Abstract: A composite material, wherein the composite material contains aluminum alloys with at least one of alkaline-earth metals and transition metals, and are used for removing pollutants by dissolving to release divalent metal ions, trivalent aluminum ions and hydroxide ions, which contact with other divalent and trivalent metal cations and anions in the contaminated water, to perform an in situ self-assemble of two-dimensional Layered Double Hydroxides (LDH) precipitates; consists of 18-70 weight % of aluminum metal, 30-80% weight of a second type of metal, and 0-2 weight % of an auxiliary agent; has a particle size of 0.01-3 mm; and preferably forms a micro-nano Alloy@LDH composite material with a core-shell structure by pretreating with dilute HCl. The present invention is used for soil remediation or sewage purification, and is suitable for chemical removal and degradation of complex contaminants from an acidic to alkaline environment.

Abstract: A high-temperature-resistant water-based varnish, comprising the following components in parts by weight: 80-90 parts of an acrylic emulsion and 10-20 parts of a zinc ammonia polytetrafluoroethylene emulsion. The solid content of the acrylic emulsion is 45-55 wt %, and the solid content of the zinc ammonia polytetrafluoroethylene emulsion is 45-55 wt %. Further disclosed are a preparation method for the high-temperature-resistant water-based varnish and an obtained high-temperature-resistant coating; the temperature resistance of the obtained high-temperature-resistant coating is not less than 220° C.

Abstract: A composite material, wherein the composite material contains aluminum alloys with at least one of alkaline-earth metals and transition metals, and are used for removing pollutants by dissolving to release divalent metal ions, trivalent aluminum ions and hydroxide ions, which contact with other divalent and trivalent metal cations and anions in the contaminated water, to perform an in situ self-assemble of two-dimensional Layered Double Hydroxides (LDH) precipitates; consists of 18-70 weight% of aluminum metal, 30-80% weight of a second type of metal, and 0-2 weight% of an auxiliary agent; has a particle size of 0.01-3 mm; and preferably forms a micro-nano Alloy@LDH composite material with a core-shell structure by pretreating with dilute HCl. The present invention is used for soil remediation or sewage purification, and is suitable for chemical removal and degradation of complex contaminants from an acidic to alkaline environment.