Abstract: A heat shrinkable film shows a heat shrinkage rate in the direction perpendicular to the main shrinkage direction that is not high even at high temperature and is printable thereon. The heat shrinkable film includes a polyester resin, wherein the heat shrinkage characteristics in the direction perpendicular to the main shrinkage direction satisfy the following Relationships 1 and 2: ?15??T70-65?0??Relationship 1 0??T100-95?5??Relationship 2 wherein ?TX-Y is a value obtained by subtracting heat shrinkage rate of the heat shrinkable film in the direction perpendicular to the main shrinkage direction after the heat shrinkable film is immersed in water bath for 10 seconds at Y° C. from heat shrinkage rate of the heat shrinkable film in the direction perpendicular to the main shrinkage direction after the heat shrinkable film is immersed in water bath for 10 seconds at X° C.

Abstract: The embodiments relate to a heat shrinkable film and a process for regenerating a polyester container using the same. The heat shrinkable film comprises a copolymerized polyester resin comprising a diol component and a dicarboxylic acid component and has a heat shrinkage rate of 30% or more in the main shrinkage direction upon thermal treatment at a temperature of 80° C. for 10 seconds, a melting point of 190° C. or higher as measured by differential scanning calorimetry, and a peak temperature (Tp) of 95° C. to 115° C. as measured in the endothermic and exothermic curve (heat flow) by differential scanning calorimetry. It not only solves the environmental problem by improving the recyclability of the polyester container, but also is capable of enhancing the yield and productivity.

Abstract: Embodiments relate to a process for regenerating a polyester container and a polyester film to be used therein, which not only solve the environmental problems by improving the recyclability of polyester containers, but also are capable of enhancing the quality, yield, and productivity. The process for regenerating a polyester container comprises providing the polyester container and a heat-shrunken polyester film that wraps at least part of the polyester container; crushing the polyester container and the heat-shrunken film to obtain flakes; and thermally treating the flakes to produce regenerated polyester chips, wherein when the flakes are thermally treated at a temperature of 200° C. to 220° C.

Abstract: Embodiments relate to a process for regenerating a polyester container and regenerated polyester chips prepared therefrom. The process comprises preparing a polyester container provided with a heat shrinkable film; crushing the container provided with the heat shrinkable film to obtain flakes; and thermally treating the flakes to produce regenerated polyester chips, wherein when the flakes are thermally treated at a temperature of 200° C. to 220° C. for 60 minutes to 120 minutes, the clumping fraction is 5% or less, and the flakes comprise first flakes obtained by crushing the container and second flakes obtained by crushing the heat shrinkable film. It not only solves the environmental problems by improving the recyclability of the polyester container, but also is capable of enhancing the yield and productivity.

Abstract: Embodiments relate to a heat shrinkable film and a process for regenerating a polyester container using the same. The heat shrinkable film comprises a copolymerized polyester resin comprising a diol component and a dicarboxylic acid component and has a heat shrinkage rate of 30% or more in the main shrinkage direction upon thermal treatment at a temperature of 80° C. for 10 seconds and a melting point of 190° C. or higher as measured by differential scanning calorimetry. It not only solves the environmental problems by improving the recyclability of the polyester container, but also is capable of enhancing the yield and productivity.

Abstract: A heat shrinkable film shows a heat shrinkage rate in the direction perpendicular to the main shrinkage direction that is not high even at high temperature and is printable thereon. The heat shrinkable film includes a polyester resin, wherein the heat shrinkage characteristics in the direction perpendicular to the main shrinkage direction satisfy the following Relationships 1 and 2: ?15??T70-65?0??Relationship 1 0??T100-95?5??Relationship 2 wherein ?TX-Y is a value obtained by subtracting heat shrinkage rate of the heat shrinkable film in the direction perpendicular to the main shrinkage direction after the heat shrinkable film is immersed in water bath for 10 seconds at Y° C. from heat shrinkage rate of the heat shrinkable film in the direction perpendicular to the main shrinkage direction after the heat shrinkable film is immersed in water bath for 10 seconds at X° C.

