Abstract: The present invention relates to the field of solid materials for the adsorption of lithium. In particular, the present invention relates to a new method for the preparation of a crystallized and shaped solid material, preferably in extruded form, of the formula (LiCl)x.2Al(OH)3,nH2O, wherein n is between 0.01 and 10, x is between 0.4 and 1, wherein it comprises a step a) of precipitation of boehmite under specific temperature and pH conditions, a step of bringing into contact the precipitate obtained with LiCl, at least one acid extrusion-kneading shaping step, wherein the method also comprises a final hydrothermal treatment step, all of which makes it possible to increase the lithium adsorption capacity, the adsorption kinetics, as well as the lithium/boron selectivity of the materials obtained with respect to the materials of the prior art, when it is used in a lithium extraction method of saline solutions.

Abstract: The present invention relates to the field of solid materials for the adsorption of lithium. In particular, the present invention relates to a novel process for preparing a solid crystalline material formed preferably in extrudate form, of formula (LiCl)x.2Al(OH)3,nH2O with n being between 0.01 and 10, x being between 0.4 and 1, comprising a step a) to precipitate boehmite under specific conditions of temperature and pH, a step to place the precipitate obtained in contact with a specific quantity of LiCl, at least one forming step preferably via extrusion, said process also comprising a final hydrothermal treatment step, all allowing an increase in lithium adsorption capacity and in the adsorption kinetics of the materials obtained compared to prior art materials, when used in a process to extract lithium from saline solutions.

Abstract: The present invention relates to the field of solid materials for the adsorption of lithium. In particular, the present invention relates to a novel process for preparing a solid crystalline material formed preferably in extrudate form, of formula (LiCl)x.2Al(OH)3,nH2O with n being between 0.01 and 10, x being between 0.4 and 1, comprising a step a) to precipitate boehmite under specific conditions of temperature and pH, a step to place the precipitate obtained in contact with a specific quantity of LiCl, at least one forming step preferably via extrusion, said process also comprising a final hydrothermal treatment step, all allowing an increase in lithium adsorption capacity and in the adsorption kinetics of the materials obtained compared to prior art materials, when used in a process to extract lithium from saline solutions.

Abstract: The present invention relates to the field of solid materials for the adsorption of lithium. In particular, the present invention relates to a new method for the preparation of a crystallized and shaped solid material, preferably in extruded form, of the formula (LiCl)x.2Al(OH)3,nH2O, wherein n is between 0.01 and 10, x is between 0.4 and 1, wherein it comprises a step a) of precipitation of boehmite under specific temperature and pH conditions, a step of bringing into contact the precipitate obtained with LiCl, at least one acid extrusion-kneading shaping step, wherein the method also comprises a final hydrothermal treatment step, all of which makes it possible to increase the lithium adsorption capacity, the adsorption kinetics, as well as the lithium/boron selectivity of the materials obtained with respect to the materials of the prior art, when it is used in a lithium extraction method of saline solutions.