Abstract: A high-strength galvanized steel sheet is excellent in the external appearance of plating and the hydrogen brittleness resistance, and has a high yield ratio, and a method for manufacturing the same. The high-strength galvanized steel sheet including a steel sheet having a specific component composition and a specific steel structure, the amount of diffusible hydrogen in the steel sheet being 0.20 mass ppm or less; and a galvanizing layer provided on a surface of the steel sheet, the galvanizing layer having a content amount of Fe of 8 to 15% in mass %, and an attachment amount of plating per one surface of 20 to 120 g/m2, wherein the amount of Mn oxides contained in the galvanizing layer is 0.050 g/m2 or less; and the high-strength galvanized steel sheet has a yield strength of 700 MPa or more and a yield strength ratio of 65% or more and less than 85%.

Abstract: A high-strength galvanized steel sheet includes a steel sheet having a steel composition having a specific component composition, a steel structure containing martensite and bainite at more than or equal to 70% (including 100%), ferrite at less than 20% (including 0%), and retained austenite at less than 5% (including 0%) in terms of area ratio, the amount of diffusible hydrogen in steel being less than or equal to 0.20 mass ppm; and a galvanizing layer provided on a surface of the steel sheet, having a content amount of Fe of 8 to 15% in mass %, and having an coating weight per one surface of 20 to 120 g/m2, wherein the amount of Mn oxides contained in the galvanizing layer is less than or equal to 0.050 g/m2, and a tensile strength is more than or equal to 1100 MPa and a yield ratio is more than or equal to 0.85.

Abstract: The steel sheet has a steel microstructure containing ferrite: 6% to 90% by area, a microstructure composed of one or more of upper bainite, fresh martensite, tempered martensite, lower bainite, and retained ?: 10% to 94% by area in total, and retained ?: 3% to 20% by volume, a ratio (SUB/S2nd)×100(%) of an area ratio SUB of an upper bainite with a width in the range of 0.8 to 7 ?m, a length in the range of 2 to 15 ?m, and an aspect ratio of 2.2 or more in contact with retained ?UB with a grain width in the range of 0.17 to 0.80 ?m and an aspect ratio in the range of 4 to 25 to an area ratio S2nd of the microstructure composed of one or more of upper bainite, fresh martensite, tempered martensite, lower bainite, and retained ? ranges from 2.0% to 15%.

Abstract: A steel sheet and a manufacturing method therefor are provided. A steel sheet has a component composition and contains 6 to 80% of ferrite and 20 to 94% of a microstructure composed of one or two or more of upper bainite, fresh martensite, tempered martensite, lower bainite, and retained ?, and contains 7 to 20% of retained ?, where: an area ratio (S?UB) of retained ? having a particle width of 0.18 to 0.60 ?m, a particle length of 1.7 to 7.0 ?m, and an aspect ratio of 5 to 15 is 0.2 to 5%; and a total area ratio (S?Block) of fresh martensite having an equivalent circle diameter of 1.5 to 15 ?m and an aspect ratio of 3 or less and/or retained ? particles having an equivalent circle diameter of 1.5 to 15 ?m and an aspect ratio of 3 or less is 3% or less (including 0%).

Abstract: A high-carbon hot-rolled steel sheet and a method for manufacturing the steel sheet are provided. The high-carbon hot-rolled steel sheet has a particular chemical composition. The microstructure of the steel sheet includes ferrite, cementite, and pearlite that accounts for 6.5% or less of the entire microstructure by area fraction. The proportion of the number of cementite grains having an equivalent circle diameter of 0.1 ?m or less to the total number of cementite grains is 20% or less, the average cementite grain size is 2.5 ?m or less, and the cementite accounts for 3.5% or more and 10.0% or less of the entire microstructure by area fraction. The average concentration of solute B in a region extending from a surface layer to a depth of 100 ?m is 10 mass ppm or more. The average concentration of N present as AlN in the region is 70 mass ppm or less.

Abstract: Disclosed is a hot-pressed steel sheet member having a tensile strength of 1780 MPa or more and excellent bending collapsibility. The hot-pressed steel sheet member includes: a specific chemical composition; a microstructure in which an average grain size of prior austenite grains is 8 ?m or less, a volume fraction of martensite is 90% or more, and a solute C content is 25% or less of a total C content; and a tensile strength of 1780 MPa or more.

