Abstract: A composite strip of compacted powders, which has a three layers structure, is continuously obtained by means of a rolling machine for powder compacting. The composite strip is sintered at a temperature of 460° C. to 550° C. to form a sintered composite strip. The sintered composite strip is continuously bonded by rolling to a steel strip. The bonded composite strip is optionally subjected to a heat treatment of heating at a temperature of 250° C. to 400° C. followed by heating to a temperature of 400° C. to 510° C., holding the strip under the temperature for not less than 30 seconds, and rapidly cooling down to 300° C. at a cooling rate of not lower than 50° C./minute, whereby obtaining a multi-layered composite material consisting of the steel strip, a sintered bonding layer, a sintered sliding layer and a sintered sacrificial layer.

Abstract: A composite strip of compacted powders, which has a three layers structure, is continuously obtained by means of a rolling machine for powder compacting. The composite strip is sintered at a temperature of 460° C. to 550° C. to form a sintered composite strip. The sintered composite strip is continuously bonded by rolling to a steel strip. The bonded composite strip is optionally subjected to a heat treatment of heating at a temperature of 250° C. to 400° C. followed by heating to a temperature of 400° C. to 510° C., holding the strip under the temperature for not less than 30 seconds, and rapidly cooling down to 300° C. at a cooling rate of not lower than 50° C./minute, whereby obtaining a multi-layered composite material consisting of the steel strip, a sintered bonding layer, a sintered sliding layer and a sintered sacrificial layer.