Abstract: Compositions and methods are provided for treating wood products to provide leach-resistant protection against fungal decay, termites and other wood destroying organisms. The preservative compositions provided include ammonia-stabilized solutions of zinc and boron, preferably in a molar ratio of Zn:B of between about 0.4:1 and 5:1, and are essentially copper free. The preservative may be applied by vacuum and/or pressure treatment or dip treatment under atmospheric pressure.

Abstract: A silica xerogel, a process for making it, and a process for using it to reduce chill haze in beer includes incorporation in the xerogel of one or more alkali metals, optionally in combination with one or more alkaline earth metals. The pH of the xerogel is between 8.0 and 10.5, preferably between 8.5 and 10.0.

Abstract: Systems and methods are provided for treating products containing wood fibers to provide protection against wood destroying organisms and fire, and resistance against leaching of the preservative from the wood by water in exposed environments such as exterior applications. The methods involve applying to a substrate a first aqueous composition containing a boron compound, a source of zinc, and ammonia, followed by application of a second aqueous composition containing an alkali metal silicate. The compositions may be applied by vacuum and/or pressure treatment or dip treatment under atmospheric pressure.

Abstract: Compositions and methods are provided for treating wood products to provide leachresistant protection against fungal decay, termites and other wood destroying organisms. The preservative compositions provided include ammonia-stabilized solutions of zinc and boron, preferably in a molar ratio of Zn:B of between about 0.4:1 and 5:1, and are essentially copper free. The preservative may be applied by vacuum and/or pressure treatment or dip treatment under atmospheric pressure.

Abstract: Systems and methods are provided for treating products containing wood fibers to provide protection against wood destroying organisms and fire, and resistance against leaching of the preservative from the wood by water in exposed environments such as exterior applications. The methods involve applying to a substrate a first aqueous composition containing a boron compound, a source of zinc, and ammonia, followed by application of a second aqueous composition containing an alkali metal silicate. The compositions may be applied by vacuum and/or pressure treatment or dip treatment under atmospheric pressure.

Abstract: A silica xerogel, a process for making it, and a process for using it to reduce chill haze in beer includes incorporation in the xerogel of one or more alkali metals, optionally in combination with one or more alkaline earth metals. The pH of the xerogel is between 8.0 and 10.5, preferably between 8.5 and 10.0.

Abstract: A silica xerogel, a process for making it, and a process for using it to reduce chill haze in beer includes incorporation in the xerogel of one or more alkali metals, optionally in combination with one or more alkaline earth metals. The pH of the xerogel is between 8.0 and 10.5, preferably between 8.5 and 10.0.

Abstract: A silica xerogel, a process for making it, and a process for using it to reduce chill haze in beer includes incorporation in the xerogel of one or more alkali metals, optionally in combination with one or more alkaline earth metals. The pH of the xerogel is between 8.0 and 10.5, preferably between 8.5 and 10.0.

Abstract: A method for making a silica supported catalyst involves impregnating a silica component with a catalytic metal using an aqueous, alkaline bath before drying. More specifically, the method involves forming and washing a silica component, such as a silica gel or a co-gel, for example a silica-zirconia co-gel. Then, the washed silica component is contacted with the alkaline bath to effect the impregnation with the catalytic metal, such as cesium, to form an activated silica component. Subsequently, the activated silica component is dried to form the catalyst. The resulting catalysts demonstrate good mechanical strength.

Abstract: An adsorbent removes certain undesirable components from beverages, such as beer, and has a low beverage soluble iron (BSI) content. These undesirable components include contaminants which cause chill haze. The adsorbent includes two components, a silica component and a polyphosphate sequestering agent component, such as sodium tripolyphosphate (STPP). The process for using the adsorbent involves first contacting a beverage with an adsorbent to adsorb at least a portion of the undesirable components then separating the adsorbent from the beverage. The adsorbent may be formed by one of two methods or a combination of both. The first method involves adding the polyphosphate sequestering agent to a reactant, such as a sodium or potassium silicate solution, prior to or during the gelation stage. A second method involves adding the polyphosphate sequestering agent to the water wash after a hydrogel is formed.

Abstract: An adsorbent removes certain undesirable components from beverages, such as beer, and has a low beverage soluble iron (BSI) content. These undesirable components include contaminants which cause chill haze. The adsorbent includes two components, a silica component and a polyphosphate sequestering agent component, such as sodium tripolyphosphate (STPP). The process for using the adsorbent involves first contacting a beverage with an adsorbent to adsorb at least a portion of the undesirable components then separating the adsorbent from the beverage. The adsorbent may be formed by one of two methods or a combination of both. The first method involves adding the polyphosphate sequestering agent to a reactant, such as a sodium or potassium silicate solution, prior to or during the gelation stage. A second method involves adding the polyphosphate sequestering agent to the water wash after a hydrogel is formed.

Abstract: A method for making a silica supported catalyst involves impregnating a silica component with a catalytic metal using an aqueous, alkaline bath before drying. More specifically, the method involves forming and washing a silica component, such as a silica gel or a co-gel, for example a silica-zirconia co-gel. Then, the washed silica component is contacted with the alkaline bath to effect the impregnation with the catalytic metal, such as cesium, to form an activated silica component. Subsequently, the activated silica component is dried to form the catalyst. The resulting catalysts demonstrate good mechanical strength.

Abstract: An adsorbent removes certain undesirable components from beverages, such as beer, and has a low beverage soluble iron (BSI) content. These undesirable components include contaminants which cause chill haze. The adsorbent includes two components, a silica component and a polyphosphate sequestering agent component, such as sodium tripolyphosphate (STPP). The process for using the adsorbent involves first contacting a beverage with an adsorbent to adsorb at least a portion of the undesirable components then separating the adsorbent from the beverage. The adsorbent may be formed by one of two methods or a combination of both. The first method involves adding the polyphosphate sequestering agent to a reactant, such as a sodium or potassium silicate solution, prior to or during the gelation stage. A second method involves adding the polyphosphate sequestering agent to the water wash after a hydrogel is formed.

Abstract: A method for preparing a titanium on silica catalyst, in the form of formed particles such as macrospheres, achieves a controlled titanium distribution type, namely either uniform, eggshell, or intermediate, by selecting the particular titanium precursor depending on its reactivity with hydroxyl groups and by selecting the molar titanium:hydroxyl ratio. Selecting a titanium precursor with a low reactivity and/or adding sufficient titanium precursor to achieve a high molar titanium:hydroxyl ratio aids in forming a uniform distribution of titanium. On the other hand, selecting a titanium precursor with a high reactivity and/or adding only a little titanium precursor resulting in a low molar titanium:hydroxyl ratio aids in forming an eggshell distribution of titanium.

Abstract: A method for preparing a titanium on silica catalyst, in the form of formed particles such as macrospheres, achieves a controlled titanium distribution type, namely either uniform, eggshell, or intermediate, by selecting the particular titanium precursor depending on its reactivity with hydroxyl groups and by selecting the molar titanium:hydroxyl ratio. Selecting a titanium precursor with a low reactivity and/or adding sufficient titanium precursor to achieve a high molar titanium:hydroxyl ratio aids in forming a uniform distribution of titanium. On the other hand, selecting a titanium precursor with a high reactivity and/or adding only a little titanium precursor resulting in a low molar titanium:hydroxyl ratio aids in forming an eggshell distribution of titanium. In particular, the method involves first preparing formed particles, such as macrospheres, of silica hydrogel then drying the formed particles.