Abstract: In a preliminary molding step 1, a metallic powder mixture 7 obtained by blending an iron-based metal powder 7a with graphite 7b such that the graphite is present in an amount of preferably not less than 0.1% by weight, more preferably not less than 0.3% by weight, is compacted into a preform 8 having a density of not less than 7.3 g/cm3. In a provisional sintering step 2, the preform 8 is provisionally sintered at a predetermined temperature to form a metallic powder-molded body 9 having a structure in which the graphite remains along a grain boundary of the metal powder. In a re-compaction step 3, the metallic powder-molded body 9 is re-compacted into a re-compacted body 10. In a re-sintering step 4, the re-compacted body 10 is re-sintered to obtain a sintered body 11. In a heat treatment step 5, the sintered body 11 is heat-treated to obtain a heat-treated sintered body 11.

Abstract: A sintered iron-based powder metal body with lower re-compacting load and having a high density and a method of manufacturing an iron-based sintered component with fewer pores of a sharp shape and having high strength and high density.

Abstract: An sintered iron-based powder metal body with outstandingly lower re-compacting load and having a high density and a method of manufacturing an iron-based sintered component with fewer pores of a sharp shape and having high strength and high density, the method comprising mixing,

Abstract: An sintered iron-based powder metal body with outstandingly lower re-compacting load and having a high density and a method of manufacturing an iron-based sintered component with fewer pores of a sharp shape and having high strength and high density, the method comprising mixing, an iron-based metal powder containing at most about 0.05% of carbon, at most about 0.3% of oxygen, at most about 0.010% of nitrogen, with at least about 0.03% and at most about 0.5% of graphite powder and a lubricant, preliminarily compacting the mixture into a preform, the density of which is about 7.3 Mg/m3 or more, and preliminarily sintering the preform in a non-oxidizing atmosphere in which a partial pressure of nitrogen is about 30 kPa or less at a temperature of about 1000° C. or higher and about 1300° C. or lower, thereby forming a sintered iron-based powder metal body with outstandingly lower re-compacting load and having high deformability, the density of which is about 7.

Abstract: In a preliminary molding step 1, a metallic powder mixture 7 obtained by blending an iron-based metal powder 7a with graphite 7b such that the graphite is present in an amount of preferably not less than 0.1% by weight, more preferably not less than 0.3% by weight, is compacted into a preform 8 having a density of not less than 7.3 g/cm3. In a provisional sintering step 2, the preform 8 is provisionally sintered at a predetermined temperature to form a metallic powder-molded body 9 having a structure in which the graphite remains along a grain boundary of the metal powder. In a re-compaction step 3, the metallic powder-molded body 9 is re-compacted into a re-compacted body 10. In a re-sintering step 4, the re-compacted body 10 is re-sintered to obtain a sintered body 11. In a heat treatment step 5, the sintered body 11 is heat-treated to obtain a heat-treated sintered body 11.

Abstract: In a preliminary molding step 1, a metallic powder mixture 7 obtained by blending an iron-based metal powder 7a with graphite 7b such that the graphite is present in an amount of preferably not less than 0.1% by weight, more preferably not less than 0.3% by weight, is compacted into a preform 8 having a density of not less than 7.3 g/cm3. In a provisional sintering step 2, the preform 8 is provisionally sintered at a predetermined temperature to form a metallic powder-molded body 9 having a structure in which the graphite remains along a grain boundary of the metal powder. In a re-compaction step 3, the metallic powder-molded body 9 is re-compacted into a re-compacted body 10. In a re-sintering step 4, the re-compacted body 10 is re-sintered to obtain a sintered body 11. In a heat treatment step 5, the sintered body 11 is heat-treated to obtain a heat-treated sintered body 11.

Abstract: A method of forging a raw material for sintering and forging. The method comprises the steps of: (a) compacting metallic powder containing iron as a main component and graphite to obtain a compact having a predetermined density; (b) sintering the compact at a temperature ranging from 700 to 1000° C. to form a sintered compact having a texture in which graphite is retained at grain boundary of metal powder; (c) compressing the sintered compact from two directions to obtain a compressed sintered compact; and (d) extruding the compressed sintered compact upon pressing the compressed sintered compact from the two directions in a manner that a pressure in one of the two directions is reduced relative to a pressure in the other of the two directions to accomplish extrusion forging.

Abstract: A method of forging a raw material for sintering and forging. The method comprises the steps of: (a) compacting metallic powder containing iron as a main component and graphite to obtain a compact having a predetermined density; (b) sintering the compact at a temperature ranging from 700 to 1000° C. to form a sintered compact having a texture in which graphite is retained at grain boundary of metal powder; (c) compressing the sintered compact from two directions to obtain a compressed sintered compact; and (d) extruding the compressed sintered compact upon pressing the compressed sintered compact from the two directions in a manner that a pressure in one of the two directions is reduced relative to a pressure in the other of the two directions to accomplish extrusion forging.

Abstract: An sintered iron-based powder metal body with outstandingly lower re-compacting load and having a high density and a method of manufacturing an iron-based sintered component with fewer pores of a sharp shape and having high strength and high density, the method comprising mixing,