Abstract: Embodiments relate to a process for regenerating a polyester container and regenerated polyester chips prepared therefrom. The process comprises preparing a polyester container provided with a heat shrinkable film; crushing the container provided with the heat shrinkable film to obtain flakes; and thermally treating the flakes to produce regenerated polyester chips, wherein when the flakes are thermally treated at a temperature of 200° C. to 220° C. for 60 minutes to 120 minutes, the clumping fraction is 5% or less, and the flakes comprise first flakes obtained by crushing the container and second flakes obtained by crushing the heat shrinkable film. It not only solves the environmental problems by improving the recyclability of the polyester container, but also is capable of enhancing the yield and productivity.

Abstract: Embodiments relate to a heat shrinkable film and a process for regenerating a polyester container using the same. The heat shrinkable film comprises a copolymerized polyester resin comprising a diol component and a dicarboxylic acid component and has a heat shrinkage rate of 30% or more in the main shrinkage direction upon thermal treatment at a temperature of 80° C. for 10 seconds and a melting point of 190° C. or higher as measured by differential scanning calorimetry. It not only solves the environmental problems by improving the recyclability of the polyester container, but also is capable of enhancing the yield and productivity.

Abstract: Embodiments relate to a heat shrinkable film, which has a heat shrinkage rate in the direction perpendicular to the main shrinkage direction that is not high even at a high temperature and which is printable thereon. The heat shrinkable film comprises a polyester resin, wherein the heat shrinkage characteristics in the direction perpendicular to the main shrinkage direction satisfy the following Relationships 1 and 2: ?15??T70?65?0??[Relationship 1] 0??T100?95?5??[Relationship 2] wherein ?TX?Y is a value obtained by subtracting a heat shrinkage rate of the heat shrinkable film in the direction perpendicular to the main shrinkage direction after the heat shrinkable film is immersed in a water bath for 10 seconds at Y° C. from a heat shrinkage rate of the heat shrinkable film in the direction perpendicular to the main shrinkage direction after the heat shrinkable film is immersed in a water bath for 10 seconds at X° C.

Abstract: The embodiments relate to a. polyester film and a process for regenerating a polyester container using the same, which not only solve the environmental problems by improving the recyclability of polyester containers, but also are capable of enhancing the yield and productivity. The polyester film comprises a first layer comprising a first resin comprising a diol component and a dicarboxylic acid component; and a second layer laminated on one side of the first layer and comprising a second resin different from the first resin, wherein when the polyester film is cut with a polyethylene terephthalate container to form flakes and the flakes are thermally treated at a temperature of 200° C. to 220° C. for 60 minutes to 120 minutes, the clumping fraction is 8% or less.

Abstract: Embodiments relate to a process for regenerating a polyester container and a polyester film to be used therein, which not only solve the environmental problems by improving the recyclability of polyester containers, but also are capable of enhancing the quality, yield, and productivity. The process for regenerating a polyester container comprises providing the polyester container and a heat-shrunken polyester film that wraps at least part of the polyester container; crushing the polyester container and the heat-shrunken film to obtain flakes; and thermally treating the flakes to produce regenerated polyester chips, wherein when the flakes are thermally treated at a temperature of 200° C. to 220° C.

Abstract: A heat shrinkable film and a process for regenerating a polyester container using the same. The heat shrinkable film comprises a copolymerized polyester resin comprising a diol component and a dicarboxylic acid component and has a heat shrinkage rate of 30% or more in the main shrinkage direction upon thermal treatment at a temperature of 80° C. for 10 seconds and a melting point of 190° C. or higher as measured by differential scanning calorimetry. It not only solves the environmental problems by improving the recyclability of the polyester container, but also is capable of enhancing the yield and productivity.

Abstract: A process for regenerating a polyester container and regenerated polyester chips prepared therefrom. The process comprises preparing a polyester container provided with a heat shrinkable film; crushing the container provided with the heat shrinkable film to obtain flakes; and thermally treating the flakes to produce regenerated polyester chips, wherein when the flakes are thermally treated at a temperature of 200° C. to 220° C. for 60 minutes to 120 minutes, the clumping fraction is 5% or less, and the flakes comprise first flakes obtained by crushing the container and second flakes obtained by crushing the heat shrinkable film. It not only solves the environmental problems by improving the recyclability of the polyester container, but also is capable of enhancing the yield and productivity.

