Abstract: A method for manufacturing a two-piece can includes punching a metal plate into a disk shape, the metal plate including a Sn-plated layer of 100 mg/m2 or more and 1500 mg/m2 or less provided on a base material made of steel, a Cr-plated layer of 6 mg/m2 or more and 100 mg/m2 or less provided on the Sn-plated layer, and a coating layer laminated on the Cr-plated layer; and shaping by performing drawing and ironing on the metal plate having the disk shape into a can body having a bottomed cylindrical shape, wherein in the shaping, the drawing and ironing is performed so that ((Tb?Tw)/Tb)×100, which is a plate thickness reduction rate from the metal plate having the disk shape to the can body, is set as 35%?((Tb?Tw)/Tb)×100(%)?60%.

Abstract: An inspection apparatus capable of improving workability in checking a registration status of a correct answer image. The inspection apparatus includes a registration unit that registers a correct answer image, an inspection unit that compares an image formed on a sheet by a printing unit with the correct answer image registered by the registration unit to inspect the sheet, and a notification unit that notifies the printing unit of information indicating a registration status of the correct answer image in a case where there is a change in the registration status.

Abstract: A printing control apparatus that reduces time and effort in security management for printing. The printing control apparatus is configured to communicate with a cloud storage that stores a plurality of print data with different degrees of confidentiality in different storage locations according to the degrees of confidentiality. The printing control apparatus receives a printing instruction and obtains installation location information indicating an installation location of a printing apparatus designated in the printing instruction, and storage location information indicating a storage location of print data designated in the printing instruction. Based on the storage location information and the installation location information, it is determined whether or not printing of the designated print data is allowed. When it is determined that printing of the designated print data is allowed, the designated print data is obtained from the cloud storage, and the obtained print data is printed.

Abstract: A steel sheet for a container according to the present invention includes: a base steel sheet; a metal chromium layer; and a chromium-containing layer, in which the metal chromium layer is located on at least one surface of the base steel sheet, the chromium-containing layer is located on the metal chromium layer and contains a granular trivalent chromium compound, or contains a granular trivalent chromium compound and granular metal chromium, the metal chromium layer and the chromium-containing layer are separately disposed in two layers on the base steel sheet, in the chromium-containing layer, an average particle size of the trivalent chromium compound and the metal chromium is 10 nm or more and 100 nm or less, and an adhesion amount of the chromium-containing layer is 1.0 mg/m2 or more and 100 mg/m2 or less in terms of a Cr content.

Abstract: A steel sheet for a container according to the present invention includes: a base steel sheet; a metal chromium layer; and a chromium-containing layer, in which the metal chromium layer is located on at least one surface of the base steel sheet, the chromium-containing layer is located on the metal chromium layer and contains a granular trivalent chromium compound, or contains a granular trivalent chromium compound and granular metal chromium, the metal chromium layer and the chromium-containing layer are separately disposed in two layers on the base steel sheet, in the chromium-containing layer, an average particle size of the trivalent chromium compound and the metal chromium is 10 nm or more and 100 nm or less, and an adhesion amount of the chromium-containing layer is 1.0 mg/m2 or more and 100 mg/m2 or less in terms of a Cr content.

Abstract: A steel sheet for containers including a steel sheet, a Sn coated layer that is formed on at least one surface of the steel sheet, and a chemical treatment layer that is formed on the Sn coated layer. A variation amount in a yellowness index measured at one measurement point on the outermost surface of the chemical treatment layer is defined as ?YI, and represented by ?YI=YI?YI0, wherein YI is the yellowness index measured after the steel sheet for containers is subjected to a retort treatment at a temperature of 130° C. for 5 hours, and YI0 is the yellowness index measured before the retort treatment. An average of absolute values of the ?YI obtained at a plurality of measurement points included in a unit area of the outermost surface is 5.0 or less.

Abstract: A steel sheet for a container includes: a steel sheet; an Ni plated layer, which is arranged on at least one side of the steel sheet and is adhered in an amount of from 0.3 to 3 g/m2 per side in terms of metal Ni amount; and a chromate coated film or a Zr coated film which is arranged on the Ni plated layer, in which the Ni plated layer contains from 0.1 to 20% by mass of ZnO particles per side in terms of metal Zn amount.

