Abstract: The present disclosure relates to a chromium-aluminum binary alloy with excellent corrosion resistance and a method of producing the same, and more particularly to a chromium-aluminum binary alloy with excellent corrosion resistance. The chromium-aluminum binary alloy may be easily produced and has ductility, thus being highly applicable as a coating material for a material requiring high-temperature corrosion resistance and wear resistance.

Abstract: A method of a nuclear fuel pellet including a thermal conductive metal and a nuclear fuel pellet prepared thereby. The method includes preparing an oxide nuclear fuel granule having about 30%-45% theoretical density, mixing the fuel granule with thermal conductive metal powder, compacting the fuel granule with which the thermal conductive metal powder is mixed to prepare a green pellet, and sintering the green pellet. In the method, the sintering may be performed under a reducing gas atmosphere that is the same as the commercial pellet preparing process. Thus, compatibility compared to existing commercial preparing processes may be superior. Also, since a liquefied oxide formation process and a reducing process are omitted, the distribution uniformity of the metal material within the pellet may be superior. Therefore, the nuclear fuel pellet in which the metal network and fine microstructure are uniformly distributed within the pellet may be prepared.

Abstract: A uranium dioxide nuclear fuel pellet has about 50 to about 400 ?M (with respect to a 3-dimentional size) microcells formed of a ceramic material having a chemical attraction with fission products generated in the nuclear fuel pellet to absorb and trap the fission products, such that the extraction of the fission product may be retrained in a normal operation condition and that the performance of the nuclear fuel may be enhanced by mitigating PCI. In addition, highly radioactive fission products including Cs and I having a large generation amount or a long half-life enough to affect the environments can be trapped in the pellet in an accident condition, without being released outside.

Abstract: The present disclosure relates to a chromium-aluminum binary alloy with excellent corrosion resistance and a method of producing the same, and more particularly to a chromium-aluminum binary alloy with excellent corrosion resistance. The chromium-aluminum binary alloy may be easily produced and has ductility, thus being highly applicable as a coating material for a material requiring high-temperature corrosion resistance and wear resistance.

Abstract: Disclosed is a uranium dioxide nuclear fuel pellet, which includes metallic microcell partitions having a high protection capacity for fission products and a high thermal conductivity simultaneously. These metal microcell partitions are arranged in the nuclear fuel pellet to trap fission products. Further disclosed is a method of making the uranium dioxide nuclear fuel pellet. The method includes providing a mixture of uranium dioxide powder and additive powder of Cr-containing compound or Mo-containing compound; compressing the powder mixture to form a green pellet; and then sintering the green pellet under reducing gas environment to form the metallic microcell partitions.

Abstract: A fabrication method of burnable absorber nuclear fuel pellets and burnable absorber nuclear fuel pellets fabricated by the same are provided, in which the fabrication method includes adding boron compound and manganese compound to one or more type of nuclear fuel powders selected from the group consisting of uranium dioxide (UO2), plutonium dioxide (PuO2) and thorium dioxide (ThO2) and mixing the same (step 1), compacting the mixed powder of step 1 into compacts (step 2), and sintering the compacts of step 2 under hydrogen atmosphere (step 3). According to the fabrication method, sintering can be performed under hydrogen atmosphere at a temperature lower than the hydrogen atmosphere sintering that is conventionally applied in the nuclear fuel sintered pellet mass production, by adding sintering additives such as manganese oxide or the like.

Abstract: A method of a nuclear fuel pellet including a thermal conductive metal and a nuclear fuel pellet prepared thereby. The method includes preparing an oxide nuclear fuel granule having about 30%-45% theoretical density, mixing the fuel granule with thermal conductive metal powder, compacting the fuel granule with which the thermal conductive metal powder is mixed to prepare a green pellet, and sintering the green pellet. In the method, the sintering may be performed under a reducing gas atmosphere that is the same as the commercial pellet preparing process. Thus, compatibility compared to existing commercial preparing processes may be superior. Also, since a liquefied oxide formation process and a reducing process are omitted, the distribution uniformity of the metal material within the pellet may be superior. Therefore, the nuclear fuel pellet in which the metal network and fine microstructure are uniformly distributed within the pellet may be prepared.

Abstract: A zirconium alloy for use in nuclear fuel assemblies is provided, which provides increased resistance against oxidation and corrosion and also improved bonding with parent material, because pure metallic material such as silicon (Si) or chromium (Cr) is evenly coated on the surface of the parent material by plasma spraying. Because the plasma spray coating used to coat the pure metallic material on the zirconium alloy does not require vacuum equipment and also is not limited due to the shape of the coated product, this is particularly useful when evenly treating the surface of the component such as 4 m-long tube or spacer grip arrangement which is very complicated in shape. Furthermore, because the coated zirconium alloy confers excellent resistance to oxidation and corrosion under emergency such as accident as well as normal service condition, both the economic and safety aspects of nuclear fuel are improved.

Abstract: The present disclosure relates to a chromium-aluminum binary alloy with excellent corrosion resistance and a method of producing the same, and more particularly to a chromium-aluminum binary alloy with excellent corrosion resistance, including: 1 to 40% by weight of aluminum (Al), the balance of chromium (Cr), and other unavoidable impurities with respect to a total weight of the alloy, and a method of producing a chromium-aluminum binary alloy with excellent corrosion resistance, the method including: (Step 1) mixing and melting a raw material comprising: 1 to 40% by weight of aluminum (Al), the balance of chromium (Cr), and other unavoidable impurities with respect to a total weight of the alloy; and (Step 2) solution treating the alloy melted in Step 1. The chromium-aluminum binary alloy may be easily produced and has ductility, thus being highly applicable as a coating material for a material requiring high-temperature corrosion resistance and wear resistance.

