Abstract: The present invention provides a dental self-adhesive resin cement having clinically-acceptable adherability for various adherends without pre-treatment with primers. Specifically, there is provided the dental self-adhesive composite resin cement comprising: (a) a radical polymerizable monomer, (b) a polymerizable monomer having a phosphonic acid group and/or a phosphoric acid ester group, (c) a polymerizable monomer having a dibasic acid carboxyl group, (d) a filler, and (e) a polymerization catalyst.

Abstract: The present invention provides a dental resin cement which is excellent in a mechanical strength, workability and storage stability, and a dental primer which significantly improves adhesiveness of the dental resin cement both to enamel and dentin of a tooth. According to the present invention, a salt of barbituric acid is used as a polymerization initiator in the dual-cure two-paste type dental resin cement being excellent in workability and storage stability to improve the storage stability, and a primer containing barbituric acid and amine is applied to a surface of a tooth to significantly improve adhesiveness of the dental resin cement both to enamel and dentin of teeth.

Abstract: The present invention provides a dental self-adhesive resin cement having clinically-acceptable adherability for various adherends without pre-treatment with primers. Specifically, there is provided the dental self-adhesive composite resin cement comprising: (a) a radical polymerizable monomer, (b) a polymerizable monomer having a phosphonic acid group and/or a phosphoric acid ester group, (c) a polymerizable monomer having a dibasic acid carboxyl group, (d) a filler, and (e) a polymerization catalyst.

Abstract: The present invention provides a dental resin cement composition comprising at least two kinds of pastes, one kind of a paste comprising (a) 20 to 50 parts by weight of a polymerizable monomer composition and (b) 50 to 80 parts by weight of a filler consisting of an inorganic compound, or an organic composite comprising an inorganic compound, amounts of (a) and (b) being based on conversion of 100 parts by weight of the dental resin-based cement composition paste, and the filler (b) comprising (c) 2.0 to 10.0 parts by weight of fine silica particles based on the above conversion, and having (d) a yield viscosity of from 100 to 3,000 [Pa·s], and (e) a thixotropy index of 3.0 or more; and another kind of a paste having the same constituent features (a) to (c) and (e) except that the paste has (d) a yield viscosity of from 70 to 4,000 [Pa·s], wherein upon use, the at least two kinds of pastes are used by mixing them.

Abstract: The present invention provides a dental resin cement which is excellent in a mechanical strength, workability and storage stability, and a dental primer which significantly improves adhesiveness of the dental resin cement both to enamel and dentin of a tooth. According to the present invention, a salt of barbituric acid is used as a polymerization initiator in the dual-cure two-paste type dental resin cement being excellent in workability and storage stability to improve the storage stability, and a primer containing barbituric acid and amine is applied to a surface of a tooth to significantly improve adhesiveness of the dental resin cement both to enamel and dentin of teeth.