Abstract: A chemical treatment steel sheet includes a steel sheet, an Fe—Sn alloy layer which is formed on at least one surface of the steel sheet, a Sn layer which is formed on the Fe—Sn alloy layer and contains Sn in which a total amount of Sn contained in the Fe—Sn alloy layer and the Sn layer is 0.10 to 30.0 g/m2, and a chemical treatment layer which is formed on the Sn layer and contains a Zr compound in which an amount of Zr contained therein is 1.0 to 150 mg/m2, a phosphate compound in an amount of P contained therein is 1.0 to 100 mg/m2 and an Al compound in an amount of Al contained therein is 0.10 to 30.0 mg/m2.

Abstract: A chemical treatment steel sheet contains: a steel sheet; a plated layer containing Ni and formed on at least one surface of the steel sheet; a chemical treatment layer containing a Zr compound in which an amount of Zr contained therein is 1.0 to 150 mg/m2, a phosphate compound in which an amount of P contained therein is 1.0 to 100 mg/m2, and an Al compound in which an amount of Al contained therein is 0.10 to 30.0 mg/m2. The plated layer is a Ni-plated layer containing Ni in which an amount of Ni contained therein is 5.0 to 3000 mg/m2 or a composite plated layer containing Ni in which an amount of Ni contained therein is 2.0 to 200 mg/m2 and Sn in which an amount of Sn contained therein is 0.10 to 10.0 g/m2 and having an island-shaped Sn-plated layer formed on a Fe—Ni—Sn alloy layer.

Abstract: A steel sheet for a container includes: a steel sheet; a coated layer containing Ni provided as an upper layer of the steel sheet; and a chemical treatment layer as an upper layer of the coated layer, and containing a Zr compound in an amount of 3.0 to 30.0 mg/m2 in terms of Zr metal, and a Mg compound in an amount of 0.50 to 5.00 mg/m2 in terms of Mg metal, in which the coated layer is one of: a Ni coated layer which contains Ni in amount of 10 to 1000 mg/m2 in terms of Ni metal, and a composite coated layer which contains Ni in an amount of 5 to 150 mg/m2 in terms of Ni metal and Sn in an amount of 300 to 3000 mg/m2 in terms of Sn metal, and has an island-shaped Sn coated layer formed on an Fe—Ni—Sn alloy layer.

Abstract: A steel sheet for a container includes a steel sheet, a Sn coated layer which is provided as an upper layer of the steel sheet and contains Sn in an amount of 560 to 5600 mg/m2 in terms of Sn metal, and a chemical treatment layer which is provided as an upper layer of the Sn coated layer and contains a Zr compound in an amount of 3.0 to 30.0 mg/m2 in terms of Zr metal and a Mg compound in an amount of 0.50 to 5.00 mg/m2 in terms of Mg metal.

Abstract: This steel sheet for containers includes a steel sheet, a Ni coated layer that is formed on at least one surface of the steel sheet, and a chemical treatment layer that is formed on the Ni coated layer. The Ni coated layer contains 10 mg/m2 to 1,000 mg/m2 of Ni in terms of an amount of metal Ni, and the chemical treatment layer contains 5 mg/m2 to 30 mg/m2 of a Zr compound in terms of an amount of metal Zr. An average roughness Ra of an outermost surface of the chemical treatment layer obtained with a scanning probe microscope is 10 nm to 100 nm, and when a variation amount in a yellowness index measured at one measurement point on the outermost surface of the chemical treatment layer is defined as ?YI represented by Equation (2), an average of absolute values of the ?YI obtained at a plurality of the measurement points included in a unit area of the outermost surface is 5.0 or less.

Abstract: A steel sheet for containers includes a steel sheet, an underlying Ni layer formed by performing a Ni coating or a Fe—Ni alloy coating containing Ni in an amount of 5 mg/m2 to 150 mg/m2 in terms of an amount of metal Ni on at least one surface of the steel sheet, a Sn coated layer formed by performing a Sn coating containing Sn in an amount of 300 mg/m2 to 3,000 mg/m2 in terms of an amount of metal Sn on the underlying Ni layer and including an island-shaped Sn formed by alloying the Sn coating and at least a part of the underlying Ni layer by a reflow treatment, an oxide layer formed on the Sn coated layer and containing tin oxide, and a chemical treatment layer formed on the oxide layer and at least contains Zr in an amount of 1 mg/m2 to 500 mg/m2 in terms of an amount of metal Zr and phosphate acid in an amount of 0.1 mg/m2 to 100 mg/m2 in terms of an amount of P, in which the oxide layer contains tin oxide in such an amount that an amount of electricity required for reduction of the oxide layer is 0.

