Abstract: According to an exemplary embodiment of the present disclosure, disclosed is an aluminum coated blank that includes a first coated steel sheet; a second coated steel sheet connected to the first coated steel sheet; and a joint portion that connects the first coated steel sheet to the second coated steel plate at a boundary between the first coated steel sheet and the second coated steel sheet.

Abstract: According to an exemplary embodiment of the present disclosure, disclosed is an aluminum coated blank that includes a first coated steel sheet; a second coated steel sheet connected to the first coated steel sheet; and a joint portion that connects the first coated steel sheet to the second coated steel plate at a boundary between the first coated steel sheet and the second coated steel sheet.

Abstract: According to an exemplary embodiment of the present disclosure, disclosed is an aluminum coated blank that includes a first coated steel sheet; a second coated steel sheet connected to the first coated steel sheet; and a joint portion that connects the first coated steel sheet to the second coated steel plate at a boundary between the first coated steel sheet and the second coated steel sheet.

Abstract: The present invention provides a heat treatment method of an aluminum alloy panel, which can prevent surface curvature of molded aluminum alloy panel. For this purpose, the present heat treatment methods comprise: cold rolling an aluminum alloy panel at a reduction ratio of 45 to 50% at a final pass in a cold rolling process; first heat-treating the cold-rolled aluminum alloy panel at 450 to 510° C. for 3 hours; rapidly cooling the heat-treated aluminum alloy panel at a rate 60° C./sec or higher after the first heat treatment; and second heat-treating the rapidly cooled aluminum alloy panel at 200 to 220° C.

Abstract: The present invention discloses a high strength and high toughness aluminum alloy for a bumper beam and a method for manufacturing the same. The method includes: casting into a billet an aluminum alloy which comprises aluminum as a principal element, silicon (Si) of 0.1 wt. % or less, ferrum (Fe) of 0.2 wt. % or less, copper of 0.45 wt. % to 0.60 wt. %, manganese (Mn) of 0.1 wt. % to 0.20 wt. %, magnesium (Mg) of 1.3 wt. % to 1.5 wt. %, chromium (Cr) of 0.1 wt. % or less, zinc of 4.5 wt. % to 5.1 wt. %, titanium (Ti) of 0.04 wt. % or less, zirconium (Zr) of 0.08 wt. % to 0.12 wt. %, and inevitable impurities of 0.15 wt. % or less; extruding the billet into a predetermined form to form an extrusion; performing a solid-solutionization process to quench the extrusion; subjecting the extrusion to an artificial age-hardening which is performed at a temperature of about 120° C. for 24 hours; and subjecting the extrusion an over age-hardening which is performed at a temperature of about 170° C. to 185° C.