Abstract: The invention relates to a catalyst for the catalytic esterification and acylation reaction.

Abstract: The present invention is a preparation method for asphalt-based spherical activated carbon which requires no infusibilization process. Placing coal tar asphalt into a melting device; introducing compressed air of 0.1 MPa-0.5 MPa into the device and stirring until a melting temperature of 280° C.-350° C. is reached; continuing for 2-8 hours until the base material has a softening point of 200° C.-260° C.; after cooling down, pulverizing the base material to obtain asphalt powder. Obtaining 34%-79% by mass of carbon powder, 1%-10% by mass of binder, and 20%-65% by mass of the asphalt powder and then forming spherical particles with a diameter of 0.5 mm-5 mm with the carbon powder, the binder and the asphalt powder at room temperature. Introducing the spherical particles of asphalt directly into an asphalt carbonization furnace for carbonization at a temperature of 600° C.-900° C. under protection of an inert gas to obtain asphalt spherical carbon.

Abstract: The invention relates to an application of organic framework porous solid acid.

Abstract: The present invention is a preparation method for asphalt-based spherical activated carbon which requires no infusibilization process. Placing coal tar asphalt into a melting device; introducing compressed air of 0.1 MPa-0.5 MPa into the device and stirring until a melting temperature of 280° C.-350° C. is reached; continuing for 2-8 hours until the base material has a softening point of 200° C.-260° C.; after cooling down, pulverizing the base material to obtain asphalt powder. Obtaining 34%-79% by mass of carbon powder, 1%-10% by mass of binder, and 20%-65% by mass of the asphalt powder and then forming spherical particles with a diameter of 0.5 mm-5 mm with the carbon powder, the binder and the asphalt powder at room temperature. Introducing the spherical particles of asphalt directly into an asphalt carbonization furnace for carbonization at a temperature of 600° C.-900° C. under protection of an inert gas to obtain asphalt spherical carbon.

Abstract: Disclosed is a method for preparing 1-octene in the presence of a catalyst system for ethylene oligomerization, which includes: premixing a part of ethylene gas as raw material with a solvent, mixing with the components a+b, c and d of the catalyst system, and then sending in a reactor; directly sending the rest of ethylene gas in the reactor; discharging the resultant liquid from the upper part of the reactor into an overflow channel; adding a catalysis stopping agent to the overflow channel; and then separating the resultant liquid. The advantages of the method are high selectivity of 1-octene and high catalytic activity.