Abstract: The present disclosure discloses a preparation method and use of a high-performance modified lithium-nickel-manganese-cobalt oxide (LNMCO) nickel 55 material. In the preparation method of the present disclosure, a silica template-containing nano-precursor coated with a polymer is prepared by electrospinning, and then the nano-precursor is sintered in the air to effectively provide effective embedding and attachment sites for subsequent nickel plating; and after the nickel plating, the silica template is removed such that distributed mesopores are generated in situ on the precursor. The mesopores provide channels for the subsequent penetration of molten lithium into the interior of the precursor material. A final prepared material has a better ion and electron conduction structure compared with traditional granular materials. The present disclosure also discloses a material prepared by the method. The present disclosure also discloses an LIB including the high-performance modified LNMCO nickel 55 material.

Abstract: A method for preparing nickel-cobalt-manganese hydroxide. The method comprises the following steps: (1) dissolving microcrystalline cellulose into water to obtain a suspension; and adding a nickel source, a cobalt source, and a manganese source into the suspension to obtain a solution containing nickel, cobalt, and manganese; (2) adding hexamethylenetetramine into the solution containing nickel, cobalt, and manganese, heating the reaction solution to 80-90° C., and reacting for 5-10 min, then heating with a microwave hydrothermal synthesis instrument at a frequency of 2450 MHz for 10-60 min; and (3) filtering the reaction solution obtained in step (2), and taking the filter residue, washing the filter residue with pure water and ethanol respectively, then drying, crushing, and screening the filter residue to obtain nickel-cobalt-manganese hydroxide.

Abstract: The present invention relates to the technical field of preparation of a nickel cobalt lithium manganese oxide positive electrode material. Disclosed are a power-type nickel cobalt lithium manganese oxide material and a preparation method therefor and uses thereof. The preparation method comprises: adding an organic acid into a mixed aqueous solution of a lithium source, a nickel source, a cobalt source and a manganese source, aging, obtaining a sol precursor, obtaining a gel fiber through electrospinning, and obtaining the power-type nickel cobalt lithium manganese oxide material after calcination. In the present invention, the nickel cobalt lithium manganese oxide material of a nano-fiber structure is prepared by using a sol-gel electrospinning method, and the nickel cobalt lithium manganese oxide material of a nano-fiber structure has a uniform structure size, thereby effectively reducing surface energy, and improving a capacity of lithium ions.

Abstract: A method for preparing nickel-cobalt-manganese hydroxide. The method comprises the following steps: (1) dissolving microcrystalline cellulose into water to obtain a suspension; and adding a nickel source, a cobalt source, and a manganese source into the suspension to obtain a solution containing nickel, cobalt, and manganese; (2) adding hexamethylenetetramine into the solution containing nickel, cobalt, and manganese, heating the reaction solution to 80-90° C., and reacting for 5-10 min, then heating with a microwave hydrothermal synthesis instrument at a frequency of 2450 MHz for 10-60 min; and (3) filtering the reaction solution obtained in step (2), and taking the filter residue, washing the filter residue with pure water and ethanol respectively, then drying, crushing, and screening the filter residue to obtain nickel-cobalt-manganese hydroxide.