Abstract: Embodiments relate to a heat shrinkable film and a process for regenerating a polyester container using the same. The heat shrinkable film comprises a copolymerized polyester resin comprising a diol component and a dicarboxylic acid component and has a heat shrinkage rate of 30% or more in the main shrinkage direction upon thermal treatment at a temperature of 80° C. for 10 seconds and a melting point of 190° C. or higher as measured by differential scanning calorimetry. It not only solves the environmental problems by improving the recyclability of the polyester container, but also is capable of enhancing the yield and productivity.

Abstract: Embodiments relate to a process for regenerating a polyester container and regenerated polyester chips prepared therefrom. The process comprises preparing a polyester container provided with a heat shrinkable film; crushing the container provided with the heat shrinkable film to obtain flakes; and thermally treating the flakes to produce regenerated polyester chips, wherein when the flakes are thermally treated at a temperature of 200° C. to 220° C. for 60 minutes to 120 minutes, the clumping fraction is 5% or less, and the flakes comprise first flakes obtained by crushing the container and second flakes obtained by crushing the heat shrinkable film. It not only solves the environmental problems by improving the recyclability of the polyester container, but also is capable of enhancing the yield and productivity.

Abstract: Embodiments relate to a heat shrinkable film, which has a heat shrinkage rate in the direction perpendicular to the main shrinkage direction that is not high even at a high temperature and which is printable thereon. The heat shrinkable film comprises a polyester resin, wherein the heat shrinkage characteristics in the direction perpendicular to the main shrinkage direction satisfy the following Relationships 1 and 2: ?15??T70?65?0??[Relationship 1] 0??T100?95?5??[Relationship 2] wherein ?TX-Y is a value obtained by subtracting a heat shrinkage rate of the heat shrinkable film in the direction perpendicular to the main shrinkage direction after the heat shrinkable film is immersed in a water bath for 10 seconds at Y° C. from a heat shrinkage rate of the heat shrinkable film in the direction perpendicular to the main shrinkage direction after the heat shrinkable film is immersed in a water bath for 10 seconds at X° C.

Abstract: Embodiments relate to a process for regenerating a polyester container and regenerated polyester chips prepared therefrom. The process comprises preparing a polyester container provided with a heat shrinkable film; crushing the container provided with the heat shrinkable film to obtain flakes; and thermally treating the flakes to produce regenerated polyester chips, wherein when the flakes are thermally treated at a temperature of 200° C. to 220° C. for 60 minutes to 120 minutes, the clumping fraction is 5% or less, and the flakes comprise first flakes obtained by crushing the container and second flakes obtained by crushing the heat shrinkable film. It not only solves the environmental problems by improving the recyclability of the polyester container, but also is capable of enhancing the yield and productivity.

Abstract: Embodiments relate to a heat shrinkable film and a process for regenerating a polyester container using the same. The heat shrinkable film comprises a copolymerized polyester resin comprising a diol component and a dicarboxylic acid component and has a heat shrinkage rate of 30% or more in the main shrinkage direction upon thermal treatment at a temperature of 80° C. for 10 seconds and a melting point of 190° C. or higher as measured by differential scanning calorimetry. It not only solves the environmental problems by improving the recyclability of the polyester container, but also is capable of enhancing the yield and productivity.

Abstract: Provided is a method of preparing a vinylchloride-based copolymer for plastisol processing. Suspension copolymerization of a vinylchloride monomer with a comonomer having a low glass transition temperature in the presence of a buffer added at an initial stage of the copolymerization can produce a vinylchloride-based copolymer resin with a good low-temperature melting property, a uniform particle size, and a narrow particle size distribution. A plastisol including the vinylchloride-based copolymer resin as a blend resin has low viscosity, and thus, can be easily processed even at a low temperature.