Abstract: The present invention discloses a non-oriented electrical steel plate, wherein the steel plate comprises, in addition to Fe and inevitable impurities, the following chemical elements in percentage by mass: 0<C<0.01%, 0<Si?4.5%, Mn: 0.05˜2.0%, AI: 0.1˜2.0%, Cr: 0.005˜0.2%; the mass percentage ratio of Al to Cr satisfies: 10?Al/Cr?80. In addition, the present invention also discloses a method for manufacturing the above-mentioned non-oriented electrical steel plate, comprising the following steps: (1) smelting and casting to obtain a continuous casting slab; (2) heating and rolling to obtain a hot-rolled steel plate, wherein when the continuous casting slab is heated in a heating furnace and a temperature is raised to 1020° C. or more, a heating rate is controlled to be 0.8˜2.0° C./min; and a soaking time of the continuous casting slab in the heating furnace/a time of the continuous casting slab in the heating furnace is controlled to be 0.10-0.

Abstract: Disclosed are a non-oriented electrical steel sheet with excellent magnetic properties and a manufacturing method thereof, wherein the mass percentage of the chemical components thereof are: C: 0-0.005%; Si: 2.1-3.2%, Mn: 0.2-1.0%, P: 0-0.2%, Al: 0.2-1.6%, N: 0-0.005%, Ti: 0-0.005%, Cu: 0-0.2%, and the balance of Fe and inevitable impurities; and at the same time, (the S content for forming MnS+the S content for forming CuxS)/the S content in the steel is required to be less than or equal to 0.2. The process for manufacturing the non-oriented electrical steel sheet of the present invention is simple and convenient, the chemical components of the steel are easy to control, the manufacturing process is stable, and the technical requirements are easy to realize.

Abstract: A non-oriented electrical steel having excellent magnetic properties, the chemical elements thereof in percentage by mass being: Si: 0.2-1.5%, Mn: 0.01-0.30%, Al: 0.001-0.009%, O: 0.005-0.02%, C?0.005%, S?0.005%, N?0.005%, and Ti?0.002%, the remainder being Fe and other unavoidable impurities, and Al/Si?0.006 and Mn/Si?0.2. The method for producing comprises the following sequence of steps: (1) smelting; (2) hot rolling: the slab heating temperature being 850° C. to 1250° C., and the final rolling temperature being 800-1050° C.; (3) acid pickling; (4) cold rolling; (5) annealing: the annealing plate temperature being controlled between 620° C.-900° C.; and (6) coating.

Abstract: Disclosed are a non-oriented electrical steel sheet with excellent magnetic properties and a manufacturing method thereof, wherein the mass percentage of the chemical components thereof are: C: 0-0.005%; Si: 2.1-3.2%, Mn: 0.2-1.0%, P: 0-0.2%, Al: 0.2-1.6%, N: 0-0.005%, Ti: 0-0.005%, Cu: 0-0.2%, and the balance of Fe and inevitable impurities; and at the same time, (the S content for forming MnS+the S content for forming CuxS)/the S content in the steel is required to be less than or equal to 0.2. The process for manufacturing the non-oriented electrical steel sheet of the present invention is simple and convenient, the chemical components of the steel are easy to control, the manufacturing process is stable, and the technical requirements are easy to realize.

Abstract: Disclosed is a non-oriented electrical steel plate having a good surface state, a high magnetic induction and a low iron loss, the contents of various chemical elements of the non-oriented electrical steel plate in mass percentage being: 0<C?0.004%, 0.1%?Si?1.6%, 0.1%?Mn?0.8%, 0.1%?Al?0.6%, Ti?0.0015%, and the balance being Fe and other inevitable impurities, with 0.2%?(Si+Al)?2.0% being met. Also disclosed is a method for manufacturing the above-mentioned steel plate, comprising the steps: a liquid iron pretreatment, smelting with a converter, RH refining, casting into slabs, hot rolling, acid pickling, cold rolling, annealing and coating. The non-oriented electrical steel plate of the present invention has an excellent magnetic property, an ultralow iron loss and a higher steel purity; in addition the surface quality of the steel plate is good and the production cost is low.

Abstract: A non-oriented electrical steel having excellent magnetic properties, the chemical elements thereof in percentage by mass being: Si: 0.2-1.5%, Mn: 0.01-0.30%, Al: 0.001-0.009%, O: 0.005-0.02%, C?0.005%, S?0.005%, N?0.005%, and Ti?0.002%, the remainder being Fe and other unavoidable impurities, and Al/Si?0.006 and Mn/Si?0.2. The method for producing comprises the following sequence of steps: (1) smelting; (2) hot rolling: the slab heating temperature being 850° C. to 1250° C., and the final rolling temperature being 800-1050° C.; (3) acid pickling; (4) cold rolling; (5) annealing: the annealing plate temperature being controlled between 620° C.-900° C.; and (6) coating.

Abstract: Disclosed is a non-oriented electrical steel plate having a good surface state, a high magnetic induction and a low iron loss, the contents of various chemical elements of the non-oriented electrical steel plate in mass percentage being: 0<C?0.004%, 0.1%?Si?1.6%, 0.1%?Mn?0.8%, 0.1%?Al?0.6%, Ti?0.0015%, and the balance being Fe and other inevitable impurities, with 0.2%?(Si+Al)?2.0% being met. Also disclosed is a method for manufacturing the above-mentioned steel plate, comprising the steps: a liquid iron pretreatment, smelting with a converter, RH refining, casting into slabs, hot rolling, acid pickling, cold rolling, annealing and coating. The non-oriented electrical steel plate of the present invention has an excellent magnetic property, an ultralow iron loss and a higher steel purity; in addition the surface quality of the steel plate is good and the production cost is low.