Abstract: Disclosed in the present invention is a non-oriented electrical steel plate with good magnetic performance. The non-oriented electrical steel plate contains Fe and inevitable impurities, and further contains the following chemical elements, in percentage by mass: 0<C?0.0015%, Si: 0.2-1.8%, Mn: 0.2-0.4%, Al: 0.2-0.6%, V: 0.002-0.005%, and N<0.002%. In addition, further disclosed in the present invention is a manufacturing method for the non-oriented electrical steel plate with good magnetic performance. The manufacturing method comprises the steps of: (1) smelting and casting: (2) hot rolling, wherein a steel coil obtained after the hot rolling is directly introduced to the next step without being subjected to normalizing annealing or cover annealing; (3) acid pickling; (4) cold rolling; and (5) continuous annealing, wherein the steel plate is heated to a target soaking temperature at a heating rate of 50-5000° C./s after the cold rolling.