Abstract: Provided is a manufacturing method of a stainless steel sheet having etching patterns. The method includes: coating a coating composition on a stainless steel sheet to form a coating layer; and forming a matte coated film layer, having an etching effect, on the coating layer. The coating composition comprises: 10 to 30 wt% of a silane-based compound, 0.5 to 6 wt% of an organic acid, 0.1 to 3 wt% of a vanadium compound, 0.1 to 3 wt% of a magnesium compound, and a remainder of a solvent.

Abstract: A galvanized steel sheet according to one aspect of the present invention comprises: a base steel sheet; and a Zn-Al-Mg-based plating layer provided on at least one surface of the base steel sheet, wherein the Zn-Al-Mg-based plating layer may include a surface modified region enriched with cerium (Ce) on a surface layer side of the Zn-Al-Mg-based plating layer.

Abstract: Provided are a hot-dipped galvanized steel material and a method for manufacturing the same. The hot-dipped galvanized steel material comprises an iron substrate and a hot-dipped galvanizing layer formed on the iron substrate, wherein the hot-dipped galvanizing layer comprises, by wt %, 0.01 to 0.5% of Al, 0.01 to 1.5% of Mg, 0.05 to 1.5% of Mn, 0.1 to 6% of Fe, and the balance of Zn and inevitable impurities, with a Zn—Fe—Mn based alloy phase present at the interface between the iron substrate and the hot-dipped galvanizing layer, and an area ratio of the Zn—Fe—Mn-based alloy phase to the hot-dipped galvanizing layer ranging from 1 to 60%.

Abstract: Provided is an ink composition for an inkjet print steel plate, an inkjet print steel plate using the same, and a method for producing an inkjet print steel plate. The ink composition comprises: a linear acrylate-based oligomer; a reactive acrylate-based monomer; an ultraviolet curable initiator; at least one selected from the group consisting of a dye and a pigment; and at least one selected from the group consisting of an antioxidant, an antifoaming agent, and a dispersant.

Abstract: Provided is a surface-treated metallic material with easy control of glossiness and a manufacturing method therefor, the surface-treated metallic material comprising: a metallic material; and a coating layer which is formed on at least one side of the metallic material and on which an ultraviolet curable coating composition is cured, wherein the coating layer consists of a plurality of protrusions, which have a volume of 3 to 16 pico liters and are arranged at a density of 5 to 610 per 1 mm2 of the metallic material. As such, the surface-treated steel sheet is excellent in adhesion, scratch resistance and corrosion resistance, and has easy control of glossiness.

Abstract: A composition for washing a pickled steel plate and a method for washing a pickled steel plate using the same are provided. The composition for washing a pickled steel plate includes a phosphoric acid ester compound, an amine-based compound, sodium carbonate, ammonium acetate, ethylene diamine tetraacetic acid (EDTA) and a remainder of water, and the method for washing a pickled steel plate is performed using the same.

Abstract: Provided are a zinc-base plated steel material comprising a base steel and a zinc-based plated layer and a post-treatment film, which are sequentially formed on the base steel. The post-treatment film comprises an oxide or oxide salt of at least one group A element selected from B, Al, V, and Fe and an organic compound, wherein the content of oxygen atoms in the post-treatment film is 50 atom % or more, and wherein when the mole number of oxygen atoms forming a covalent bond with hydrogen in the post-treatment film is a and the mole number of oxygen atoms not forming the covalent bond with hydrogen is b, a/b is 0.3 or greater; and a composition for forming the post-treatment film.

Abstract: A composition for washing a pickled steel plate and a method for washing a pickled steel plate using the same are provided. The composition for washing a pickled steel plate includes a phosphoric acid ester compound, an amine-based compound, sodium carbonate, ammonium acetate, ethylene diamine tetraacetic acid (EDTA) and a remainder of water, and the method for washing a pickled steel plate is performed using the same.

Abstract: Provided is a hot dip aluminized steel material including a base steel and a hot-dip Al—Si-coated layer, wherein the surface layer of the base steel is provided with an Al-enriched layer in which 2 wt % to 20 wt % of Al is solid-solubilized, and an interface between the base steel and the hot-dip Al—Si-coated layer has a double-layer structured interfacial alloy layer having different hardnesses.

Abstract: Provided are a high manganese hot dip aluminum-plated steel sheet and a method for manufacturing the same, the steel sheet including: a base steel comprising, by wt %, 0.3-0.9% of C, 10-25% of Mn, 0.01-0.5% of Ti, 0.01-0.2% of Sn, 0.01-0.1% of Sb, and the balance of Fe and inevitable impurities; a hot dip aluminum-based steel plated layer formed on the base steel sheet and comprising 0.1 wt % or more of a sum of one or more types among Li, Na, and K, and the balance of Al and inevitable impurities; and an Al—Fe—Si—Mn based alloy layer formed between the base steel sheet and the aluminum-based plated layer, and having a dual structure with different average Fe amounts.

Abstract: A composition for washing a pickled steel plate and a method for washing a pickled steel plate using the same are provided. The composition for washing a pickled steel plate includes a phosphoric acid ester compound, an amine-based compound, sodium carbonate, ammonium acetate, ethylene diamine tetraacetic acid (EDTA) and a remainder of water, and the method for washing a pickled steel plate is performed using the same.

