristic value .mu..multidot.s of less than 4 m.

Abstract: The instant invention is directed to a process for the preparation of glass constructions comprising applying to glass, compositions comprising(a) a polyisocyanate component and(b) a polyol component comprising at least one dihydroxy polyester carbonate with a molecular weight of from 800 to 3000 which is a reaction product of hexanediol-(1,6) with .epsilon.-caprolactone and/or .epsilon.-hydroxycaproic acid, in a molar ratio of hexanediol-(1,6) to .epsilon.-caprolactone and/or .epsilon.

Abstract: The present invention is concerned with a new class of compounds prepared by reacting cyclic aminals of the formula ##STR1## with polyisocyanates of the formula R.sub.5 (NCO).sub.m+n to yield ##STR2## and with this process for obtaining said compounds, as well as the use of such compounds in polyurethane chemistry. If such compounds are free of isocyanates (n=0) they are useful as latent cross-linkers or hardeners activatable by heat or moisture. If such compounds carry free isocyanate groups (n=1 or 2) there are useful as synthetic resin precursors. In the above formulaem represents an integer of from 1 to 3, andn represents 0, 1 or 2, and the sum of m+n is 2 or 3,R.sub.1 represents an aliphatic hydrocarbon group which is optionally cyano-substituted and which has from 1 to 6 carbon atoms, a cycloaliphatic hydrocarbon group having from 5-10 carbon atoms or an araliphatic hydrocarbon group having from 7-10 carbon atoms;R.sub.

Abstract: The present invention relates to a process for the production of polyureas by reacting organic polyisocyanates containing blocked isocyanate groups with organic compounds containing at least two primary and/or secondary amino groups in the presence of catalysts which accelerate the condensation reaction of the above-mentioned starting materials, characterized in that compounds containing at least one guanidine group corresponding to the following formula: ##STR1## are used as catalysts.

Abstract: An aqueous dispersion of an epoxide compound comprising water, one or more water-insoluble 1,2-epoxide compounds having mol weights Mn of from between 150 and 3000 and an emulsifying system comprising:(A) from 9.5 to 35% by weight of at least one polyester resin containing carboxyl groups having an acid number of from 10 to 50 mg KOH/g substance and a molecular weight Mn of from 400 to 4000, at least 30% of the carboxyl groups being neutralized;(B) from 0.5 to 25% by weight of at least one emulsifier having an HLB-value.gtoreq.15 and represented by the formula: ##STR1## wherein R.sup.1 represents a C.sub.1 -C.sub.16 -alkyl group,R.sup.2 represents H or a C.sub.1 -C.sub.16 -alkyl group,R.sup.3 represents H or methyl,n represents a number from 10 to 50;(C) from 40 to 90% by weight of at least one emulsifier having an HLB-value of 15 and the general formula: ##STR2## wherein R.sup.2 is previously defined, R.sup.4 represents C.sub.1 -C.sub.

Abstract: A water hardenable mixture comprising a blocked polyamine and cyclic anhydride compounds.

Abstract: Hardeners for polyepoxides containing more than one, 1,2-epoxide group per molecule comprising a cyanoethylated polyamide amine containing free secondary or primary or secondary and primary amino groups, said cyanoethylated poly-amide amine is a reaction product of polyadded units of(A) 1 mole of a polyamine corresponding to the formula: ##STR1## in which p=0, n=2 or 3, m=0 to 6 and X=NH.sub.2, or p=1, n=2 or 3, m=0 and X=H,(B) from 0.5 to 2.3 moles of a saturated lactam, and(C) from 0.4 to 2.8 moles of acrylonitrile, methacrylonitrile or mixtures thereof.The hardener may be additionally modified with from 0.01 to 1.8 moles of a 1,2-alkylene oxide containing from 2 to 4 carbon atoms or with from 0.001 to 0.3 moles of a carboxylic acid or with the 1,2-alkylene oxide and the carboxylic acid in the quantities indicated, based in each case on 1 mole of the polyamine.

Abstract: This invention relates to a process for the preparation of new organic compounds having blocked hydroxyl groups, which compounds are converted by the action of moisture into compounds having free hydroxyl groups, the preferred compounds obtainable by this process, and a process for the preparation of polyurethanes in which mixtures containing polyisocyanates and compounds which can be converted into polyols by hydrolysis are reacted with water.

Abstract: The present invention relates to a process for the production of polyisocyanate polyaddition products by reacting organic polyisocyanates with compounds which give off organic diamines under the hydrolytic influence of water and also with water, optionally in the presence of sub-equivalent quantities, based on the NCO-groups present in the reaction mixture, of organic compounds containing isocyanate-reactive hydrogen atoms, wherein polycyclic condensation products of formaldehyde with aliphatic or cycloaliphatic diprimary 1,2-diamines are used as the compounds which give off organic diamines under the hydrolytic influence of water. The present invention also relates to the mixtures preferably used for carrying out this process, containing:(a) at least one organic polyisocyanate; and(b) a moisture-activatable hardener for component (a); distinguished by the fact that condensation products of formaldehyde with aliphatic or cycloaliphatic diprimary 1,2-diamines are used as hardener (b).