Abstract: Provided is a chemical treatment steel sheet including a steel sheet; a composite coated layer which is formed on at least one surface of the steel sheet, and contains 2 to 200 mg/m2 of Ni in terms of an amount of metal Ni and 0.1 to 10 g/m2 of Sn in terms of an amount of metal Sn, and in which an island-shaped Sn coated layer is formed on an Fe—Ni—Sn alloy layer; and a chemical treatment layer that is formed on the composite coated layer, and contains a 0.01 to 0.1 mg/m2 of Zr compounds in terms of an amount of metal Zr and 0.01 to 5 mg/m2 of phosphate compounds in terms of an amount of P.

Abstract: A chemical treatment steel sheet includes a steel sheet; a Fe—Sn alloy layer which is formed on at least one surface of the steel sheet; an Sn layer which is formed on the Fe—Sn alloy layer; and a chemical treatment layer that is formed on the Sn layer, and contains a 0.01 to 0.1 mg/m2 of Zr compounds in terms of an amount of metal Zr and 0.01 to 5 mg/m2 of phosphate compounds in terms of an amount of P. The total Sn content of the Fe—Sn alloy layer and the Sn layer is 0.1 to 15 g/m2 of Sn in terms of the amount of metal Sn.

Abstract: Provided is a chemical treatment steel sheet including a steel sheet; a composite coated layer which is formed on at least one surface of the steel sheet, and contains 2 to 200 mg/m2 of Ni in terms of an amount of metal Ni and 0.1 to 10 g/m2 of Sn in terms of an amount of metal Sn, and in which an island-shaped Sn coated layer is formed on an Fe—Ni—Sn alloy layer; and a chemical treatment layer that is formed on the composite coated layer, and contains a 0.01 to 0.1 mg/m2 of Zr compounds in terms of an amount of metal Zr and 0.01 to 5 mg/m2 of phosphate compounds in terms of an amount of P.

Abstract: A Ni-plated steel sheet according to the present invention includes a steel sheet, a first Ni-plated layer which is formed at least on a one-sided surface of the steel sheet and contains Ni, and a second Ni-plated layer which is formed on the first Ni-plated layer and contains Ni. An average central-line roughness Ra at an interface between the first Ni-plated layer and the second Ni-plated layer is less than 0.1 ?m, an average central-line roughness Ra of a surface of the second Ni-plated layer is 0.1 ?m to 100 ?m, and a coating amount of Ni in the entirety of the first Ni-plated layer and the second Ni-plated layer is 20 mg/m2 to 2500 mg/m2 per one-sided surface in terms of metal Ni.

Abstract: A steel sheet for a container includes a steel sheet, a Sn coated layer which is provided as an upper layer of the steel sheet and contains Sn in an amount of 560 to 5600 mg/m2 in terms of Sn metal, and a chemical treatment layer which is provided as an upper layer of the Sn coated layer and contains a Zr compound in an amount of 3.0 to 30.0 mg/m2 in terms of Zr metal and a Mg compound in an amount of 0.50 to 5.00 mg/m2 in terms of Mg metal.

Abstract: This steel sheet for containers includes a steel sheet, a Sn coated layer that is formed on at least one surface of the steel sheet, and a chemical treatment layer that is formed on the Sn coated layer. The Sn coated layer contains 300 mg/m2 to 5,600 mg/m2 of Sn in terms of an amount of metal Sn, and the chemical treatment layer contains 5 mg/m2 to 30 mg/m2 of a Zr compound in terms of an amount of metal Zr, an average roughness Ra of an outermost surface of the chemical treatment layer obtained with a scanning probe microscope is 10 nm to 100 nm. A variation amount in a yellowness index measured at one measurement point on the outermost surface of the chemical treatment layer is defined as ?YI represented by Equation (1), an average of absolute values of the ?YI obtained at a plurality of the measurement points included in a unit area of the outermost surface is 5.0 or less.

Abstract: This steel sheet for containers includes a steel sheet, a Ni coated layer that is formed on at least one surface of the steel sheet, and a chemical treatment layer that is formed on the Ni coated layer. The Ni coated layer contains 10 mg/m2 to 1,000 mg/m2 of Ni in terms of an amount of metal Ni, and the chemical treatment layer contains 5 mg/m2 to 30 mg/m2 of a Zr compound in terms of an amount of metal Zr. An average roughness Ra of an outermost surface of the chemical treatment layer obtained with a scanning probe microscope is 10 nm to 100 nm, and when a variation amount in a yellowness index measured at one measurement point on the outermost surface of the chemical treatment layer is defined as ?YI represented by Equation (2), an average of absolute values of the ?YI obtained at a plurality of the measurement points included in a unit area of the outermost surface is 5.0 or less.