Abstract: A titanium trichloride catalytic component and a method for homo- or co-polymerization of an .alpha.-olefin. In separating a titanium trichloride catalytic component from a solution prepared by dissolving titanium tetrachloride, an organic ether compound and an organo-aluminum compound in a solvent, the above stated solvent is a mixed solvent prepared by allowing 20.about.70% by volume of an aromatic hydrocarbon halide to be concomitant with a saturated aliphatic hydrocarbon and/or an alicyclic hydrocarbon in the presence of an olefin; the organo-aluminum compound, the titanium tetrachloride and the organic ether compound are added to the mixed solvent at a solvent temperature not exceeding 55.degree. C.; then, the solvent temperature is raised to a temperature between 45.degree. and 150.degree. C.

Abstract: Titanium trichloride catalytic component and homo- or co-polymerization of .alpha.-olefin by employing the titanium trichloride catalytic component combined with organic aluminium compound, wherein the titanium trichloride catalytic component is prepared by a process comprising the following steps:first step: reducing titanium tetrachloride with an organoaluminum compoundsecond step: treating the resultant reduced solid, which is obtained by the first step, with an organic ether compoundthird step: reacting the treated solid, which is obtained by the second step, with titanium tetrachlorideand whose objects lie in producing polymer of high stereo-regularity advantageously by carrying out reaction of the first step in a single solvent of aromatic compound or a mixed solvent of aliphatic hydrocarbon and aromatic compound.

Abstract: A highly active titanium trichloride catalytic component to be used for polymerization of .alpha.-olefin has highly uniform particle size the mean value of which is adjustable to a desired value between 10 and 500.mu.; and a method for manufacturing an .alpha.-olefin polymer having extremely uniform particle diameter by using a catalyst which is prepared by combining the above stated catalytic component with an organo-aluminum compound. In the manufacture of the olefin polymer, deashing processes can be either omitted or simplified. Further, the pelletizing process on the catalytic component or the polymer also can be omitted.

Abstract: A titanium trichloride catalytic component and a method for homo- or co-polymerization of an .alpha.-olefin. In separating a titanium trichloride catalytic component from a solution prepared by dissolving titanium tetrachloride, an organic ether compound and an organo-aluminum compound in a solvent, the above stated solvent is a mixed solvent prepared by allowing 20.about.70% by volume of an aromatic hydrocarbon halide to be concomitant with a saturated aliphatic hydrocarbon and/or an alicyclic hydrocarbon in the presence of an olefin; the organo-aluminum compound, the titanium tetrachloride and the organic ether compound are added to the mixed solvent at a solvent temperature not exceeding 55.degree. C.; then, the solvent temperature is raised to a temperature between 45 and 150.degree. C.

Abstract: A titanium trichloride catalytic component obtained by separating it out of a solution consisting of titanium tetrachloride, an organic ether compound and an organo-aluminum compound dissolved in a solvent. The solvent is a mixture consisting of a saturated aliphatic hydrocarbon and/or an alicyclic hydrocarbon with 20 to 70% by volume of a concomitant aromatic hydrocarbon halide included therein. The organo-aluminum compound, the titanium tetrachloride and the organic ether compound is added to this mixed solvent at a solvent temperature not exceeding 55.degree. C. Following this, the solvent temperature is raised up to a value between 45.degree. and 150.degree. C. over a period of 10 minutes to 24 hours with an organic ether compound and/or titanium tetrachloride further added during this temperature raising process to obtain thereby a titanium trichloride catalytic component having average particle diameter between 10 and 1000.mu.. Then homo- or co-polymerization of .alpha.

Abstract: A titanium tirchloride catalytic component obtained by separating it out of a solution consisting of titanium tetrachloride, an organic ether compound and an organo-aluminum compound dissolved in a solvent. The solvent is a mixture consisting of a saturated aliphatic hydrocarbon and/or an alicyclic hydrocarbon with 20 to 70% by volume of a concomitant aromatic hydrocarbon halide included therein. The organo-aluminum compound, the titanium tetrachloride and the organic ether compound are added to this mixed solvent at a solvent temperature not exceeding 55.degree. C.Following this, on the way of a process for raising the solvent temperature to 45.degree.-150.degree. C. a temporary cooling process was repeated twice or more than twice, in the cooling process of which the solvent is temporarily cooled to a temperature lower than 40.degree. C.

Abstract: A titanium trichloride catalytic component obtained by separating it out of a solution consisting of titanium tetrachloride, an organic ether compound and an organo-aluminum compound dissolved in a solvent. The solvent is a mixture consisting of a saturated aliphatic hydrocarbon and/or an alicyclic hydrocarbon with 20 to 70% by volume of a concomitant aromatic hydrocarbon halide included therein. The organo-aluminum compound, the titanium tetrachloride and the organic ether compound is added to this mixed solvent at a solvent temperature not exceeding 55.degree. C. Following this, the solvent temperature is raised up to a value between 45.degree. and 150.degree. C. over a period of 10 minutes to 24 hours with an organic ether compound and/or titanium tetrachloride further added during this temperature raising process to obtain thereby a titanium trichloride catalytic component having average particle diameter between 10 and 1000.mu. . Then homo- or co-polymerization of .alpha.

Abstract: A titanium trichloride catalytic component suitable for preparing highly stereospecific polymers having highly uniform particle diameters from .alpha.-olefins is prepared by precipitating such catalytic component from a solution of TiCl.sub.4 in a solvent comprising a saturated aliphatic hydrocarbon and/or an alicyclic hydrocarbon. Such solution is obtained by dissolving TiCl.sub.4, an ether and an organo-aluminum compound having the formula AlR.sub.n X.sub.3-n (wherein R, X and n are as defined hereinafter) in the solvent. The organo-aluminum compound is added at a solvent temperature not exceeding 55.degree. C. in the concomitant presence of an aromatic hydrocarbon halide; subsequently, the temperature of the resulting system is raised to 45.degree.-150.degree. C. over a period of 10 minutes to 24 hours to precipitate the catalytic component which has a uniform particle diameter between 10 and 1000.mu..Homo- or co-polymerization of .alpha.