Abstract: Disclosed are a hot-rolled galvanized steel sheet having excellent galling resistance and formability, and a method for manufacturing the same. The hot-rolled galvanized steel sheet, includes: a base steel; and a hot-rolled galvanizing layer formed on the surface of the base steel, wherein the hot-rolled galvanizing layer provides a hot-rolled galvanized steel sheet having a Mn crystallite having a size of 10 ?m or less between the resin dendrites of zinc that form sequins.

Abstract: Provided is a surface-treated metallic material with easy control of glossiness and a manufacturing method therefor, the surface-treated metallic material comprising: a metallic material; and a coating layer which is formed on at least one side of the metallic material and on which an ultraviolet curable coating composition is cured, wherein the coating layer consists of a plurality of protrusions, which have a volume of 3 to 16 pico liters and are arranged at a density of 5 to 610 per 1 mm2 of the metallic material. As such, the surface-treated steel sheet is excellent in adhesion, scratch resistance and corrosion resistance, and has easy control of glossiness.

Abstract: A composition for washing a pickled steel plate and a method for washing a pickled steel plate using the same are provided. The composition for washing a pickled steel plate includes a phosphoric acid ester compound, an amine-based compound, sodium carbonate, ammonium acetate, ethylene diamine tetraacetic acid (EDTA) and a remainder of water, and the method for washing a pickled steel plate is performed using the same.

Abstract: Provided is a coating composition having excellent corrosion resistance and fingerprint resistance, and also provides a stainless steel sheet having etching patterns and a manufacturing method therefor, the stainless steel sheet comprising: a stainless steel sheet; a coating layer, which is formed on the stainless steel sheet and is a cured product of the coating composition; and a quenching coated film layer formed on the coating layer and having a quenching effect, wherein: the coating layer, formed by curing the coating composition having excellent corrosion resistance and fingerprint resistance, is transparent and has high gloss, thereby having an effect of enabling the surface characteristics of the stainless steel sheet to be expressed as they are; the stainless steel sheet having etching patterns has excellent corrosion resistance and fingerprint resistance even on the parts thereof on which the etching patterns are not formed.

Abstract: An ink composition for a printed steel sheet, having excellent adhesion to a steel sheet, processability, solvent resistance, and the like, a method for manufacturing a printed steel sheet using the same, and a printed steel sheet manufactured thereby, are provided. The ink composition for a steel material includes 10 to 30 parts by weight of a mixture of a urethane acrylate oligomer and another type of acrylate oligomer different from the urethane acrylate oligomer, 65 to 80 parts by weight of a radiation curable monomer which is a mixture of a monofunctional radiation curable monomer and a di- or more functional radiation curable monomer, 1 to 10 parts by weight of a photoinitiator, and 0.01 to 10 parts by weight of an adhesion promoter.

Abstract: Provided are a high manganese hot dip aluminum-plated steel sheet and a method for manufacturing the same, the steel sheet including: a base steel comprising, by wt %, 0.3-0.9% of C, 10-25% of Mn, 0.01-0.5% of Ti, 0.01-0.2% of Sn, 0.01-0.1% of Sb, and the balance of Fe and inevitable impurities; a hot dip aluminum-based steel plated layer formed on the base steel sheet and comprising 0.1 wt % or more of a sum of one or more types among Li, Na, and K, and the balance of Al and inevitable impurities; and an Al—Fe—Si—Mn based alloy layer formed between the base steel sheet and the aluminum-based plated layer, and having a dual structure with different average Fe amounts.

Abstract: Provided are a hot-dipped galvanized steel material and a method for manufacturing the same. The hot-dipped galvanized steel material comprises an iron substrate and a hot-dipped galvanizing layer formed on the iron substrate, wherein the hot-dipped galvanizing layer comprises, by wt %, 0.01 to 0.5% of Al, 0.01 to 1.5% of Mg, 0.05 to 1.5% of Mn, 0.1 to 6% of Fe, and the balance of Zn and inevitable impurities, with a Zn—Fe—Mn based alloy phase present at the interface between the iron substrate and the hot-dipped galvanizing layer, and an area ratio of the Zn—Fe—Mn-based alloy phase to the hot-dipped galvanizing layer ranging from 1 to 60%.

Abstract: Provided is a hot dip aluminized steel material including a base steel and a hot-dip Al—Si-coated layer, wherein the surface layer of the base steel is provided with an Al-enriched layer in which 2 wt % to 20 wt % of Al is solid-solubilized, and an interface between the base steel and the hot-dip Al—Si-coated layer has a double-layer structured interfacial alloy layer having different hardnesses.

Abstract: Provided are a zinc-base plated steel material comprising a base steel and a zinc-based plated layer and a post-treatment film, which are sequentially formed on the base steel. The post-treatment film comprises an oxide or oxide salt of at least one group A element selected from B, Al, V, and Fe and an organic compound, wherein the content of oxygen atoms in the post-treatment film is 50 atom % or more, and wherein when the mole number of oxygen atoms forming a covalent bond with hydrogen in the post-treatment film is a and the mole number of oxygen atoms not forming the covalent bond with hydrogen is b, a/b is 0.3 or greater; and a composition for forming the post-treatment film.