Abstract: A steel sheet is provided with a coating having at least one layer of zinc and a top layer of paint applied by cataphoresis. The zinc layer is deposited by a jet vapor deposition process in a deposition chamber maintained at a pressure between 6·10?2 mbar and 2·10?1 mbar. A fabrication method and an installation are also provided.

Abstract: A steel sheet is provided with a coating having at least one layer of zinc and a top layer of paint applied by cataphoresis. The zinc layer is deposited by a jet vapor deposition process in a deposition chamber maintained at a pressure between 6·10?2 mbar and 2·10?1 mbar. A fabrication method and an installation are also provided.

Abstract: A method for fabricating a substrate provided with a plurality of layers, includes: providing a steel substrate with an oxide layer including metal oxides on the steel substrate; providing a metal coating layer directly on the oxide layer, the metal coating layer including: at least 8% by weight nickel; at least 10% by weight chromium; and a remainder being iron and impurities from a fabrication process; and providing an anti-corrosion coating layer directly on the metal coating layer.

Abstract: A method for fabricating a substrate provided with a plurality of layers, includes: providing a steel substrate with an oxide layer including metal oxides on the steel substrate; providing a metal coating layer directly on the oxide layer, the metal coating layer including: at least 8% by weight nickel; at least 10% by weight chromium; and a remainder being iron and impurities from a fabrication process; and providing an anti-corrosion coating layer directly on the metal coating layer.

Abstract: Substrate provided with a plurality of layers, at least one of which includes metal oxides and is topped directly by a metal coating layer that contains at least 8% by weight nickel and at least 10% by weight chromium, the remainder being iron, additional elements and the impurities resulting from the fabrication process, wherein this metal coating layer is topped directly by an anticorrosion coating layer. A corresponding fabrication method is also provided.

Abstract: A steel sheet is provided with a coating having at least one layer of zinc and a top layer of paint applied by cataphoresis. The zinc layer is deposited by a jet vapor deposition process in a deposition chamber maintained at a pressure between 6·10?2 mbar and 2·10?1 mbar. A fabrication method is also provided.

Abstract: A steel sheet is provided with a coating having at least one layer of zinc and a top layer of paint applied by cataphoresis. The zinc layer is deposited by a jet vapor deposition process in a deposition chamber maintained at a pressure between 6·10?2 mbar and 2·10?1 mbar. A fabrication method and an installation are also provided.

Abstract: A method for the fabrication of a coated sheet is provided. The method includes the steps of providing a sheet in a deposition chamber, maintaining the deposition chamber at a pressure Pchamber, maintaining an ejection chamber that is located inside the deposition chamber at a pressure Peject and coating the sheet with zinc with a sonic vapor jet. A ratio of the pressures Pchamber to Peject is between 2·10?3 and 5.5·10?2.

Abstract: Substrate provided with a plurality of layers, at least one of which includes metal oxides and is topped directly by a metal coating layer that contains at least 8% by weight nickel and at least 10% by weight chromium, the remainder being iron, additional elements and the impurities resulting from the fabrication process, wherein this metal coating layer is topped directly by an anticorrosion coating layer. A corresponding fabrication method is also provided.

Abstract: A steel sheet is provided with a coating having at least one layer of zinc and a top layer of paint applied by cataphoresis. The zinc layer is deposited by a jet vapor deposition process in a deposition chamber maintained at a pressure between 6·10?2 mbar and 2·10?1 mbar. A fabrication method is also provided.

Abstract: A steel sheet is provided with a coating. The coating includes at least one layer of zinc, obtained by a jet vapor deposition method in which a ratio between a pressure inside the deposition chamber Pchamber and a pressure inside the zinc ejection chamber Peject is between 2·10?3 et 5.5·10?2 A method for fabricating the steel sheet is also provided.

Abstract: The present application relates to a method for continuously annealing and preparing a strip of high-strength steel for the purpose of hot-dip coating it in a bath of liquid metal, in which said steel strip is treated in at least two sections, comprising in succession, when considering the direction of advance of the strip: a section called the heating and holding section, in which the strip is heated and then held at a given annealing temperature in an oxidizing atmosphere; and a section called the cooling and transfer section, in which the annealed strip at least is cooled and undergoes complete reduction, in a reducing atmosphere, of the iron oxide present in the oxide layer formed in the previous section, in such a way that the oxidizing atmosphere is separated from the reducing atmosphere, a controlled oxygen content is maintained in the heating and holding section between 50 and 1000 ppm, and a controlled hydrogen content is maintained in the cooling and transfer section at a value of less than 4% and p

Abstract: The present application relates to a method for continuously annealing and preparing a strip of high-strength steel for the purpose of hot-dip coating it in a bath of liquid metal, in which said steel strip is treated in at least two sections, comprising in succession, when considering the direction of advance of the strip: a section called the heating and holding section, in which the strip is heated and then held at a given annealing temperature in an oxidizing atmosphere; and a section called the cooling and transfer section, in which the annealed strip at least is cooled and undergoes complete reduction, in a reducing atmosphere, of the iron oxide present in the oxide layer formed in the previous section, in such a way that the oxidizing atmosphere is separated from the reducing atmosphere, a controlled oxygen content is maintained in the heating and holding section between 50 and 1000 ppm, and a controlled hydrogen content is maintained in the cooling and transfer section at a value of less than 4% and p