Abstract: A non-sintered high-strength lightweight aggregate one-shot prepared from sulfur-based and alkaline-based solid wastes by stirring, granulation, and foaming, and a preparation method therefor and use thereof. The non-sintered high-strength lightweight aggregate is prepared from a sulfur-based solid waste, an alkaline-based solid waste, an auxiliary cementing material, a ferro-aluminum-sulfur cementing material, water, and a foaming agent as raw materials. Based on the mass of the total solid, the total content of the sulfur-based solid waste, the alkaline-based solid waste, and the auxiliary cementing material is 80-90 wt %, and the content of the ferro-aluminum-sulfur cementing material is 10-20 wt %. The mass ratio of the water to the total solid is (15-20):(80-85). The foaming agent accounts for 0.3-0.7% of the mass of the total solid. The mass ratio between the sulfur-based solid waste, the alkaline-based solid waste, and the auxiliary cementing material is (27-33):(27-33):(18-25).

Abstract: A method and system for producing low-alkalinity sulphoaluminate cement with a new mineral system using steel slag. The method includes the following steps: evenly mixing and homogenizing ground steel slag with dry desulfurization gypsum, aluminum ash and carbide slag according to a set ratio; and conveying the homogenized raw meal to a rotary kiln for calcination to obtain cement clinker, where the calcination temperature is 1200° C.-1270° C., and the calcination time is 20-60 min; the alkalinity modulus of the homogenized cement raw meal is 0.81-0.9, and the Fe2O3 content is 8-13%. The method breaks through the requirements on contents of calcium, aluminum and iron in traditional sulphoaluminate cement production, and realizes application of a large amount of steel slag.

Abstract: A method and system for producing low-alkalinity sulphoaluminate cement with a new mineral system using steel slag. The method includes the following steps: evenly mixing and homogenizing ground steel slag with dry desulfurization gypsum, aluminum ash and carbide slag according to a set ratio; and conveying the homogenized raw meal to a rotary kiln for calcination to obtain cement clinker, where the calcination temperature is 1200° C.-1270° C., and the calcination time is 20-60 min; the alkalinity modulus of the homogenized cement raw meal is 0.81-0.9, and the Fe2O3 content is 8-13%. The method breaks through the requirements on contents of calcium, aluminum and iron in traditional sulphoaluminate cement production, and realizes application of a large amount of steel slag.