Abstract: A high-carbon hot-rolled steel sheet and a method for manufacturing the steel sheet are provided. The high-carbon hot-rolled steel sheet has a particular chemical composition. The microstructure of the steel sheet includes ferrite, cementite, and pearlite that accounts for 6.5% or less of the entire microstructure by area fraction. The proportion of the number of cementite grains having an equivalent circle diameter of 0.1 ?m or less to the total number of cementite grains is 20% or less, the average cementite grain size is 2.5 ?m or less, and the cementite accounts for 1.0% or more and less than 3.5% of the entire microstructure by area fraction. The average concentration of solute B in a region extending from a surface layer to a depth of 100 ?m is 10 mass ppm or more. The average concentration of N present as AlN in the region is 70 mass ppm or less.

Abstract: A steel sheet having a specified chemical composition and a tensile strength of 1,320 MPa or more, and methods for producing the steel sheet. The steel sheet has a specified microstructure including martensite and bainite, the total area fraction of the martensite and the bainite being 92% or more and 100% or less, the balance being one or more selected from ferrite and retained austenite. The forumulae [%Ti]+[%Nb]>0.007 and [%Ti]×[%Nb]2?7.5×10?6 are satisfied in the chemical composition.

Abstract: A steel sheet having a specified chemical composition and a method for producing the steel sheet. The steel sheet has a microstructure including martensite and bainite. The total area fraction of the martensite and the bainite to the entirety of the microstructure is 95% or more and 100% or less. The balance of the microstructure is at least one of ferrite and retained austenite. The microstructure includes specific inclusion clusters, the content of the inclusion clusters in the microstructure being 5 clusters/mm2 or less. The microstructure includes prior-austenite grains having an average size of more than 5 ?m. The steel sheet has a tensile strength of 1320 MPa or more.

Abstract: A hot-pressed member having excellent bending collapsibility, a method for manufacturing the same, and a method for manufacturing a steel sheet for the hot-pressed member. The hot-pressed member includes a steel sheet as a base material, the steel sheet having a specified chemical composition. The hot-pressed member has a microstructure in which a martensite microstructure is present in a volume fraction of 70% or greater, and a number density of inclusions having a longest diameter of 25 ?m or greater is 0.02/mm2 or less. The hot-pressed member has a tensile strength of 1.8 GPa or greater.

Abstract: A steel sheet having a specified chemical composition and a tensile strength of 1,320 MPa or more, and methods for producing the steel sheet. The steel sheet has a specified microstructure including martensite and bainite, the total area fraction of the martensite and the bainite being 95% or more and 100% or less, the balance being one or more selected from ferrite and retained austenite. The forumulae [% Ti]+[% Nb]>0.007 and [% Ti]×[% Nb]2?7.5×10?6 are satisfied in the chemical composition.

Abstract: A steel sheet having excellent fatigue resistance as a material for automobile parts and a TS of 590 MPa or more, and a method for producing the same. The steel sheet has a composition comprising, by mass %, C: 0.04% or more and 0.15% or less, Si: 0.3% or less, Mn: 1.0% or more and 2.6% or less, P: 0.1% or less, S: 0.01% or less, Al: 0.01% or more and 0.1% or less, N: 0.015% or less, one or two of Ti and Nb: 0.01% or more and 0.2% or less in a total, and the balance being Fe and unavoidable impurities. The steel sheet has 50% or more of ferrite and 10% or more and 50% or less of martensite in terms of an area ratio, and a microstructure in which a standard deviation of nano-hardness is 1.50 GPa or less and tensile strength of 590 MPa or more.

Abstract: A steel sheet having a specified chemical composition and a method for producing the steel sheet. The steel sheet has a microstructure comprising ferrite: 5% or less, and at least one of upper bainite, fresh martensite, tempered martensite, lower bainite, and retained ?: 95% to 100%, and retained ?: 5% to 20%. Retained ?UB has a specified area percentage S?UB, retained ?LB has a specified distribution number N?LB, and at least one of (i) fresh martensite has a specified equivalent circular grain diameter and aspect ratio and (ii) retained ? grains has a specified equivalent circular grain diameter and aspect ratio.

Abstract: A thin steel sheet has a specific chemical composition. The thin steel sheet has a microstructure in which ferrite is present in an area fraction of 4% or less (including 0%), as-quenched martensite is present in an area fraction of 10% or less (including 0%), retained austenite is present in an amount of 7% or more and 20% or less, and upper bainite, lower bainite, and tempered martensite are present in a total area fraction of more than 71% and less than 93%; and BCC iron that has a misorientation of 1° or less and surrounds retained austenite having an equivalent circular diameter of 1 ?m or less is present in an area fraction of 4% or more and 50% or less, and BCC iron that has a misorientation of more than 1° is present in an area fraction of 25% or more and 85% or less.

