Abstract: Disclosed is a method of forming a W—Cu composite powder having a Cu particle surrounded by tungsten by mixing and pulverizing tungsten oxide powder and copper oxide powder using turbular mixing or ball milling, reducing the Cu powder firstly at 200˜400° C. under a hydrogen atmosphere or a reducing gas environment including hydrogen, generating W nuclei on the reduced Cu powder at 500˜700° C., and growing the generated W nuclei at 750˜1080° C. as well as a use of the same for the use of powder injection molding.

Abstract: Disclosed is a method of forming a W—Cu composite powder having a Cu particle surrounded by tungsten by mixing and pulverizing tungsten oxide powder and copper oxide powder using turbular mixing or ball milling, reducing the Cu powder firstly at 200˜400° C. under a hydrogen atmosphere or a reducing gas environment including hydrogen, generating W nuclei on the reduced Cu powder at 500˜700° C., and growing the generated W nuclei at 750˜1080° C. as well as a use of the same for the use of powder injection molding.

Abstract: A sintering method for a W--Ni--Mn type heavy alloy, including controlling the deoxidization of tungsten and nickel under an inert atmosphere, changing to a hydrogen atmosphere at above a temperature at which manganese is deoxidized and simultaneously deoxidizing tungsten, nickel and manganese, and sintering by raising the temperature, resulting in the fabrication of a sintered heavy alloy having a 100% relative theoretical density.

Abstract: A fabrication method for a tungsten heavy alloy includes first fabricating a green compact or a sintered body composed of tungsten and other elements except manganese, then putting manganese thereon, and sintering the tungsten heavy alloy with manganese manganese, whereby the formation of pores, which occurs because manganese is oxidized by the deoxidation of oxides existing on the surface of powders of tungsten, nickel and iron is prevented, and a tungsten heavy alloy having a 100% non-theoretical density of 100% is obtained.

Abstract: A method for producing an irregular tungsten/matrix interface in tungsten based heavy alloy is disclosed. The method involves a cyclic heat treatment and resintering at above liquidus temperature for tungsten heavy alloys consisting of 80 to 98 weight % tungsten and remainder of matrix phase. The sintered specimens are cyclically heat treated at above 1000.degree. C. and resintered at liquidus temperature of the matrix phase for one minute to 4 hours at a constant temperature.

Abstract: A tungsten based heavy alloy having a W--Ni--Fe based composition containing traces of lanthanum or calcium, thereby capable of exhibiting high toughness, irrespective of the content of impurities such as phosphorous and sulfur contained therein, the cooling rate after the sintering treatment and the re-heating treatment. The present invention provides a method for making the high toughness tungsten based heavy alloy. The tungsten based heavy alloy of the present invention is useful to manufacture warheads for breaking armor plates, which require high toughness.