Abstract: Provided is a martensitic stainless steel having excellent productivity and high corrosion resistance, which comprises, as percentages by weight, 0.45 to 0.60% carbon, 0.02 to 0.08% nitrogen, 0.2 to 0.4% silicon, 0.3 to 0.6% manganese, 12 to 15% chromium, one or more kinds of 0.1 to 1.5% molybdenum or 0.1 to 1.5% tungsten and Fe and other unavoidable impurities as remnants.

Abstract: Provided is a martensitic stainless steel having excellent productivity and high corrosion resistance, which comprises, as percentages by weight, 0.45 to 0.60% carbon, 0.02 to 0.08% nitrogen, 0.2 to 0.4% silicon, 0.3 to 0.6% manganese, 12 to 15% chrome, one or more kinds of 0.1 to 1.5% molybdenum or 0.1 to 1.5% tungsten and Fe and other unavoidable impurities as remnants.

Abstract: Disclosed is duplex stainless steel that containes relatively low content of Ni, and limits constituents of Cr—Mo—Mn—N to make volume fraction of ? and ? have about 50:50, thereby minimizing incidence of a edge crack to enhance a production yield and decrease a processing load, in which the alloy constituents includes Cr of 19.5˜22.5%. Mo of 0.5-2.5%, Ni if 1.0-3.0%, Mn of 1.5-4.5%, N of 0.15-0.25%, Fe and unavoidable elements, and a constitution range of the alloy constituents are adjusted to make a CPt higher than 20° C. depending on the constitution range of the alloy constituents. Thus, the contents of Cr, Mo and Ni is decreased and the content of Mn is increased a little, so that a production cost thereof is reduced; the corrosion resistance is secured to be better than the STS 304 steel and the 316L steel; the incidence of the edge cract is decreased while being hot-rolled, thereby decreasing a load on the following process; and the surface defective is decreased, thereby improving a production yield.