Abstract: The present disclosure provides a method for preparing lithium iron phosphate from ferric hydroxyphosphate, including: purifying ferrous sulfate to form a ferrous sulfate solution, adding hydrogen peroxide, phosphoric acid, an ammonium dihydrogen phosphate solution and ammonia water into the ferrous sulfate solution and then reacting to form a mixed slurry, holding the mixed slurry at a temperature for a period of time, and then washing with water and subjecting to press filtration to form ferric hydroxyphosphate precursors with different iron-phosphorus ratios; then flash drying, sintering at a high temperature, and pulverizing to obtain ferric hydroxyphosphate precursors with different iron-phosphorus ratios and different specific surface areas.

Abstract: The present disclosure relates to the technical field of lithium ion battery cathode materials, and particularly discloses a method for preparing a carbon-coated lithium iron phosphate material from ferrous phosphate. The method comprises: mixing self-made ferrous phosphate with a carbon source, and sintering at a low temperature under nitrogen to remove a part of crystal water to obtain carbon-coated ferrous phosphate with a small amount of crystal water; evenly mixing ferrous phosphate with a lithium source, a phosphorus source and multiple carbon sources, and adjusting until a proper iron-to-phosphorus ratio is 0.960-0.975 and a carbon content is 1.5%-1.8%; subsequently drying slurry to obtain material powder; and sintering the material powder through a two-stage temperature rising curve, naturally cooling and then pulverizing to obtain the carbon-coated lithium iron phosphate material.

Abstract: The present disclosure belongs to technical field of cathode materials of lithium batteries, and discloses a preparation method of high-safety high-capacity lithium manganese iron phosphate.

Abstract: The present disclosure belongs to the technical field of lithium battery cathode materials, and discloses a preparation method of multiple carbon-coated high-compaction lithium iron manganese phosphate, comprising the following steps: (1) synthesizing a carbon and vanadium co-doped ferromanganese phosphate precursor through a co-precipitation method, sintering, and removing crystal water to obtain an anhydrous ferromanganese phosphate precursor; (2) adding lithium phosphate, a supplemental phosphorus source, an organic carbon source, a dopant and deionized water, and performing ball milling, wet sanding, spray drying and sintering to obtain an intermediate material; and (3) adding deionized water and the organic carbon source, then performing ball milling, sanding, spray drying, sintering and air jet pulverization to obtain multiple carbon-coated high-compaction lithium iron manganese phosphate.