Abstract: A method for passivating tantalum metal surface is provided, the method comprises cooling tantalum metal to or below 32° C. and/or passivating tantalum metal surface by oxygen-containing gas with a temperature of 0° C. or below. Also provided is an apparatus for passivating tantalum metal surface for applying the method, comprising a heat treatment furnace, an argon forced-cooling device and/or a device for cooling oxygen-containing gas.

Abstract: The present invention provides a process for preparing a tantalum powder with high specific capacity, which process comprising the steps of, in sequence, (1) a first reduction step: mixing tantalum oxide powder and a first reducing agent powder homogenously, and then carrying out reduction reaction in hydrogen and/or inert gas or vacuum atmosphere to obtain a tantalum suboxides powder; (2) a second reduction step: mixing the tantalum suboxides powder obtained from the step (1), in which impurities have been removed, and a second reducing agent powder homogenously, and then carrying out reduction reaction in hydrogen and/or inert gas or vacuum atmosphere to obtain a tantalum powder having high oxygen content; (3) a third reduction step: mixing the tantalum powder having high oxygen content obtained from the step (2), in which impurities have been removed, with a third reducing agent powder homogenously, and then carrying out reduction reaction in hydrogen and/or inert gas or vacuum atmosphere to obtain a tanta

Abstract: The present invention provides a process for preparing a tantalum powder with high specific capacity, which process comprising the steps of, in sequence, (1) a first reduction step: mixing tantalum oxide powder and a first reducing agent powder homogenously, and then carrying out reduction reaction in hydrogen and/or inert gas or vacuum atmosphere to obtain a tantalum suboxides powder; (2) a second reduction step: mixing the tantalum suboxides powder obtained from the step (1), in which impurities have been removed, and a second reducing agent powder homogenously, and then carrying out reduction reaction in hydrogen and/or inert gas or vacuum atmosphere to obtain a tantalum powder having high oxygen content; (3) a third reduction step: mixing the tantalum powder having high oxygen content obtained from the step (2), in which impurities have been removed, with a third reducing agent powder homogenously, and then carrying out reduction reaction in hydrogen and/or inert gas or vacuum atmosphere to obtain a tanta

Abstract: The present invention relates to a process for preparing powders of niobium suboxides or niobium, wherein the process comprising: mixing the niobium oxides as raw material with reducing agent, conducting a reaction at a temperature in the range of 600˜1300° C. in an atmosphere of vacuum or inert gas or hydrogen gas, leaching the reaction product to remove the residual reducing agent and the oxides of the reducing agent and other impurities, heat treating at a temperature of the range of 1000˜1600° C. in an atmosphere of vacuum or inert gas, and screening to obtain the powders of niobium suboxide or niobium of capacitor grade. According to the present invention, the niobium oxides were directly reduced into capacitor grade niobium suboxides or niobium with reducing agents which can be easily removed by mineral acids, wherein the speed of the reaction can be controlled and the reaction can directly reduce the niobium oxides into capacitor grade niobium suboxides or niobium powder.

Abstract: The present invention relates to a process for preparing powders of niobium suboxides or niobium, wherein the process comprising: mixing the niobium oxides as raw material with reducing agent, conducting a reaction at a temperature in the range of 600˜1300° C. in an atmosphere of vacuum or inert gas or hydrogen gas, leaching the reaction product to remove the residual reducing agent and the oxides of the reducing agent and other impurities, heat treating at a temperature of the range of 1000˜1600° C. in an atmosphere of vacuum or inert gas, and screening to obtain the powders of niobium suboxide or niobium of capacitor grade. According to the present invention, the niobium oxides were directly reduced into capacitor grade niobium suboxides or niobium with reducing agents which can be easily removed by mineral acids, wherein the speed of the reaction can be controlled and the reaction can directly reduce the niobium oxides into capacitor grade niobium suboxides or niobium powder.