Abstract: A carbonaceous support member for a high-temperature heat-treated metal molding object, particularly a setter for heat-treatment in powder metallurgy, is formed as a carbon-ceramic composite shaped product having a bulk density of 1.2-1.6 g/ml and including a carbonaceous matrix and 3-20 wt. % of ceramic particles which are uniformly dispersed in the carbonaceous matrix and partly exposed to the surface of the composite. The support member can effectively prevent carburization of a metal molding object supported thereby during the heat-treatment without causing a problem of peeling of coating layer as encountered in a ceramic-coated support member. The support member may be prepared by compression molding of a powdery mixture of a fine carbon precursor and ceramic particles, followed by heating at 1000-2000° C. to carbonize the fine carbon precursor.

Abstract: A carbonaceous support member for a high-temperature heat-treated metal molding object, particularly a setter for heat-treatment in powder metallurgy, is formed as a carbon-ceramic composite shaped product having a bulk density of 1.2-1.6 g/ml and including a carbonaceous matrix and 3-20 wt. % of ceramic particles which are uniformly dispersed in the carbonaceous matrix and partly exposed to the surface of the composite. The support member can effectively prevent carburization of a metal molding object supported thereby during the heat-treatment without causing a problem of peeling of coating layer as encountered in a ceramic-coated support member. The support member may be prepared by compression molding of a powdery mixture of a fine carbon precursor and ceramic particles, followed by heating at 1000-2000° C. to carbonize the fine carbon precursor.

Abstract: A carbonaceous support member for a high-temperature heat-treated metal molding object, particularly a setter for heat-treatment in powder metallurgy, is formed as a carbon-ceramic composite shaped product having a bulk density of 1.2-1.6 g/ml and including a carbonaceous matrix and 3-20 wt. % of ceramic particles which are uniformly dispersed in the carbonaceous matrix and partly exposed to the surface of the composite. The support member can effectively prevent carburization of a metal molding object supported thereby during the heat-treatment without causing a problem of peeling of coating layer as encountered in a ceramic-coated support member. The support member may be prepared by compression molding of a powdery mixture of a fine carbon precursor and ceramic particles, followed by heating at 1000-2000° C. to carbonize the fine carbon precursor.