Abstract: A Ni—, Co—, and Mn— multi-element doped positive electrode material for lithium ion batteries and its preparation method are provided. The method for preparing said material consists of: first forming a Ni—, Co—, and Mn— multi-element doped intermediate compound by coprecipitation or chemical synthesis; mixing said multi-element intermediate compound with lithium salt and pre-processing the resulting mixture; adding polyvinyl alcohol into the mixture and mixing uniformly, then pressing the resulting mixture into blocks, and calcining these at 800˜930° C.; cooling outside the furnace, crushing and passing through a 400-mesh sieve; calcining the resulting powder at 700˜800° C., cooling outside the furnace and crushing to obtain the product. The positive electrode material obtained by the method described is in the form of non-agglomerated monocrystal particles, with a particle diameter of 0 5˜30 ?m, the chemical formula LiNixCoyMnzM(1-x-y-z)O2, a compacted density of up to 3.

Abstract: The present invention discloses a high compact density nickel-cobalt-manganese multi-element lithium ion battery cathode material with dopants and methods of its preparation. A preparation method of this battery cathode material is as follows: (A) preparing a nickel-cobalt-manganese multi-element intermediate with dopants by co-precipitation or chemical synthesis; (B) preparing a mixture by mixing said multi-element intermediate with a lithium salt; (C) pre-treating the said mixture, then adding into it polyvinyl alcohol and mixing uniformly; (D) pressing the resulting material into lumps, calcining the lumps at 800˜950° C., cooling after its removal from the furnace, crushing, passing through a 400 mesh sieve; (E) calcining the resulting power at 700˜800° C., cooling after its removal from the furnace, crushing and sieving to obtain a product. The lithium battery cathode material obtained using the above-described method has the formula LiNixCoyMnzM(1-x-y-z)O2.

Abstract: The present invention discloses a high compact density nickel-cobalt-manganese multi-element lithium ion battery cathode material with dopants and methods of its preparation. A preparation method of this battery cathode material is as follows: (A) preparing a nickel-cobalt-manganese multi-element intermediate with dopants by co-precipitation or chemical synthesis; (B) preparing a mixture by mixing said multi-element intermediate with a lithium salt; (C) pre-treating the said mixture, then adding into it polyvinyl alcohol and mixing uniformly; (D) pressing the resulting material into lumps, calcining the lumps at 800˜950° C., cooling after its removal from the furnace, crushing, passing through a 400 mesh sieve; (E) calcining the resulting power at 700˜800° C., cooling after its removal from the furnace, crushing and sieving to obtain a product. The lithium battery cathode material obtained using the above-described method has the formula LiNixCoyMnzM(1-x-y-z)O2.

Abstract: A Ni—, Co—, and Mn— multi-element doped positive electrode material for lithium ion batteries and its preparation method are provided. The method for preparing said material consists of: first forming a Ni—, Co—, and Mn— multi-element doped intermediate compound by coprecipitation or chemical synthesis; mixing said multi-element intermediate compound with lithium salt and pre-processing the resulting mixture; adding polyvinyl alcohol into the mixture and mixing uniformly, then pressing the resulting mixture into blocks, and calcining these at 800˜930° C.; cooling outside the furnace, crushing and passing through a 400-mesh sieve; calcining the resulting powder at 700˜800° C., cooling outside the furnace and crushing to obtain the product. The positive electrode material obtained by the method described is in the form of non-agglomerated monocrystal particles, with a particle diameter of 0 5˜30 ?m, the chemical formula LiNixCoyMnzM(1-x-y-z)O2, a compacted density of up to 3.