Abstract: An intumescent fire-retardant and anti-corrosive coating modified by polyaniline-silicon carbide and a preparation method thereof are provided, the coating includes a compound A and a compound B. The compound A includes a waterborne epoxy resin emulsion, polyaniline-silicon carbide composite material, fire-retardant filler, titanium dioxide, aluminum hydroxide, talc powder, a wetting dispersant, a defoaming agent, a flow agent and water, the compound B includes an epoxy hardener. The polyaniline-silicon carbide composite material is prepared from silicon carbide, phenylamine, protonic acid and an oxidizing agent through an ice bath. The polyaniline-silicon carbide composite material can enhance dispersion in the emulsion through the organic-inorganic composite, and silicon carbide has high thermal stability and good density, while polyaniline serves as a material with unique fire-retardant properties.

Abstract: A titanium dioxide micro-nanocontainers, corrosion-resistant waterborne epoxy coatings and preparation method thereof, including preparation steps as follows: TiO2 micro-nano spheres are synthesized by applying hydrothermal method; a polyaniline layer doped with molybdate ions is deposited on the surface of TiO2 micro-nano spheres by adopting the method of in-situ chemical polymerization, TiO2/PANI-MoO42? micro-nano-spheres are obtained, then, polydopamine is encapsulated on the surface of TiO2/PANI-MoO42? micro-nano spheres to obtain titanium dioxide micro-nanocontainers; next, antirust filler, defoamer, dispersant and thickener are added into waterborne epoxy emulsion, then titanium dioxide micro-nanocontainers are added in the waterborne epoxy emulsion for dispersing and grinding, filtering and encapsulating to obtain component A; the waterborne epoxy curing agent and deionized water are mixed in proportion to obtain component B; component A is stirred, then it is mixed with the component B in proportion,

Abstract: A titanium dioxide micro-nanocontainers, corrosion-resistant waterborne epoxy coatings and preparation method thereof, including preparation steps as follows: TiO2 micro-nano spheres are synthesized by applying hydrothermal method; a polyaniline layer doped with molybdate ions is deposited on the surface of TiO2 micro-nano spheres by adopting the method of in-situ chemical polymerization, TiO2/PANI-MoO42? micro-nano-spheres are obtained, then, polydopamine is encapsulated on the surface of TiO2/PANI-MoO42? micro-nano spheres to obtain titanium dioxide micro-nanocontainers; next, antirust filler, defoamer, dispersant and thickener are added into waterborne epoxy emulsion, then titanium dioxide micro-nanocontainers are added in the waterborne epoxy emulsion for dispersing and grinding, filtering and encapsulating to obtain component A; the waterborne epoxy curing agent and deionized water are mixed in proportion to obtain component B; component A is stirred, then it is mixed with the component B in proportion,

Abstract: A titanium dioxide micro-nanocontainers, corrosion-resistant waterborne epoxy coatings and preparation method thereof, including preparation steps as follows: TiO2 micro-nano spheres are synthesized by applying hydrothermal method; a polyaniline layer doped with molybdate ions is deposited on the surface of TiO2 micro-nano spheres by adopting the method of in-situ chemical polymerization, TiO2/PANI-MoO42? micro-nano-spheres are obtained, then, polydopamine is encapsulated on the surface of TiO2/PANI-MoO42? micro-nano spheres to obtain titanium dioxide micro-nanocontainers; next, antirust filler, defoamer, dispersant and thickener are added into waterborne epoxy emulsion, then titanium dioxide micro-nanocontainers are added in the waterborne epoxy emulsion for dispersing and grinding, filtering and encapsulating to obtain component A; the waterborne epoxy curing agent and deionized water are mixed in proportion to obtain component B; component A is stirred, then it is mixed with the component B in proportion,