Abstract: A preparation method of improved sintered neodymium-iron-boron (Nd—Fe—B) casting strips includes the following steps: firstly nucleation assisted alloy particles used for sintered Nd—Fe—B casting strips are prepared, all elements are weighted as follows: 26.68-28% of Pr—Nd, 70-72.5% of Fe and 0.90-1% of B, and a Pr element in two elements of Pr—Nd accounts for 0-30 wt %; the compounded materials are smelted and poured to obtain alloy strips, then the alloy strips are crushed into particles with diameter of 1-10 mm; secondly, Nd—Fe—B casting strips are prepared: the prepared intermediate materials are smelted and melted into molten steel, and then are refined; after the intermediate materials are fully melted, the nucleation assisted alloy particles are added; and after the nucleation assisted alloy particles are added, smelting is performed for 3-15 minutes pouring is performed, and final Nd—Fe—B alloy casting strips are obtained.

Abstract: A neodymium-iron-boron permanent magnet, a preparation method and use thereof are disclosed. The neodymium-iron-boron permanent magnet has a composition represented by formula I: [mHR(1?m) (Pr25Nd75)]x(Fe100-a-b-c-dMaGabIncSnd)100-x-yBy formula I; where a is 0.995-3.493, b is 0.114-0.375, c is 0.028-0.125, d is 0.022-0.100; x is 29.05-30.94, y is 0.866-1.000; m is 0.02-0.05; HR is Dy and/or Tb; M is at least one selected from the group consisting of Co, Cu, Ti, Al, Nb, Zr, Ni, W and Mo.

Abstract: A neodymium-iron-boron permanent magnet, a preparation method and use thereof are disclosed. The neodymium-iron-boron permanent magnet has a composition represented by formula I: [mHR(1-m) (Pr25Nd75)]x(Fe100-a-b-c-dMaGabIncSnd)100-x-yBy formula I; where a is 0.995-3.493, b is 0.114-0.375, c is 0.028-0.125, d is 0.022-0.100; x is 29.05-30.94, y is 0.866-1.000; m is 0.02-0.05; HR is Dy and/or Tb; M is at least one selected from the group consisting of Co, Cu, Ti, Al, Nb, Zr, Ni, W and Mo.

Abstract: A preparation method of improved sintered neodymium-iron-boron (Nd—Fe—B) casting strips includes the following steps: firstly nucleation assisted alloy particles used for sintered Nd—Fe—B casting strips are prepared, all elements are weighted as follows: 26.68-28% of Pr—Nd, 70-72.5% of Fe and 0.90-1% of B, and a Pr element in two elements of Pr—Nd accounts for 0-30 wt %; the compounded materials are smelted and poured to obtain alloy strips, then the alloy strips are crushed into particles with diameter of 1-10 mm; secondly, Nd—Fe—B casting strips are prepared: the prepared intermediate materials are smelted and melted into molten steel, and then are refined; after the intermediate materials are fully melted, the nucleation assisted alloy particles are added; and after the nucleation assisted alloy particles are added, smelting is performed for 3-15 minutes pouring is performed, and final Nd—Fe—B alloy casting strips are obtained.