Abstract: The present disclosure discloses a method for preparing dual-sensitive cellulose-based aerogel. The DAC (Dialdehyde cellulose), the DAC/PDMAEMA (poly-2-(dimethylamino)ethyl methacrylate) copolymer, the DAC/PDMAEMA/PEI (Polyethylenimine) copolymer are serially prepared, was freeze-dried to obtain a product. The product is the dual-sensitive cellulose-based aerogel, a cumulative adsorption capacity of the dual-sensitive cellulose-based aerogel is 250 mg/g, and a cumulative release amount of the dual-sensitive cellulose-based aerogel in 0.05 mol/L NaH2PO4 (pH=3-8), 0.2% NaCl (pH<3), or NaOH (pH>8) is 63-90%.

Abstract: A method for preparing 2,5-bishydroxymethylfuran using 5-chloromethylfurfural, the 5-chloromethylfurfural is transformed into the 2,5-bishydroxymethylfuran using a catalyst, a base neutralizer, sodium dithionite, and deionized water.

Abstract: A catalyst, an application, and a method for preparing 2,5-furanedicarboxylic acid by catalyzing 5-hydroxymethylfurfural in a base-free condition, which include a catalyst having the formula A/MnaBbOx-yVC, wherein A is Pt, Ru, Pd, or Au, B is Co, Ce, Cu, or Ni, a mole ratio of a and b is 1.5-14, and y=0.0-0.4.

Abstract: A method for preparing anisotropic cellulose-based hydrogel is provided. The method comprises ammoniating the dialdehyde cellulose obtained by oxidizing cellulose using sodium periodate to obtain ammoniated cellulose derivatives; performing Schiff reaction using the ammoniated cellulose derivatives and dopamine to obtain cellulose-based nanosheets; depositing Fe3O4 nanoparticles on a surface of the cellulose-based nanosheets by a deposition method to obtain magnetic cellulose-based nanosheets; and forming the anisotropic cellulose-based hydrogel using the magnetic cellulose-based nanosheets by a polymerization method.

Abstract: A method for preparing anisotropic cellulose-based hydrogel is provided. The method comprises ammoniating the dialdehyde cellulose obtained by oxidizing cellulose using sodium periodate to obtain ammoniated cellulose derivatives; performing Schiff reaction using the ammoniated cellulose derivatives and dopamine to obtain cellulose-based nanosheets; depositing Fe3O4 nanoparticles on a surface of the cellulose-based nanosheets by a deposition method to obtain magnetic cellulose-based nanosheets; and forming the anisotropic cellulose-based hydrogel using the magnetic cellulose-based nanosheets by a polymerization method.

Abstract: Bimetal oxide catalyst and methods, a method comprises: mixing and grinding to obtain a mixture comprising a manganese salt (a), at least one of other metal salt (b), and an additive (c), wherein the other metal salt comprises at least one of a copper salt, a cobalt salt, a cerium salt, an iron salt, or a nickel salt, and the additive comprises at least one of polyol or organic acid, and calcining the mixture to obtain the bimetal oxide catalyst.

Abstract: Bimetal oxide catalyst and methods, a method comprises: mixing and grinding to obtain a mixture comprising a manganese salt (a), at least one of other metal salt (b), and an additive (c), wherein the other metal salt comprises at least one of a copper salt, a cobalt salt, a cerium salt, an iron salt, or a nickel salt, and the additive comprises at least one of polyol or organic acid, and calcining the mixture to obtain the bimetal oxide catalyst.

Abstract: The present disclosure discloses a method for preparing dual-sensitive cellulose-based aerogel. The DAC (Dialdehyde cellulose), the DAC/PDMAEMA (poly-2-(dimethylamino)ethyl methacrylate) copolymer, the DAC/PDMAEMA/PEI (Polyethylenimine) copolymer are serially prepared, was freeze-dried to obtain a product. The product is the dual-sensitive cellulose-based aerogel, a cumulative adsorption capacity of the dual-sensitive cellulose-based aerogel is 250 mg/g, and a cumulative release amount of the dual-sensitive cellulose-based aerogel in 0.05 mol/L NaH2PO4 (pH=3-8), 0.2% NaCl (pH<3), or NaOH (pH>8) is 63-90%.