Abstract: A high-yield-ratio high-strength electrogalvanized steel sheet having an electrogalvanized coating layer formed on a surface of a base steel sheet, in which the base steel sheet has a certain chemical composition, and a steel microstructure, in which a total area fraction of one or both of bainite containing carbides having an average grain diameter of 50 nm or less and tempered martensite containing carbides having an average grain diameter of 50 nm or less is 90% or more in the whole of the steel microstructure, and in which a total area fraction of one or both of the bainite containing and the tempered martensite containing carbides is 80% or more in a region from the surface of the base steel sheet to a position located at ? of a thickness of the base steel sheet, and diffusible hydrogen in steel in an amount of 0.20 mass ppm or less.

Abstract: A thin steel sheet has a specific chemical composition. The thin steel sheet has a microstructure in which ferrite is present in an area fraction of 5% or more and 60% or less, as-quenched martensite is present in an area fraction of 10% or less (including 0%), retained austenite is present in an area fraction of 5% or more and 20% or less, and upper bainite, lower bainite, and tempered martensite are present in a total area fraction of more than 15% and less than 85%; BCC iron that has a misorientation of 1° or less and surrounds retained austenite having an aspect ratio of 2.5 or higher is present in an area fraction of 5% or more and 70% or less; and a top 10% of retained austenite in terms of an equivalent circular diameter has an average aspect ratio of 2.5 or higher.

Abstract: A high-strength cold rolled steel sheet having mechanical characteristics having a tensile strength of not less than 780 MPa, a yield ratio of not more than 70%, and a small in-plane anisotropy of a tensile characteristicis obtained by hot rolling a steel slab comprising by mass % C: 0.07 to 0.12%, Si: not more than 0.7%, Mn: 2.2 to 2.8% and Ti and Nb: 0.02 to 0.08% in total, and cold rolling the sheet, followed by continuous annealing to form a steel texture comprised of ferrite having an area ratio of 40 to 80% with respect to the whole texture, and a second phase constituted by tempered martensite, fresh martensite and bainite, wherein the total area ratio of the bainite and the tempered martensite to the second phase is 50 to 80%, and the aspect ratio of the fresh martensite is in the range of 1.0 to 1.5.

Abstract: A steel sheet having a specified chemical composition and a method for producing the steel sheet. The steel sheet has a microstructure comprising ferrite: 5% or less, and at least one of upper bainite, fresh martensite, tempered martensite, lower bainite, and retained ?: 95% to 100% by area percentage, and retained ?: 4% to 15% by volume percentage. Retained ?UB has a specified area percentage S?UB, retained ?LB has a specified distribution number N?LB, and at least one of (i) fresh martensite has a specified equivalent circular grain diameter and aspect ratio and (ii) retained ? grains has a specified equivalent circular grain diameter and aspect ratio.

Abstract: A high-strength steel sheet of the present invention has a specific chemical composition. Furthermore, in the steel sheet, a degree of Mn segregation in a specific region is 1.5 or less; a maximum P concentration in a specific region is 0.08 mass % or less; in a specific region, the number of specific MnS particle groups is 2.0 or fewer per 1 mm2, and the number of specific oxide-based inclusions is 8 or fewer per 1 mm2; of all of the oxide-based inclusions, oxide-based inclusions having a specified composition are present in a number ratio of 80% or greater; the microstructure includes, in terms of a volume fraction, 30 to 95% martensite and bainite in total, 5 to 70% ferrite phase, and less than 3% (and 0% or greater) austenite phase; and a tensile strength is 980 MPa or greater.

Abstract: A high-strength steel sheet of the present invention has a specific chemical composition. Furthermore, in the steel sheet, a degree of Mn segregation in a specific region is 1.5 or less; a maximum P concentration in a specific region is 0.08 mass % or less; in a specific region, at least one specific MnS particle group is present, the number of specific MnS particle groups is 2.0 or fewer per 1 mm2, and the number of specific oxide-based inclusions is 8 or fewer per 1 mm2; of all oxide-based inclusions, oxide-based inclusions having a specific composition are present in a number ratio of 80% or greater; the microstructure includes, in terms of a volume fraction, 30 to 95% martensite, 5 to 70% ferrite phase, less than 30% (and 0% or greater) bainite, and less than 2.0% (and 0% or greater) austenite phase; and a tensile strength is 980 MPa or greater.