Abstract: A white phosphor, and a light emission device including the white phosphor, and a display device including the white phosphor, the white phosphor including 40 to 45 parts by weight of a blue phosphor selected from the group consisting of ZnS:(Ag,Cl), ZnS:(Ag,Al), ZnS:(Ag,Al,Cl), and combinations thereof; 30 to 40 parts by weight of a green phosphor selected from the group consisting of ZnS:(Cu,Al), ZnS:(Cu,Au,Al), and combinations thereof; and 20 to 25 parts by weight of a red phosphor selected from the group consisting of Y2O3:Eu, Y2O3:(Eu,Tb), Y2O2S:Eu, Y2O2S:(Eu,Tb), and combinations thereof. The white phosphor shows a color temperature of from 12,000K and 14,000K.

Abstract: A green emitting phosphor of the following composition: Sr1-xBaxGa2S4:yEu2+, where 0.01?x?0.9 and 0.01?y?0.1. The green emitting phosphor can be applied to a light emitting device due to having light emitting peaks at a short wavelength of 522 to 535 nm and improved color coordinate characteristics.

Abstract: An yttrium based phosphor, a process for preparing the yttrium based phosphor, and a display device using the yttrium based phosphor, the yttrium based phosphor including a conducting material such as WO3 or SnO2, and exhibiting an enhanced luminance characteristic under low voltage, and high current density conditions.

Abstract: Disclosed is a low-voltage blue color fluorescent substance which is doped with 0.5 to 3 weight % of P, and a manufacturing method of the same. The above blue color fluorescent substance is manufactured by mixing phosphoric compound as flux with a mixture of zinc oxide (ZnO) and gallium oxide (Ga2O3); carrying out a primary burn on the mixture at a temperature of 1,200 to 1,300° C.; ball milling and washing; and carrying out a secondary burn on the resultant material at a temperature of 900 to 1,100° C., and then classifying the substance.

Abstract: A low-voltage excited blue phosphor is provided. The phosphor comprises a matrix represented by general formula ZnO.Ga2O3, and Bi doped in the matrix. To prepare the phosphor, ZnO, Ga2O3, Bi compound, and a flux are mixed to produce a mixture, and the mixture is fired at 1100-1300° C. to produce a fired material. Then the fired material is milled, and washed with an acid. The washed material is fired at 800-1100° C. and sieved to produce the blue phosphor.

Abstract: Disclosed is a low voltage blue emitting phosphor and a method for producing the same including the steps of: mixing ZnO, Ga2O3and a Na-based compound to obtain a mixture material; sintering the material at a temperature of 1100 to 1300° C.; milling the first sintered material; washing the milled material using hydrochloric acid; sintering the washed material at a temperature of 800 to 1100° C.; and classifing the material. The low voltage blue emitting phosphor produced as described above is a ZnO—Ga2O3matrix doped with Na, and has an x value of 0.18±0.05 and a y value of 0.17±0.05 in a CIE chromaticity diagram.

Abstract: A display device includes a backlight having a main emitting peak in the region of 380-420 nm, a polarizer for selecting light having prescribed direction among the light emitted from a backlight source and an analyzer for receiving the selected light, a pair of electrodes provided between the polarizer and analyzer, optoelectronic material such as liquid crystal materials and PLZT provided between the electrodes, and a phosphor layer including phosphors which can be stimulated by exposure to the light from the backlight source. The display device has an increased viewing angle and improved luminance.