Abstract: Disclosed are a zirconium alloy for a nuclear fuel cladding having a good corrosion resistance by reducing an amount of alloying elements and a method of preparing a zirconium alloy nuclear fuel cladding using thereof. The zirconium alloy includes 0.2 to 0.5 wt % of niobium (Nb); 0.2 to 0.6 wt % of iron (Fe); 0.3 to 0.5 wt % of chromium (Cr); 0.1 to 0.15 wt % of oxygen (O); 0.008 to 0.012 wt % of silicon (Si) and a remaining amount of zirconium (Zr). The total amount of the niobium, the iron and the chromium is 1.1 to 1.2 wt %. A good oxidation resistance of the nuclear fuel cladding may be confirmed under accident conditions as well as normal operating conditions of a reactor, thereby improving economic feasibility and safety.

Abstract: Disclosed are a zirconium alloy for a nuclear fuel cladding having a good corrosion resistance by reducing an amount of alloying elements and a method of preparing a zirconium alloy nuclear fuel cladding using thereof. The zirconium alloy includes 0.2 to 0.5 wt % of niobium (Nb); 0.2 to 0.6 wt % of iron (Fe); 0.3 to 0.5 wt % of chromium (Cr); 0.1 to 0.15 wt % of oxygen (O); 0.008 to 0.012 wt % of silicon (Si) and a remaining amount of zirconium (Zr). The total amount of the niobium, the iron and the chromium is 1.1 to 1.2 wt %. A good oxidation resistance of the nuclear fuel cladding may be confirmed under accident conditions as well as normal operating conditions of a reactor, thereby improving economic feasibility and safety.

Abstract: Disclosed are a zirconium alloy for a nuclear fuel cladding having a good oxidation resistance in a severe reactor operation condition and a method of preparing zirconium alloy nuclear fuel claddings by using thereof. The zirconium alloy includes 1.8 to 2.0 wt % of niobium (Nb); at least one element selected from iron (Fe), chromium (Cr) and copper (Cu); 0.1 to 0.15 wt % of oxygen (O); 0.008 to 0.012 wt % of silicon (Si) and a remaining amount of zirconium (Zr). The amount of Fe is 0.1 to 0.4 wt %, the amount of Cr is 0.05 to 0.2 wt %, and the amount of Cu is 0.03 to 0.2 wt %. A good oxidation resistance of the nuclear fuel cladding may be confirmed under a severe reactor operation condition at an accident condition as well as a normal operating condition of a reactor, thereby improving economic efficiency and safety.

Abstract: Disclosed are a zirconium alloy for a nuclear fuel cladding having a good oxidation resistance in reactor accident conditions, a zirconium alloy nuclear fuel cladding prepared by using thereof and a method of preparing the same. The zirconium alloy includes 1.0 to 1.2 wt % of niobium (Nb); at least one element selected from tin (Sn), iron (Fe) and chromium (Cr); 0.02 to 0.1 wt % of copper (Cu); 0.1 to 0.15 wt % of oxygen (O); 0.008 to 0.012 wt % of silicon (Si) and a remaining amount of zirconium (Zr). The amount of Sn is 0.1 to 0.3 wt %, the amount of Fe is 0.3 to 0.8 wt %, and the amount of Cr is 0.1 to 0.3 wt %. A good oxidation resistance of the nuclear fuel cladding may be confirmed under accident conditions as well as normal operating conditions of a reactor, thereby improving economic efficiency and safety.

Abstract: A uranium dioxide nuclear fuel pellet includes metallic microcells having a high protection capacity for fission products and a high thermal conductivity simultaneously arranged in the nuclear fuel pellet to trap fission products, such that extraction of fission products may be restrained in a normal operation condition and that the temperature of a nuclear fuel may be lowered to enhance the performance of the nuclear fuel, only to restrain extraction of radioactive fission products toward the environment in an accident condition to enhance a stability of the nuclear fuel pellet, and a fabricating method thereof.

Abstract: A uranium dioxide nuclear fuel pellet has about 50 to about 400 ?M (with respect to a 3-dimentional size) microcells formed of a ceramic material having a chemical attraction with fission products generated in the nuclear fuel pellet to absorb and trap the fission products, such that the extraction of the fission product may be retrained in a normal operation condition and that the performance of the nuclear fuel may be enhanced by mitigating PCI. In addition, highly radioactive fission products including Cs and I having a large generation amount or a long half-life enough to affect the environments can be trapped in the pellet in an accident condition, without being released outside.

Abstract: A zirconium alloy with a coating layer formed on a surface comprising a mixed layer, the mixed layer comprises one or more very high temperature oxidation resistant material and zirconium alloy parent material selected from the group consisting of Y2O3, SiO2, ZrO2, Cr2O3, Al2O3, Cr3C2, SiC, ZrC, ZrN, Si and Cr, and in a vertical direction on a boundary between the mixed layer and the zirconium alloy parent material is formed a gradient of compositions between the very high temperature oxidation resistance material and the zirconium alloy parent material.

Abstract: Disclosed is a breeding nuclear fuel mixture including metallic thorium useable in a nuclear power plant, prepared by mixing uranium dioxide (UO2) or plutonium dioxide (PuO2) having ceramic properties with metallic thorium (Th), in order to enable thorium breeding by neutrons released during nuclear fission of U or Pu and conversion of the bred thorium into a novel nuclear fissile material, i.e., U-233, thereby ensuring continuous nuclear fission. The foregoing nuclear fuel mixture may be burned at a reactor core of a nuclear power plant through thorium breeding over a long period of time. Therefore, when the inventive breeding nuclear fuel mixture is employed in a nuclear power plant, utilization of the nuclear power plant may be increased while maximizing conservation of limited uranium resources.